Oxidation of silicon nitride in semiconductor devices
Assignee: International Business Machines Corp
•
Filing: 1993-04-27
•
Granted: 1995-07-18
•
Expires: 2013-04-27
Abstract
Abstract A silicon nitride layer in a semiconductor device is oxidized by exposure to a mixture of an oxygen reactant and a dilute amount of a fluorine-containing compound at a temperature sufficiently high to substantially cause the oxidation of the silicon nitride. Generally, a temperature greater than about 600 DEG C. is sufficient to cause such oxidation, although some oxidation may occur at lower temperatures. The concentration of the fluorine-containing compound is also not critical, but is generally between about 100 to 1500 ppm by volume relative to the total mixture volume. Preferably, NF3 is the fluorine-containing compound, and a temperature greater than about 700 DEG C. at a concentration of between about 100 to 1000 ppm is used.
Inventors
- 👤 Stephen F. Geissler
- 👤 Josef W. Korejwa
- 👤 Jerome B. Lasky
- 👤 Pai-Hung Pan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:00
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6516; H10P14/6518; H10P14/6519; H10P14/6522; H10P14/6529; H10P14/6548; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/694; H10P14/6943; H10P14/69433; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
105 words
A method for manufacturing a semiconductor device, comprising the steps of: providing a semiconductor substrate; etching a trench into said substrate, said trench having an interior surface and a top end and extending into the body of said substrate; forming an insulation layer on said interior surface of said trench; said insulation layer comprising at least in part a silicon nitride layer; and oxidizing said silicon nitride using a mixture comprising an oxygen reactant and a dilute amount of NF 3 at a temperature greater than about 700° C. and below 1000° C.; the concentration of NF 3 being between about 100 to 1000 ppm.
Claim 2
Independent Claim
105 words
A method for manufacturing a semiconductor device, comprising the steps of: providing a semiconductor substrate; etching a trench into said substrate, said trench having an interior surface and a top end and extending into the body of said substrate; forming an insulation layer on said interior surface of said trench; said insulation layer comprising at least in part a silicon nitride layer; and oxidizing said silicon nitride using a mixture comprising an oxygen reactant and a dilute amount of NF 3 at a temperature greater than about 700° C. and below 1000° C.; the concentration of NF 3 being between about 100 to 1000 ppm.
Claim 3
Dependent Claim
38 words
The method of claim 1 further comprising the steps of: forming an oxide collar overlying a portion of said insulation layer; and forming a cap oxide having a top surface substantially near the top end of said trench.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein said insulation layer is an ONO layer.
Claim 5
Dependent Claim
16 words
The method of claim 3 further comprising the step of substantially filling said trench with polysilicon.
Claim 6
Dependent Claim
22 words
The method of claim 4 wherein said silicon nitride is oxidized in a region substantially near said top end of said trench.
Claim 7
Dependent Claim
29 words
The method of claim 5 wherein said silicon nitride is oxidized below said top surface of said cap oxide to a depth sufficient to substantially eliminate parasitic leakage current.
Claim 8
Dependent Claim
14 words
The method of claim 5 wherein said semiconductor device is a deep-trench memory cell.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said oxygen reactant is selected from the group consisting of diatomic oxygen, atomic oxygen, ozone, and an ionized oxygen radical.
Claim 10
Dependent Claim
30 words
The method of claim 8 wherein said mixture comprises a diluent having a proportion between about 10 to 95 percent by volume relative to the total volume of said mixture.
Claim 11
Independent Claim
76 words
A method for manufacturing a semiconductor device having a silicon nitride layer, comprising oxidizing said silicon nitride layer using a mixture comprising an oxygen reactant and a dilute amount of NF 3 at a temperature between about 700° C. to 1000° C.; wherein said oxygen reactant is selected from the group consisting of diatomic oxygen, atomic oxygen, ozone and ionized oxygen radical and wherein the proportion of NF 3 is between about 100 to 1000 ppm.
Claim 12
Independent Claim
76 words
A method for manufacturing a semiconductor device having a silicon nitride layer, comprising oxidizing said silicon nitride layer using a mixture comprising an oxygen reactant and a dilute amount of NF 3 at a temperature between about 700° C. to 1000° C.; wherein said oxygen reactant is selected from the group consisting of diatomic oxygen, atomic oxygen, ozone and ionized oxygen radical and wherein the proportion of NF 3 is between about 100 to 1000 ppm.
Claim 13
Dependent Claim
12 words
The method of claim 10 wherein said mixture further comprises a diluent.
Claim 14
Dependent Claim
10 words
The method of claim 11 wherein said diluent is argon.
Claim 15
Dependent Claim
16 words
The method of claim 12 wherein said step of oxidizing is performed substantially at atmospheric pressure.
Claim 16
Dependent Claim
19 words
The method of claim 13 further comprising the step of heating said silicon nitride layer using rapid thermal annealing.
Claim 17
Independent Claim
65 words
A method for manufacturing a semiconductor device, comprising: providing a silicon nitride layer; and oxidizing said silicon nitride layer using a gas mixture comprising an oxygen reactant and NF 3 at a temperature between about 700° C. to 1000° C., the proportion by volume of NF 3 in said mixture being between about 100 to 1000 ppm relative to the total volume of said mixture.
Claim 18
Independent Claim
65 words
A method for manufacturing a semiconductor device, comprising: providing a silicon nitride layer; and oxidizing said silicon nitride layer using a gas mixture comprising an oxygen reactant and NF 3 at a temperature between about 700° C. to 1000° C., the proportion by volume of NF 3 in said mixture being between about 100 to 1000 ppm relative to the total volume of said mixture.
Claim 19
Dependent Claim
26 words
The method of claim 15 wherein said oxygen reactant is selected from the group consisting of diatomic oxygen, atomic oxygen, ozone, and an ionized oxygen radical.
Claim 20
Dependent Claim
12 words
The method of claim 16 wherein said mixture further comprises a diluent.
References Cited (Backward Citations)
US4833094A
Cited
US4801988A
Cited
US4748131A
Cited
US4960581A
Cited
US5043224A
Cited
US4894352A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-17 | 1999-01-16 | 1999-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-17 | 2003-01-16 | 2003-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-17 | 2007-01-16 | 2007-07-18 | $7700.00 | Window Closed / Lapsed |