Method for preparing gaseous metallic fluoride
Assignee: Mitsui Chemicals Inc
•
Filing: 1989-03-13
•
Granted: 1990-10-02
•
Expires: 2009-03-13
Abstract
Abstract The method for preparing a gaseous metallic floride is here disclosed which comprises reacting a metal or its oxide with a fluorine gas or nitrogen trifluoride gas, the aforesaid method being characterized by comprising the steps of mixing the metal or its oxide with a molding auxiliary comprising a solid metallic fluoride which does not react with fluorine and nitrogen trifluoride; molding the resulting mixture under pressure; and contacting the molded pieces with the fluorine gas or nitrogen trifluoride gas, while the molded pieces are heated.
Inventors
- 👤 Isao Harada
- 👤 Yukihiro Yoda
- 👤 Naruyuki Iwanaga
- 👤 Toshihiko Nishitsuji
- 👤 Akio Kikkawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:23
CPC Classifications
C; C01; C01B; C01B17/00; C01B17/45; C01B17/4507; C01B17/4515; C01B17/453; C01B25/00; C01B25/10; C01B33/00; C01B33/08; C01B33/107; C01B33/10705; C01B35/00; C01B35/06; C01B35/061; C01B9/00; C01B9/08; C01G; C01G41/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
115 words
A method for preparing a gaseous metallic fluoride by reacting a metal or its oxide wit fluorine gas or nitrogen trifluoride gas, the process comprising the steps of mixing said metal or its oxide with a molding auxiliary compound comprising at least one compound selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride and aluminum sodium fluoride; molding the resulting mixture under pressure to form molded pieces; and contacting the molded pieces with said fluorine gas or nitrogen trifluoride gas while said molded pieces are heated to form said gaseous metallic fluoride.
Claim 2
Independent Claim
115 words
A method for preparing a gaseous metallic fluoride by reacting a metal or its oxide wit fluorine gas or nitrogen trifluoride gas, the process comprising the steps of mixing said metal or its oxide with a molding auxiliary compound comprising at least one compound selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride and aluminum sodium fluoride; molding the resulting mixture under pressure to form molded pieces; and contacting the molded pieces with said fluorine gas or nitrogen trifluoride gas while said molded pieces are heated to form said gaseous metallic fluoride.
Claim 3
Dependent Claim
45 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said gaseous metallic fluoride is at least one compound selected from the group consisting of tungsten hexafluoride (WF 6 ), molybdenum hexafluoride (MoF 6 ), antimony trifluoride (SbF 3 ), antimony pentafluoride.
Claim 4
Dependent Claim
38 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said metal is at least one selected from metals in the groups IIIA, IIIB, IVA, IVB, VA, VB, VIA and VIB of the periodic table.
Claim 5
Dependent Claim
52 words
A method for preparing a gaseous metallic fluoride according to claim 3 wherein said metal is at least one selected from the group consisting of tungsten (W), molybdenum (Mo), antimony (Sb), niobium (Nb), arsenic (As), phosphorus (P), boron (B), tantalum (Ta), titanium (Ti), silicon (Si), germanium (Ge), sulfur (S) and uranium (U).
Claim 6
Dependent Claim
86 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said metal oxide is at least one selected from the group consisting of tungsten oxide (WO 3 ), molybdenum oxide (MoO 3 ), uranium oxide (UO, UO 2 and U 3 O 8 ), arsenic oxide (As 2 O 5 ), antimony oxide (Sb 2 O 5 ), niobium oxide (Nb 2 O 5 ), tantalum oxide (Ta 2 O 5 ), titanium oxide (TiO 2 ) and germanium oxide (GeO 2 ).
Claim 7
Dependent Claim
49 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein the amount of said metal or its oxide in the mixture is in the range of 30 to 70% by weight based on said mixture of said metal or its oxide and said molding auxiliary compound.
Claim 8
Dependent Claim
38 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said mixture of said metal or its oxide and said molding auxiliary compound is molded under a pressure of 0.5 to 10 t/cm 2 .
Claim 9
Dependent Claim
31 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said molded pieces have a shape of a cylinder, ring, cubic sphere, gear wheel shape or ribbed shape.
Claim 10
Dependent Claim
36 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said reaction of said molded pieces with said fluorine gas or nitrogen trifluoride is performed at a temperature of 150° to 700° C.
Claim 11
Dependent Claim
38 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said reaction of said molded pieces with said fluorine gas or nitrogen trifluoride is performed under a pressure of 1 to 10 kg/cm 2 .
Claim 12
Dependent Claim
36 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said reaction of said molded pieces with said fluorine gas or nitrogen trifluoride is performed for a period of 1 to 20 hours.
Claim 13
Dependent Claim
40 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein when the molded pieces are brought into contact with said fluorine gas or nitrogen trifluoride gas, said molded pieces are present in the form of filler layer.
Claim 14
Dependent Claim
61 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein said heating treatment in said reducing gas atmosphere is performed for a period of 1 to 100 hours in the case that the raw material is said metal, or for a period of 2 to 500 hours in the case that the raw material is said metallic oxide.
Claim 15
Dependent Claim
58 words
A method for preparing a gaseous metallic fluoride according to claim 1 wherein before contacting the molded pieces with said fluoride gas or nitrogen trifluoride gas, said molded pieces are heated in a reducing gas at a temperature of 500° to 850° C. and then brought into contact with said fluorine gas or nitrogen trifluoride gas under heating.
Claim 16
Independent Claim
102 words
A method of preparing a gaseous metallic fluoride comprising the steps of compacting a mixture of a metal or metal oxide with a solid metal fluoride under pressure to form a molded piece, wherein the metal fluoride is selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride, and aluminum sodium fluoride; heating the molded piece in an atmosphere containing fluorine gas or nitrogen trifluoride gas at a temperature and for sufficient time to produce a substantially pure metallic fluoride.
Claim 17
Independent Claim
102 words
A method of preparing a gaseous metallic fluoride comprising the steps of compacting a mixture of a metal or metal oxide with a solid metal fluoride under pressure to form a molded piece, wherein the metal fluoride is selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride, and aluminum sodium fluoride; heating the molded piece in an atmosphere containing fluorine gas or nitrogen trifluoride gas at a temperature and for sufficient time to produce a substantially pure metallic fluoride.
Claim 18
Dependent Claim
29 words
The method of claim 15 wherein said metal or metal oxide is selected from the group consisting of group IIIA, IIIB, IVA, IVB, VA, VB, VIA, and VIB metals.
Claim 19
Dependent Claim
28 words
The method of claim 16 wherein said metallic fluoride is represented by MF m wherein M is a metal and m is an integer from 3 to 6.
Claim 20
Independent Claim
144 words
A method of preparing a gaseous metallic fluoride comprising the steps of; (a) compacting a mixture of a solid metallic fluoride and a metal or metal oxide under pressure to form a molded piece, wherein said solid metallic fluoride is selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride, thallium fluoride and aluminum sodium fluoride, and wherein the metal or metal oxide is a metal selected from the group consisting of groups IIIA, IIIB, IVA, IVB, VA, VB, VIA and VIB; (b) heating the molded piece in a reducing gas atmosphere; (c) heating the molded pieces in an atmosphere containing fluorine gas or nitrogen trifluoride gas at a temperature and for sufficient time whereby substantially pure metallic fluoride gas is produced.
Claim 21
Independent Claim
144 words
A method of preparing a gaseous metallic fluoride comprising the steps of; (a) compacting a mixture of a solid metallic fluoride and a metal or metal oxide under pressure to form a molded piece, wherein said solid metallic fluoride is selected from the group consisting of lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, beryllium fluoride, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, aluminum fluoride, gallium fluoride, indium fluoride, thallium fluoride and aluminum sodium fluoride, and wherein the metal or metal oxide is a metal selected from the group consisting of groups IIIA, IIIB, IVA, IVB, VA, VB, VIA and VIB; (b) heating the molded piece in a reducing gas atmosphere; (c) heating the molded pieces in an atmosphere containing fluorine gas or nitrogen trifluoride gas at a temperature and for sufficient time whereby substantially pure metallic fluoride gas is produced.
References Cited (Backward Citations)
DE1050315B
Cited
US4704261A
Cited
US2904398A
Cited
DE1123298B
Cited
US4179492A
Cited
JPS60271A
Cited
JPS60272A
Cited
JPS60273A
Cited
JPS60274A
Cited
JPH0314694A
Cited
JPH083749A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-01 | 1994-04-02 | 1994-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-01 | 1998-04-02 | 1998-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-01 | 2002-04-02 | 2002-10-02 | $7700.00 | Window Closed / Lapsed |