Method for in-situ cleaning a Ti target in a Ti + TiN coating process
Assignee: Applied Materials Inc
•
Filing: 1993-09-09
•
Granted: 1995-06-27
•
Expires: 2013-09-09
Abstract
Abstract A novel method of in-situ cleaning a Ti target in a Ti+TiN anti-reflective coating process when such Ti and TiN deposition process are conducted in the same process chamber by the addition of a simple process step and without the use of a shutter.
Inventors
- 👤 Mark A. Mueller
- 👤 Xin Guo
- 👤 John C. Egermeier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:48
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C23C14/06; C23C14/0641; C23C14/14; C23C14/18; C23C14/185; C23C14/22; C23C14/56; C23C14/564; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
129 words
A method of forming a multilayer conductive structure on a semiconductor substrate which comprises: a) forming one or more conductive layers in electrical contact with said semiconductor substrate, the uppermost of said one or more layers comprising a layer of aluminum; b) forming an anti-reflective coating of titanium nitride over said aluminum layer by sputtering titanium from a titanium target in the presence of nitrogen gas; and c) forming a titanium layer over said titanium nitride layer by sputtering titanium from said titanium target, wherein said titanium layer is sufficiently thin to retain the anti-reflective properties of said underlying anti-reflective layer of titanium nitride, yet thick enough to accomplish removal of titanium nitride from said titanium target deposited thereon during said sputter formation of said titanium nitride anti-reflective layer.
Claim 2
Independent Claim
129 words
A method of forming a multilayer conductive structure on a semiconductor substrate which comprises: a) forming one or more conductive layers in electrical contact with said semiconductor substrate, the uppermost of said one or more layers comprising a layer of aluminum; b) forming an anti-reflective coating of titanium nitride over said aluminum layer by sputtering titanium from a titanium target in the presence of nitrogen gas; and c) forming a titanium layer over said titanium nitride layer by sputtering titanium from said titanium target, wherein said titanium layer is sufficiently thin to retain the anti-reflective properties of said underlying anti-reflective layer of titanium nitride, yet thick enough to accomplish removal of titanium nitride from said titanium target deposited thereon during said sputter formation of said titanium nitride anti-reflective layer.
Claim 3
Dependent Claim
52 words
The method of claim 1 wherein said step of forming said one or more conductive layers in electrical contact with said semiconductor substrate further comprises forming one or more barrier layers capable of inhibiting migration of aluminum from said aluminum layer through said one or more barrier layers to said semiconductor layer.
Claim 4
Dependent Claim
39 words
The method of claim 2 wherein said step of forming said one or more barrier layers between said semiconductor substrate and said aluminum layer further comprises forming a titanium nitride layer between said semiconductor substrate and said aluminum layer.
Claim 5
Dependent Claim
51 words
The method of claim 2 wherein said step of forming said one or more barrier layers between said semiconductor substrate and said aluminum layer further comprises the steps of sputtering a layer of titanium in contact with said semiconductor substrate, and then forming a titanium nitride layer over said titanium layer.
Claim 6
Dependent Claim
36 words
The method of claim 1, wherein said semiconductor substrate has a four-layer stack of Ti, TiN, Al, and TiN deposited thereon prior to said deposition of said Ti layer over said anti-reflective layer of titanium nitride.
Claim 7
Dependent Claim
21 words
The method of claim 1, wherein said Ti layer formed over said anti-reflective layer of TiN contains a contaminate of TiN.
Claim 8
Dependent Claim
24 words
The method of claim 1, wherein said Ti layer formed over said anti-reflective layer of TiN has a thickness of less than 20 nm.
Claim 9
Dependent Claim
34 words
A method according to claim 1, wherein said anti-reflective characteristic of said TiN layer is substantially retained such that the reflectivity measured on the surface of said second Ti layer is less than 40%.
Claim 10
Dependent Claim
24 words
A method according to claim 1, wherein said Ti layer is deposited by a total deposition energy no larger than 14 J/cm 2 .
Claim 11
Dependent Claim
29 words
A method according to claim 1, wherein said Ti layer being deposited by a total deposition energy in the range between 4.7 J/cm 2 and 14 J/cm 2 .
Claim 12
Independent Claim
145 words
A method of forming a multilayer conductive structure on a semiconductor substrate which comprises: a) forming a first layer of titanium in electrical contact with said semiconductor substrate; b) forming a first barrier layer of titanium nitride over said first titanium layer; c) forming a layer of aluminum over said first layer of titanium nitride; d) forming an anti-reflective coating of titanium nitride over said aluminum layer by sputtering titanium from a titanium target in the presence of nitrogen gas; and e) forming a second titanium layer over said anti-reflective titanium nitride layer by sputtering titanium from said titanium target, wherein said titanium layer is sufficiently thin to retain the anti-reflective properties of said underlying anti-reflective layer of titanium nitride, yet thick enough to accomplish removal of titanium nitride from said titanium target deposited thereon during said sputter formation of said titanium nitride anti-reflective layer.
Claim 13
Independent Claim
145 words
A method of forming a multilayer conductive structure on a semiconductor substrate which comprises: a) forming a first layer of titanium in electrical contact with said semiconductor substrate; b) forming a first barrier layer of titanium nitride over said first titanium layer; c) forming a layer of aluminum over said first layer of titanium nitride; d) forming an anti-reflective coating of titanium nitride over said aluminum layer by sputtering titanium from a titanium target in the presence of nitrogen gas; and e) forming a second titanium layer over said anti-reflective titanium nitride layer by sputtering titanium from said titanium target, wherein said titanium layer is sufficiently thin to retain the anti-reflective properties of said underlying anti-reflective layer of titanium nitride, yet thick enough to accomplish removal of titanium nitride from said titanium target deposited thereon during said sputter formation of said titanium nitride anti-reflective layer.
Claim 14
Dependent Claim
21 words
A method according to claim 11, wherein said second layer of Ti deposited on said wafer contains a contaminant of TiN.
Claim 15
Dependent Claim
19 words
The method according to claim 11, wherein said second layer of titanium has a thickness not exceeding 20 nm.
Claim 16
Dependent Claim
28 words
A method according to claim 11, wherein said second layer of Ti is deposited by a total deposition energy between 4.7 J/cm 2 and 14 J/cm 2 .
Claim 17
Dependent Claim
21 words
A method according to claim 11, wherein said second layer of Ti has a surface reflectivity of less than about 40%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-26 | 1998-12-26 | 1999-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-26 | 2002-12-26 | 2003-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-26 | 2006-12-26 | 2007-06-27 | $7700.00 | Window Closed / Lapsed |