Methods of forming local interconnections in semiconductor devices
Assignee: Texas Instruments Inc
•
Filing: 1993-06-30
•
Granted: 1995-05-30
•
Expires: 2013-06-30
Abstract
Abstract A method is provided for forming a local interconnect (24) at a face of semiconductor workpiece (10). A layer of conductive material (24) is formed across the workpiece face, followed by the formation of a layer (28) of photoresist adjacent the layer of conductive material (24). The layer of photoresist (28) is patterned to define selected areas of the layer of conductive material (24) to be removed. A dry etch is performed, using a plasma established in a gaseous mixture of carbon tetrachloride, carbon tetrafluoride, and helium, to remove the selected areas of the conductive material and conductive filaments (26) formed at the face of workpiece (10).
Inventors
- 👤 Edmund Burke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:40
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
98 words
A method of forming a local interconnect at a face of a semiconductor workpiece comprising the steps of: forming a layer of conductive material across the workpiece face; forming a layer of photoresist over the layer of conductive material; patterning the layer of photoresist to define selected areas of the layer of conductive material to be removed; and performing a dry etch in a plasma etch chamber using a plasma established from a gaseous mixture of carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1 to remove the layer of conductive material from the selected areas.
Claim 2
Independent Claim
98 words
A method of forming a local interconnect at a face of a semiconductor workpiece comprising the steps of: forming a layer of conductive material across the workpiece face; forming a layer of photoresist over the layer of conductive material; patterning the layer of photoresist to define selected areas of the layer of conductive material to be removed; and performing a dry etch in a plasma etch chamber using a plasma established from a gaseous mixture of carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1 to remove the layer of conductive material from the selected areas.
Claim 3
Dependent Claim
66 words
The method of claim 1, wherein said steps of performing an etch comprises the substeps: introducing carbon tetrachloride into the chamber at a rate of approximately 90 standard cubic centimeters per minute; introducing helium into the chamber at a rate of approximately 30 standard cubic centimeters per minute; and introducing carbon tetrafluoride into the chamber at a rate of approximately 15 standard cubic centimeters per minute.
Claim 4
Dependent Claim
25 words
The method of claim 1, wherein said step of forming a layer of conductive material comprises the step of forming a layer of titanium nitride.
Claim 5
Dependent Claim
74 words
The method of claim 1, wherein said step of forming a layer of conductive material comprises the substeps of: forming a layer of titanium across the face of the workpiece; and exposing the workpiece to heat in a nitrogen atmosphere to form layers of silicide across surfaces of areas of silicon at the face of the workpiece and a layer of titanium nitride across a substantial portion of the entire face of the workpiece.
Claim 6
Independent Claim
91 words
A method of forming a local interconnect at a face of a semiconductor workpiece comprising the steps of: forming a layer of titanium nitride across the workpiece face; forming a layer of photoresist over the layer of titanium nitride; patterning the layer of photoresist to define selected areas of the layer of titanium nitride to be removed; and performing a dry etch to remove the selected areas of the layer of titanium nitride, the dry etch includes a mixture of carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1.
Claim 7
Independent Claim
91 words
A method of forming a local interconnect at a face of a semiconductor workpiece comprising the steps of: forming a layer of titanium nitride across the workpiece face; forming a layer of photoresist over the layer of titanium nitride; patterning the layer of photoresist to define selected areas of the layer of titanium nitride to be removed; and performing a dry etch to remove the selected areas of the layer of titanium nitride, the dry etch includes a mixture of carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1.
Claim 8
Dependent Claim
57 words
The method of claim 5, wherein said step of performing a dry etch comprises the substeps: placing the workpiece inside a plasma etch chamber; introducing a mixture of carbon tetrachloride, helium, and carbon tetrafluoride gases into the chamber; and introducing a radio frequency signal into the chamber to maintain an etching plasma in the mixture of gases.
Claim 9
Dependent Claim
103 words
The method of claim 5, wherein said step of performing a dry etch comprises the substeps of: disposing the workpiece inside a plasma etch chamber; introducing carbon tetrachloride gas into the chamber at a rate of approximately 90 standard cubic centimeters per minute; introducing helium gas into the chamber at a rate of approximately 30 standard cubic centimeters per minute; introducing carbon tetrafluoride gas into the chamber at a rate of approximately 15 standard cubic centimeters per minute; and introducing a radio frequency signal into the chamber to establish a plasma for etching away the selected areas of the layer of titanium nitride.
Claim 10
Dependent Claim
29 words
The method of claim 5, wherein said step of introducing a radio frequency signal comprises the step of introducing a radio frequency of a power of approximately 220 Watts.
Claim 11
Independent Claim
192 words
A method of forming an interconnection between first and second conductors disposed at the face of a semiconductor workpiece, the semiconductor workpiece further including sidewall oxide regions formed at selected locations thereon, the method comprising the steps of: forming a layer of titanium across surfaces of the first and second conductors and the sidewall oxide regions; exposing the workpiece to heat in a nitrogen atmosphere to silicide the surfaces of the first and second conductors and form a layer of titanium nitride across the silicided surfaces of the first and second conductors and the sidewall oxide regions, filaments being created adjacent the sidewall oxide regions during said step of exposing; forming a layer of photoresist over the layer of titanium nitride; patterning the layer of photoresist to define selected areas of said layer of titanium nitride to be removed; and performing a dry etch to remove the selected areas of the layer of titanium nitride to define a titanium nitride interconnection between the first and second conductors and to remove the filaments, using a plasma etch chamber into which is introduced carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1.
Claim 12
Independent Claim
192 words
A method of forming an interconnection between first and second conductors disposed at the face of a semiconductor workpiece, the semiconductor workpiece further including sidewall oxide regions formed at selected locations thereon, the method comprising the steps of: forming a layer of titanium across surfaces of the first and second conductors and the sidewall oxide regions; exposing the workpiece to heat in a nitrogen atmosphere to silicide the surfaces of the first and second conductors and form a layer of titanium nitride across the silicided surfaces of the first and second conductors and the sidewall oxide regions, filaments being created adjacent the sidewall oxide regions during said step of exposing; forming a layer of photoresist over the layer of titanium nitride; patterning the layer of photoresist to define selected areas of said layer of titanium nitride to be removed; and performing a dry etch to remove the selected areas of the layer of titanium nitride to define a titanium nitride interconnection between the first and second conductors and to remove the filaments, using a plasma etch chamber into which is introduced carbon tetrachloride, helium, and carbon tetrafluoride in a ratio of 6:2:1.
Claim 13
Dependent Claim
32 words
The method of claim 9, wherein said step of performing a dry etch comprises the step of performing a dry etch using a gaseous mixture of carbon tetrachloride, carbon tetrafluoride and helium.
Claim 14
Dependent Claim
71 words
The method of claim 9, wherein said step of performing a dry etch comprises the substeps of: introducing carbon tetrachloride gas into the chamber at a rate of approximately 90 standard cubic centimeters per minute; introducing helium gas into the chamber at a rate of approximately 30 standard cubic centimeters per minute; and introducing carbon tetrafluoride gas into the chamber at a rate of approximately 15 standard cubic centimeters per minute.
Claim 15
Dependent Claim
16 words
The method of claim 9, wherein the chamber ambient pressure is maintained at approximately 380 mtorr.
Claim 16
Dependent Claim
25 words
The method of claim 9, wherein the temperature of the chamber electrode and substrate is maintained in a temperature range of 60° to 80° C.
References Cited (Backward Citations)
US4675073A
Cited
US4713141A
Cited
US4878994A
Cited
US4793896A
Cited
US4863559A
Cited
US4957590A
Cited
US4863559B1
Cited
US4793896C1
Cited
US4980020A
Cited
US5122225A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-05-29 | 1998-11-28 | 1999-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-05-29 | 2002-11-28 | 2003-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-05-29 | 2006-11-28 | 2007-05-30 | $7700.00 | Window Closed / Lapsed |