Method for forming local interconnects using chlorine bearing agents
Assignee: Texas Instruments Inc
•
Filing: 1988-11-17
•
Granted: 1989-09-05
•
Expires: 2008-11-17
Abstract
Abstract A method for etching titanium nitride local interconnects is disclosed. A layer of titanium nitride is formed as a by-product of the formation of titanium silicide by direct reaction; this layer of titanium nitride is present over the titanium silicide layer, as well as over insulators such as oxide. A plasma etch using CCl4 as the etchant is used to etch the titanium nitride anisotropically, and selectively relative to the titanium silicide due to the passivation of the titanium silicide surface by the carbon atoms of the CCl4. Excess chlorine concentration may be reduced, further reducing the undesired etching of the titanium silicide, by providing a consumable power electrode, or by introducing chlorine scavenger gases into the reactor. The plasma may be ignited by exposing the gases to a mercury/argon light source, photodetaching electrons from the anions in the gas.
Inventors
- 👤 Monte A. Douglas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:53
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
81 words
A method for dry etching a conductive material comprising a titanium chemical compound, said conductive material being formed over a dielectric and over a silicide on a semiconductor surface, comprising the steps of: disposing the semiconductor surface within a plasma etcher; flowing a chlorine bearing agent into said plasma etcher and over the semiconductor surface; igniting said chlorine bearing agent to form plasma; and etching the titanium chemical compound with said plasma without undesirably etching the silicide from the semiconductor surface.
Claim 2
Independent Claim
81 words
A method for dry etching a conductive material comprising a titanium chemical compound, said conductive material being formed over a dielectric and over a silicide on a semiconductor surface, comprising the steps of: disposing the semiconductor surface within a plasma etcher; flowing a chlorine bearing agent into said plasma etcher and over the semiconductor surface; igniting said chlorine bearing agent to form plasma; and etching the titanium chemical compound with said plasma without undesirably etching the silicide from the semiconductor surface.
Claim 3
Dependent Claim
13 words
The method of claim 1, wherein the titanium chemical compound comprises titanium nitride.
Claim 4
Dependent Claim
13 words
The method of claim 1, wherein the titanium chemical compound comprises titanium oxide.
Claim 5
Dependent Claim
21 words
The method of claim 1, further comprising: mixing a chlorine scavenging reagent with the chlorine bearing agent in said flowing step.
Claim 6
Dependent Claim
13 words
The method of claim 1, wherein the chlorine bearing agent is carbon tetrachloride.
Claim 7
Dependent Claim
20 words
The method of claim 5, wherein the stop of flowing further includes mixing an inert gas with said carbon tetrachloride.
Claim 8
Dependent Claim
19 words
The method of claim 1, wherein the step of igniting comprises passing radio frequency energy through said plasma etcher.
Claim 9
Dependent Claim
19 words
The method of claim 7, wherein the step of igniting further includes shining ultraviolet light through said plasma etcher.
Claim 10
Independent Claim
105 words
A method for forming a local interconnect at a silicon surface, comprising the steps of: forming an insulating layer over a selected location of said surface; forming a layer of titanium silicide in contact with the silicon surface at a location adjacent said insulating layer; forming an interconnect layer of material comprising titanium over said titanium silicide and said insulating layer; forming a protective masking material over a specific portion of said interconnect layer to define an interconnect; and etching said interconnect layer with a chlorine bearing agent in a plasma reactor to remove portions of said interconnect layer not underlying said protective masking layer.
Claim 11
Independent Claim
105 words
A method for forming a local interconnect at a silicon surface, comprising the steps of: forming an insulating layer over a selected location of said surface; forming a layer of titanium silicide in contact with the silicon surface at a location adjacent said insulating layer; forming an interconnect layer of material comprising titanium over said titanium silicide and said insulating layer; forming a protective masking material over a specific portion of said interconnect layer to define an interconnect; and etching said interconnect layer with a chlorine bearing agent in a plasma reactor to remove portions of said interconnect layer not underlying said protective masking layer.
Claim 12
Dependent Claim
55 words
The method of claim 9, wherein the steps of forming said titanium silicide layer and said interconnect layer comprise: depositing a layer of titanium over the silicon surface and said insulating layer; heating the silicon surface so that the layer of titanium reacts with said silicon surface to form a layer of titanium silicide thereat.
Claim 13
Dependent Claim
61 words
The method of claim 10, wherein said heating step comprises: heating said silicon surface in a nitrogen and argon ambient at a temperature sufficient to cause the titanium layer to react with said silicon surface to form a layer of titanium silicide covered with a layer of titanium nitride, and to form a layer comprising titanium nitride over said insulating layer.
Claim 14
Dependent Claim
24 words
The method of claim 11, wherein the step of etching further includes passivating said titanium silicide with radicals dissociated from said chlorine bearing agent.
Claim 15
Dependent Claim
29 words
The method of claim 10, wherein the step of forming a protective masking material over a specific portion of said second layer comprises patterning photoresist over said second layer.
Claim 16
Dependent Claim
16 words
The method of claim 10, wherein the step of etching comprises plasma etching with carbon tetrachloride.
Claim 17
Dependent Claim
21 words
The method of claim 14, wherein the step of etching further includes mixing a chlorine scavenging reagent with aid carbon tetrachloride.
Claim 18
Dependent Claim
20 words
The method of claim 15, wherein the step of etching further includes mixing an inert gas with said carbon tetrachloride.
Claim 19
Dependent Claim
23 words
The method of claim 14, wherein the step of etching further includes providing an electrode in said plasma reactor which reacts with chlorine.
Claim 20
Dependent Claim
26 words
The method of claim 14, wherein the step of etching further includes igniting said carbon tetrachloride to form plasma by adding a mercury/argon ultraviolet light source.
Claim 21
Dependent Claim
93 words
The method of claim 10, wherein the steps of forming said titanium silicide layer and said interconnect layer comprise: depositing a layer of titanium over the silicon surface and said insulating layer; depositing silicon oxide over said titanium; and reacting said titanium in a nitrogen and argon ambient in a furnace at approximately 650 degrees Celsius to cause the titanium layer to react with said silicon surface to form a layer of titanium silicide covered with a layer of titanium oxide, and to form a layer of titanium oxide over said insulating layer.
Claim 22
Dependent Claim
29 words
The method of claim 10, further comprising: wet etching with a water diluted ammonium hydroxide/hydrogen peroxide solution in an agitated tank having a bottom-mounted transducer, after said etching step.
Claim 23
Dependent Claim
48 words
The method of claim 9, wherein the step of forming a protective masking material over a specific portion of said second layer comprises patterning photoresist over said second layer; and wherein said etching step is performed in such a manner that the patterned photoresist is not undesirably etched.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |