Chemical-mechanical polishing processes of planarizing insulating layers
Assignee: Round Rock Research LLC
•
Filing: 1993-09-29
•
Granted: 1995-03-07
•
Expires: 2013-09-29
Abstract
Abstract A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer includes the following sequential steps: a) providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; b) providing a CMP polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer; and c) chemical-mechanical polishing the protective layer and conformal layer in a single CMP step using a single CMP slurry and under conditions which in combination with the slurry remove the conformal layer material at a faster rate than the protective layer material, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such chemical-mechanical polishing. Alternately, the protective layer and conformal layer are CMPed in at least two steps using first and second respective CMP slurries. The first CMP step and slurry remove outermost portions of the protective layer in a manner which is substantially selective to the underlying conformal layer to outwardly expose conformal layer material in high topographical areas. The second CMP step and slurry remove the conformal layer material at a faster rate than the protective layer material. The protective layer upon outward exposure of conformal layer material in high topographical areas restricts material removal from low topographical areas during such second CMP step.
Inventors
- 👤 Trung T. Doan
- 👤 Scott Meikle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:29
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/092
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
173 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing through the outermost surface of the blanketing protective layer and then through the conformal layer in a single chemical-mechanical polishing step using a single chemical-mechanical polishing slurry and under conditions which in combination with the slurry remove the conformal layer material at a faster rate than the protective layer material, and continuing chemical-mechanical polishing in the single step through the protective layer and the conformal layer until all protective layer material is removed, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such chemical-mechanical polishing.
Claim 2
Dependent Claim
173 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing through the outermost surface of the blanketing protective layer and then through the conformal layer in a single chemical-mechanical polishing step using a single chemical-mechanical polishing slurry and under conditions which in combination with the slurry remove the conformal layer material at a faster rate than the protective layer material, and continuing chemical-mechanical polishing in the single step through the protective layer and the conformal layer until all protective layer material is removed, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such chemical-mechanical polishing.
Claim 3
Dependent Claim
17 words
The semiconductor processing method of claim 1 wherein the first thickness is greater than the second thickness.
Claim 4
Dependent Claim
107 words
The semiconductor processing method of claim 1 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 5
Dependent Claim
110 words
The semiconductor processing method of claim 1 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than or equal to 1.1 times the greatest topographical distance.
Claim 6
Dependent Claim
30 words
The semiconductor processing method of claim 1 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 .
Claim 7
Dependent Claim
29 words
The semiconductor processing method of claim 1 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound.
Claim 8
Dependent Claim
28 words
The semiconductor processing method of claim 1 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal.
Claim 9
Dependent Claim
41 words
The semiconductor processing method of claim 1 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer is selected from the group consisting of tungsten metal, tungsten nitride and polysilicon, or mixtures thereof.
Claim 10
Dependent Claim
130 words
The semiconductor processing method of claim 1 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 ; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 11
Dependent Claim
129 words
The semiconductor processing method of claim 1 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 12
Dependent Claim
128 words
The semiconductor processing method of claim 1 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 13
Dependent Claim
128 words
The semiconductor processing method of claim 1 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises tungsten metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 14
Dependent Claim
220 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing the protective layer and conformal layer in at least two chemical-mechanical polishing steps using first and second respective chemical-mechanical polishing slurries, the first chemical-mechanical polishing slurry and step being conducted through the outermost surface of the protective layer and removing outermost portions of the protective layer in a manner which is substantially selective to the underlying conformal layer to outwardly expose conformal layer material in high topographical areas by such first chemical mechanical polishing step, the second chemical-mechanical polishing step and slurry removing the conformal layer material at a faster rate than the protective layer material, and continuing the second step chemical-mechanical polishing .through the protective layer and the conformal layer until all protective layer material is removed, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such second chemical-mechanical polishing step.
Claim 15
Dependent Claim
220 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing the protective layer and conformal layer in at least two chemical-mechanical polishing steps using first and second respective chemical-mechanical polishing slurries, the first chemical-mechanical polishing slurry and step being conducted through the outermost surface of the protective layer and removing outermost portions of the protective layer in a manner which is substantially selective to the underlying conformal layer to outwardly expose conformal layer material in high topographical areas by such first chemical mechanical polishing step, the second chemical-mechanical polishing step and slurry removing the conformal layer material at a faster rate than the protective layer material, and continuing the second step chemical-mechanical polishing .through the protective layer and the conformal layer until all protective layer material is removed, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such second chemical-mechanical polishing step.
Claim 16
Dependent Claim
17 words
The semiconductor processing method of claim 13 wherein the first thickness is greater than the second thickness.
Claim 17
Dependent Claim
107 words
The semiconductor processing method of claim 13 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 18
Dependent Claim
107 words
The semiconductor processing method of claim 13 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than 1.1 times the greatest topographical distance.
Claim 19
Dependent Claim
30 words
The semiconductor processing method of claim 13 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 .
Claim 20
Dependent Claim
29 words
The semiconductor processing method of claim 13 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound.
Claim 21
Dependent Claim
28 words
The semiconductor processing method of claim 13 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal.
Claim 22
Dependent Claim
28 words
The semiconductor processing method of claim 13 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises tungsten metal.
Claim 23
Dependent Claim
130 words
The semiconductor processing method of claim 13 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 ; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 24
Dependent Claim
129 words
The semiconductor processing method of claim 13 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 25
Dependent Claim
128 words
The semiconductor processing method of claim 13 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest ,points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 26
Dependent Claim
128 words
The semiconductor processing method of claim 13 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises tungsten metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 27
Dependent Claim
217 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing the protective layer and conformal layer in at least three chemical-mechanical polishing steps using first and second respective chemical-mechanical polishing slurries, the first chemical-mechanical polishing slurry and step being conducted through the outermost surface of the protective layer and removing outermost portions of the protective layer in a manner which is substantially selective to the underlying conformal layer to outwardly expose conformal layer material in high topographical areas by such first chemical mechanical polishing step, the second chemical-mechanical polishing step and slurry removing the conformal layer material at a faster rate than the protective layer material, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such second chemical-mechanical polishing step, the third chemical-mechanical polishing step using the first slurry and being conducted to remove any remaining protective layer material.
Claim 28
Dependent Claim
217 words
A semiconductor processing method of providing and planarizing an insulating layer on a semiconductor wafer comprising the following sequential steps: providing a conformal layer of insulating material to a first thickness over a semiconductor wafer having non-planar topography; providing a blanketing chemical-mechanical polishing protective layer over the conformal layer to a second thickness, the protective layer being of different composition than the conformal layer, the blanketing protective layer having an outermost surface; and chemical-mechanical polishing the protective layer and conformal layer in at least three chemical-mechanical polishing steps using first and second respective chemical-mechanical polishing slurries, the first chemical-mechanical polishing slurry and step being conducted through the outermost surface of the protective layer and removing outermost portions of the protective layer in a manner which is substantially selective to the underlying conformal layer to outwardly expose conformal layer material in high topographical areas by such first chemical mechanical polishing step, the second chemical-mechanical polishing step and slurry removing the conformal layer material at a faster rate than the protective layer material, the protective layer upon outward exposure of conformal layer material in high topographical areas restricting material removal from low topographical areas during such second chemical-mechanical polishing step, the third chemical-mechanical polishing step using the first slurry and being conducted to remove any remaining protective layer material.
Claim 29
Dependent Claim
17 words
The semiconductor processing method of claim 25 wherein the first thickness is greater than the second thickness.
Claim 30
Dependent Claim
107 words
The semiconductor processing method of claim 25 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 31
Dependent Claim
107 words
The semiconductor processing method of claim 25 wherein, the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; the first thickness being selected such that the first thickness minus the third thickness is less than 1.1 times the greatest topographical distance.
Claim 32
Dependent Claim
30 words
The semiconductor processing method of claim 25 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 .
Claim 33
Dependent Claim
29 words
The semiconductor processing method of claim 25 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound.
Claim 34
Dependent Claim
28 words
The semiconductor processing method of claim 25 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal.
Claim 35
Dependent Claim
28 words
The semiconductor processing method of claim 25 wherein the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises tungsten metal.
Claim 36
Dependent Claim
130 words
The semiconductor processing method of claim 25 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises undoped SiO 2 ; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 37
Dependent Claim
129 words
The semiconductor processing method of claim 25 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises a nitride compound; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 38
Dependent Claim
128 words
The semiconductor processing method of claim 25 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises titanium metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
Claim 39
Dependent Claim
128 words
The semiconductor processing method of claim 25 wherein, the conformal layer insulating material comprises boron and/or phosphorus doped SiO 2 , and the protective layer comprises tungsten metal; the non-planar wafer topography has a highestmost projecting surface prior to the provision of the conformal layer, the conformal layer of insulating material has a greatest topographical distance immediately prior to the step of chemical-mechanical polishing, the greatest topographical distance being defined by the elevational difference between the highest and lowest points of the outermost surface of the conformal layer, and the post chemical-mechanical polished insulating layer has a third thickness over the highestmost projecting surface; and the first thickness being selected such that the first thickness minus the third thickness is less than 1.5 times the greatest topographical distance.
References Cited (Backward Citations)
US4944836A
Cited
US4735679A
Cited
US4956313A
Cited
US5084419A
Cited
US4957881A
Cited
US4910155A
Cited
US5077234A
Cited
US4992135A
Cited
US5064683A
Cited
US5124780A
Cited
US5272117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-06 | 1998-09-05 | 1999-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-06 | 2002-09-05 | 2003-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-06 | 2006-09-05 | 2007-03-07 | $7700.00 | Window Closed / Lapsed |