US5387481A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of preparing a switchable shield
Assignee: Northrop Grumman Corp
•
Filing: 1993-03-15
•
Granted: 1995-02-07
•
Expires: 2013-03-15
Abstract
Abstract A vanadium oxide compound having the formula VO 2 is disclosed for the purpose of selectively shielding an electromagnetic transmitter or receiver. Vanadium oxide exhibits a marked and rapid transition from dielectric and transparent to electromagnetic radiation to metallic and impervious to such radiation at a specific temperature, 68° C. The compound is preferably mounted as a thin layer on a substrate which has been specifically selected for the desired application. The transmission of radiation is then temperature selected. The preferred method of deposition is an organic hydrolysis reaction.
Inventors
- 👤 Kenneth C. Radford
- 👤 Deborah P. Partlow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:57
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/12; G; G21; G21F; G21F1/00; H; H10; H10W; H10W42/00; H10W42/20
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
161 words
A method of preparing a switchable film layer of an oxide of vanadium upon a substrate comprising: (a) preparing a solution containing vanadium alkoxide in a solution concentration of about 2 to 6 weight percent equivalent VO 2 ; (b) applying said solution to said substrate to dispose a thickness of about 2,000 to 10,000 Angstroms of continuous film of the solution upon the substrate; (c) drying said film in a moisture free environment; (d) first heating said dried film in an oxidizing atmosphere to remove the organic components from said film to produce a polycrystalline film which is substantially vanadium pentoxide; (e) secondly heating the polycrystalline vanadium pentoxide film in a reducing atmosphere to convert said film to the desired oxide of vanadium; and (f) wherein the solution concentration and the applied film thickness are such that following drying, first heating and second heating the resulting vanadium oxide film is switchable from an opaque reflective mode to a transmissive mode.
Claim 2
Independent Claim
161 words
A method of preparing a switchable film layer of an oxide of vanadium upon a substrate comprising: (a) preparing a solution containing vanadium alkoxide in a solution concentration of about 2 to 6 weight percent equivalent VO 2 ; (b) applying said solution to said substrate to dispose a thickness of about 2,000 to 10,000 Angstroms of continuous film of the solution upon the substrate; (c) drying said film in a moisture free environment; (d) first heating said dried film in an oxidizing atmosphere to remove the organic components from said film to produce a polycrystalline film which is substantially vanadium pentoxide; (e) secondly heating the polycrystalline vanadium pentoxide film in a reducing atmosphere to convert said film to the desired oxide of vanadium; and (f) wherein the solution concentration and the applied film thickness are such that following drying, first heating and second heating the resulting vanadium oxide film is switchable from an opaque reflective mode to a transmissive mode.
Claim 3
Dependent Claim
44 words
The method set forth in claim 1, wherein the solution is applied to the substrate by dipping the substrate surface to be covered into the solution and pulling the substrate therefrom at a rate which leaves the desired solution layer thickness upon the substrate.
Claim 4
Dependent Claim
32 words
The method set forth in claim 2, wherein the pull rate is about 85 centimeters per minute for a solution concentration of about 2 to 6 weight percent equivalent VO 2 .
Claim 5
Dependent Claim
67 words
The method set forth in claim 1, wherein plural layers of oxide film are provided upon the substrate by following the first heating of the applied film with successive application of film layers with repeated first heating to remove organic components from the applied film layer prior to application of the succeeding film layer and with the second heating taking place after all plural layers are applied.
Claim 6
Dependent Claim
32 words
The method set forth in claim 1, wherein the second heating is carried out for a sufficient time at a temperature sufficient to convert the film to vanadium oxide (VO 2 ).
References Cited (Backward Citations)
US3483110A
Cited
US4022716A
Cited
US3834793A
Cited
US3975658A
Cited
US3993603A
Cited
US4056378A
Cited
US4283113A
Cited
US4421985A
Cited
US4393095A
Cited
US4401690A
Cited
US5103103A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-06 | 1998-08-08 | 1999-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-06 | 2002-08-08 | 2003-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-06 | 2006-08-08 | 2007-02-07 | $7700.00 | Window Closed / Lapsed |