Composition for VO2 incandescent lamp current inrush limiters
Assignee: Philips North America LLC
•
Filing: 1975-06-10
•
Granted: 1976-11-23
•
Expires: 1995-06-10
Abstract
Abstract An improved composition of VO 2 current inrush limiting ceramics for incandescent lamps using a 0.003-0.06 weight percent MoO 3 addition. This addition modifies the resistance-temperature relationship to provide a more gradual transition and also to provide a resistance which varies less at temperatures below the transition temperature. The more gradual change is desirable as it reduces the tendency for a delayed current overshoot and also reduces the tendency for the current to be funnelled through a relatively small portion of the thermistor. The more nearly constant low temperature resistance provides good current inrush limiting in a wider range of ambient temperatures.
Inventors
- 👤 Philip J. Nalepa
- 👤 Peter R. Emtage
- 👤 Robert C. Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:57
CPC Classifications
H; H01; H01K; H01K1/00; H01K1/62
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
66 words
An improved composition of vanadium oxide current inrush limiting ceramic for incandescent lamps, said ceramic being of the type electrically connected in series with an incandescible lamp filament and comprising vanadium oxide having a composite formula V 2 O x , where x is less than 4.5 and greater than 3.5; wherein said improvement comprises doping said ceramic with 0.003-0.06 weight percent of MoO 3 .
Claim 2
Dependent Claim
66 words
An improved composition of vanadium oxide current inrush limiting ceramic for incandescent lamps, said ceramic being of the type electrically connected in series with an incandescible lamp filament and comprising vanadium oxide having a composite formula V 2 O x , where x is less than 4.5 and greater than 3.5; wherein said improvement comprises doping said ceramic with 0.003-0.06 weight percent of MoO 3 .
Claim 3
Dependent Claim
19 words
The composition of claim 1, wherein said ceramic is doped with about 0.03 weight percent of MoO 3 .
References Cited (Backward Citations)
US3402131A
Cited
US3557026A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-23 | 1980-05-24 | 1980-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-23 | 1984-05-24 | 1984-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-23 | 1988-05-24 | 1988-11-23 | $7700.00 | Window Closed / Lapsed |