Claim 2

Process of controlling the photodegradation by sunlight of a film of polypropylene, or propylene copolymers, said film having a thickness of about 1.25 mils or less by forming a composition comprising carbon black as the sole UV light absorbing stabilizer, said carbon black comprising about 0.5% to about 2.4% by weight of said film and said carbon black having a particle size of about 15 nm to about 120 nm; hindered amine light stabilizer for interrupting the free radical chain degradation mechanism, said hindered amine light stabilizer comprising about 0.02% to about 0.4% by weight of said film; an impact modifier for enhancing the photodegradability of said film, said impact modifier comprising about 1% to about 40% by weight of said film; and forming a film from said composition.

Claim 3

Process according to claim 1 wherein said carbon black comprises about 0.9% to about 2.4% by weight of said film, wherein said carbon black has a particle size of about 50 nm to about 120 nm, and wherein said hindered amine light stabilizer comprises about 0.03% to about 0.2% by weight of said film.

Claim 4

Process according to claim 1 wherein said carbon black comprises about 0.5% to about 1.6% by weight of said film, wherein said carbon black has a particle size of about 15 nm to about 40 nm, and wherein said hindered amine light stabilizer comprises about 0.08% to about 0.25% by weight of said film.

Claim 5

Process according to claim 1 wherein said carbon black comprises about 1.3% to about 2.4% by weight of said film, wherein said carbon black has a particle size of about 50 nm to about 120 nm, and wherein said hindered amine light stabilizer comprises about 0.15% to about 0.28% by weight of said film.

Claim 6

Process according to claim 1 wherein said carbon black comprises about 0.6% to about 1.3% by weight of said film, wherein said carbon black has a particle size of about 15 nm to about 40 nm, and wherein said hindered amine light stabilizer comprises about 0.02% to about 0.15% by weight of said film.

Claim 7

Process according to claim 1 wherein said modifier comprises about 3% to about 30% by weight of said film.

Claim 8

Process according to claim 1 wherein said modifier comprises about 5% to about 25% by weight of said film.

Claim 9

Process according to claim 1 wherein said modifier is selected from a group consisting of a terpolymer of ethylene, propylene, and a diene selected from a group consisting of hexadiene, dicyclopentadiene, and ethylidene norbornylene; copolymers of ethylene and propylene; copolymers of butene-1 and ethylene; copolymers of propylene and butene-1; copolymers of ethylene and vinyl acetate; and copolymers of butadiene and styrene.

Claim 10

Process according to claim 1 wherein said impact modifier is selected from a group consisting of a terpolymer of ethylene, propylene, and a diene selected from a group consisting of hexadiene, dicyclopentadiene, and ethylidene norbornylene; copolymers of ethylene and propylene; and copolymers of butene-1 and ethylene.

Claim 11

Process according to claim 1 wherein said impact modifier is selected from a group consisting of copolymers of ethylene and propylene; copolymers of butene-1 and ethylene; and copolymers of propylene and butene-1.

Claim 12

Process according to claim 1 wherein said impact modifier comprises copolymers of butene-1 and ethylene.

Claim 13

Process according to claim 1 wherein said impact modifier comprises a terpolymer of ethylene, propylene, and a diene selected from a group consisting of hexadiene, dicyclopentadiene, and ethylidene norbornylene.

Claim 14

Process according to claim 1 wherein said impact modifier comprises a terpolymer of ethylene, propylene, and hexadiene.

Claim 15

Process according to claim. 1 wherein said impact modifier comprises a blend of a copolymer of butene-1 and ethylene and a terpolymer of ethylene, propylene, and a diene selected from a group consisting of hexadiene, ethylidene norbornylene, and dicyclopentadiene,

Claim 16

Process according to claim 1 wherein said impact modifier comprises a blend of a copolymer of butene-1 and ethylene and a terpolymer of ethylene, propylene, and hexadiene.

Claim 17

Process according to claim 11 wherein said butene-1 is about 85% by weight of said copolymer.

Claim 18

Process according to claim 1 wherein said hindered amine light stabilizer is selected from a group consisting of bis (2,2,6,6-tetramethyl-4-piperridinyl) sebacate; bis(1,2,2,6,6,-pentamethyl-4-piperridinyl) sebacate; n-butyl-(3,5-di-tert-butyl-4-hydroxybenzyl) bis-(1,2,2,6,6-pentamethyl-4-piperridinyl)malonate; N-N'-bis(2,2,6,6,-tetramethyl-4-piperidinyl)-1,6-hexanediamine, polymer with 2,4,6-trichloro-1,3,5-triazine and 2,4,4-trimethyl-1,2-pentanamine; dimethyl succinate polymer with 4-hydroxy-2,2,6,6,tetramethyl-1-piperidine ethanol; hexane-1,6-diamine; N,N'-bis(-2,2,6,6-tetramethyl-4-piperidinyl)-, polymer with 2,4-dichloro-6-)4-morpholinyl)-1,3,5-triazine; a high molecular weight tri-functional hindered amine light stabilizer based on tetramethylpiperazinone; and a hindered amine light stabilizer with a silicon backbone and tetramethylpiperidine as a side chain.

Claim 19

Process according to claim 1 wherein said film is formed from said composition by being extruded in a cast film extruder.