Process for cold forming propylene copolymers
Assignee: Union Carbide Chemicals and Plastics Technology LLC
•
Filing: 1990-04-12
•
Granted: 1992-11-24
•
Expires: 2010-04-12
Abstract
Abstract A process for the solid phase forming of an impact polypropylene copolymer comprising (a) providing an impact polypropylene copolymer comprising (i) a matrix, which is either a homopolymer of propylene or a copolymer of propylene and up to about 5 percent by weight of at least one other alpha-olefin based on the weight of the copolymer, and, incorporated into said matrix, (ii) a copolymer of ethylene and at least one other alpha-olefin, said copolymer having a crystallinity of at least about 20 percent and being present in the impact copolymer in an amount of at least about 10 percent by weight based on the total weight of the impact copolymer; and (b) forming the impact polypropylene copolymer at a temperature above the melting point of component (ii) but below the melting point of component (i).
Inventors
- 👤 Harold K. Ficker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:09
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/14; C08L23/142; C08J; C08J5/00; B; B29; B29C; B29C67/00; B29C67/0029; B29C67/24; C08F; C08F297/00; C08F297/06; C08F297/08; C08L23/12; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/10; B29K2023/12; B29K2105/00; B29K2105/0085; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
117 words
A process for the manufacture of a shaped article which comprises cold forming an impact copolymer composition comprised of: a. at least ten percent (10%) by weight of the total composition of an interpolymer of at least about 85 percent by weight ethylene and one or more other alpha-olefins, having a crystallinity of at least about twenty percent (20%), incorporated, via in situ polymerization, into: b. a matrix which is either a of propylene or an interpolymer of propylene and to about 15 percent by weight of one or more other alpha olefins; at a temperature above the melting point of said interpolymer of ethylene and below the melting point of said homopolymer or interpolymer of propylene.
Claim 2
Dependent Claim
117 words
A process for the manufacture of a shaped article which comprises cold forming an impact copolymer composition comprised of: a. at least ten percent (10%) by weight of the total composition of an interpolymer of at least about 85 percent by weight ethylene and one or more other alpha-olefins, having a crystallinity of at least about twenty percent (20%), incorporated, via in situ polymerization, into: b. a matrix which is either a of propylene or an interpolymer of propylene and to about 15 percent by weight of one or more other alpha olefins; at a temperature above the melting point of said interpolymer of ethylene and below the melting point of said homopolymer or interpolymer of propylene.
Claim 3
Dependent Claim
18 words
The process defined in claim 1 wherein component (a) contains at least about 90 percent by weight ethylene.
Claim 4
Dependent Claim
24 words
The process defined in claim 1 wherein component (a) has a crystallinity in the range of about 20 to about 60 percent by weight.
Claim 5
Dependent Claim
37 words
The process defined in claim 1 wherein component (a) is present in the impact polypropylene copolymer in an amount of about 10 to about 50 percent by weight based on the weight of the impact polypropylene copolymer.
Claim 6
Dependent Claim
17 words
The process defined in claim 1 wherein one of the other alpha-olefins of component (a) is propylene.
Claim 7
Dependent Claim
25 words
The process defined in claim 1 wherein the forming is accomplished at a temperature in the range of about 130° C. to about 145° C.
Claim 8
Dependent Claim
14 words
The process defined in claim 1 wherein component (b) is a homopolymer of propylene.
Claim 9
Dependent Claim
16 words
The process defined in claim 1 wherein component (b) is a copolymer of propylene and ethylene.
Claim 10
Dependent Claim
145 words
A process for the solid phase forming of an impact polypropylene copolymer comprising (a) providing an impact polypropylene copolymer comprising (i) a matrix, which is either a homopolymer of propylene or a copolymer of propylene and up to about 2 percent by weight of at least one other alpha-olefin based on the weight of the copolymer and, incorporated, via in situ polymerization, into said matrix, (ii) a copolymer of at least about 85 percent by weight ethylene and at least one other alpha-olefin, said copolymer having a crystallinity of at least about 20 percent and being present in the impact copolymer in an amount of at least about 10 percent by weight based on the weight of the impact copolymer; and (b) forming said impact polypropylene copolymer at a temperature above the melting point of component (ii) but below the melting point of component (i).
Claim 11
Dependent Claim
145 words
A process for the solid phase forming of an impact polypropylene copolymer comprising (a) providing an impact polypropylene copolymer comprising (i) a matrix, which is either a homopolymer of propylene or a copolymer of propylene and up to about 2 percent by weight of at least one other alpha-olefin based on the weight of the copolymer and, incorporated, via in situ polymerization, into said matrix, (ii) a copolymer of at least about 85 percent by weight ethylene and at least one other alpha-olefin, said copolymer having a crystallinity of at least about 20 percent and being present in the impact copolymer in an amount of at least about 10 percent by weight based on the weight of the impact copolymer; and (b) forming said impact polypropylene copolymer at a temperature above the melting point of component (ii) but below the melting point of component (i).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-24 | 1996-05-25 | 1996-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-24 | 2000-05-25 | 2000-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-24 | 2004-05-25 | 2004-11-24 | $7700.00 | Window Closed / Lapsed |