Process for manufacturing semiconductor devices
Assignee: VACHELLIA LLC
•
Filing: 1992-03-06
•
Granted: 1994-08-09
•
Expires: 2012-03-06
Abstract
Abstract Herein disclosed is a process for manufacturing a semiconductor device, which comprises: a step of forming a first electrode composed of tantalum and tungsten over a semiconductor substrate; a step of depositing a dielectric film of tantalum oxide on the first electrode; a step of oxidizing the first electrode and the dielectric film of tantalum oxide; and a step of forming a second electrode over the dielectric film.
Inventors
- 👤 Masayuki Suzuki
- 👤 Ryo Haruta
- 👤 Hiroshi Shinriki
- 👤 Masayuki Nakata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:10
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10D; H10D1/00; H10D1/60; H10D1/68; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0144; Y; Y10; Y10S; Y10S148/00; Y10S148/117
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
97 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a first electrode comprised of a first film of a mixture of first and second metals over a semiconductor substrate; (b) a step of depositing a dielectric film made of an oxide film of said first metal on said first electrode; (c) a step of oxidizing said first electrode and said dielectric film in an oxidizing atmosphere such that said first metal is oxidized and said second metal is not oxidized; and (d) a step of forming a second electrode over said dielectric film.
Claim 2
Dependent Claim
97 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a first electrode comprised of a first film of a mixture of first and second metals over a semiconductor substrate; (b) a step of depositing a dielectric film made of an oxide film of said first metal on said first electrode; (c) a step of oxidizing said first electrode and said dielectric film in an oxidizing atmosphere such that said first metal is oxidized and said second metal is not oxidized; and (d) a step of forming a second electrode over said dielectric film.
Claim 3
Dependent Claim
43 words
A process for manufacturing a semiconductor device according to claim 1, wherein said first metal is an element belonging to the IVb or Vb group whereas said second metal is at least one metal selected from the group consisting of Mo and W.
Claim 4
Dependent Claim
27 words
A process for manufacturing a semiconductor device according to claim 2, wherein said oxidation is performed in an atmosphere containing H 2 O and H 2 .
Claim 5
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim 3, wherein said first metal is Ta whereas said second metal is W.
Claim 6
Dependent Claim
22 words
A process for manufacturing a semiconductor device according to claim 4, wherein the content of said first metal is 50 atom %.
Claim 7
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim 3, wherein said first metal is Ta whereas said second metal is Mo.
Claim 8
Dependent Claim
93 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a first electrode comprised of a first film of a mixture of first and second metals over a semiconductor substrate; (b) a step of forming a dielectric film of an oxide film of said first metal by oxidizing said first electrode in such an atmosphere, containing H 2 O and H 2 , such that said first metal is oxidized and said second metal is not oxidized; and (c) a step of forming a second electrode over said dielectric film.
Claim 9
Dependent Claim
93 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a first electrode comprised of a first film of a mixture of first and second metals over a semiconductor substrate; (b) a step of forming a dielectric film of an oxide film of said first metal by oxidizing said first electrode in such an atmosphere, containing H 2 O and H 2 , such that said first metal is oxidized and said second metal is not oxidized; and (c) a step of forming a second electrode over said dielectric film.
Claim 10
Dependent Claim
43 words
A process for manufacturing a semiconductor device according to claim 7, wherein said first metal is an element belonging to the IVb or Vb group whereas said second metal is at least one metal selected from the group consisting of Mo and W.
Claim 11
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim, 8 wherein said first metal is Ta whereas said second metal is W.
Claim 12
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim 8, wherein said first metal is Ta whereas said second metal is Mo.
Claim 13
Dependent Claim
130 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a MISFET having a source, a drain and a gate electrode over the surface of a semiconductor substrate; (b) a step of forming a first electrode connected electrically with one of the source and drain of said MISFET and including a first film of a mixture of a first metal and a second metal; (c) a step of depositing a dielectric film formed of an oxide film of said first metal over said first electrode; (d) a step of oxidizing said first electrode and said dielectric film in an atmosphere such that said first metal is oxidized and said second metal is not oxidized; and (e) a step of forming a second electrode over said dielectric film.
Claim 14
Dependent Claim
130 words
A process for manufacturing a semiconductor device, comprising: (a) a step of forming a MISFET having a source, a drain and a gate electrode over the surface of a semiconductor substrate; (b) a step of forming a first electrode connected electrically with one of the source and drain of said MISFET and including a first film of a mixture of a first metal and a second metal; (c) a step of depositing a dielectric film formed of an oxide film of said first metal over said first electrode; (d) a step of oxidizing said first electrode and said dielectric film in an atmosphere such that said first metal is oxidized and said second metal is not oxidized; and (e) a step of forming a second electrode over said dielectric film.
Claim 15
Dependent Claim
43 words
A process for manufacturing a semiconductor device according to claim 11, wherein said first metal is an element belonging to the IVb or Vb group whereas said second metal is at least one metal selected from the group consisting of Mo and W.
Claim 16
Dependent Claim
27 words
A process for manufacturing a semiconductor device according to claim 12, wherein the oxidation is performed in an atmosphere containing H 2 O and H 2 .
Claim 17
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim 13, wherein said first metal is Ta whereas said second metal is W.
Claim 18
Dependent Claim
22 words
A process for manufacturing a semiconductor device according to claim 14, wherein the content of said first metal is 50 atom %.
Claim 19
Dependent Claim
23 words
A process for manufacturing a semiconductor device according to claim 13, wherein said first metal is Ta whereas said second metal is Mo.
Claim 20
Dependent Claim
34 words
A process for manufacturing a semiconductor device according to claim 13, further comprising a step of forming an underlying film of silicon between said first electrode and one of said source and said drain.
Claim 21
Dependent Claim
34 words
A process for manufacturing a semiconductor device according to claim 17, further comprising a step of forming a barrier layer of an oxidation resisting conductive film between said underlaying film and said first electrode.
Claim 22
Dependent Claim
37 words
A process for manufacturing a semiconductor device according to claim 18, wherein said barrier layer is made of any selected from the group consisting of TiN, a Ti-W alloy, TiSi 2 , NiSi and CoSi 2 .
Claim 23
Dependent Claim
28 words
A process for manufacturing a semiconductor device according to claim 1, wherein the first and second metals respectively are metals that can be oxidized under different oxidizing conditions.
Claim 24
Dependent Claim
37 words
A process for manufacturing a semiconductor device according to claim 1, comprising the further step of forming a polycrystalline silicon film between the semiconductor substrate and said first film, said first electrode including said polycrystalline silicon film.
Claim 25
Dependent Claim
39 words
A process for manufacturing a semiconductor device according to claim 21, further comprising the step of forming a barrier layer between the polycrystalline silicon film and the first film, so as to reduce oxidation of the polycrystalline silicon film.
Claim 26
Dependent Claim
27 words
A process for manufacturing a semiconductor device according to claim 21, including the further step of forming a refractory metal silicide film on the polycrystalline silicon film.
Claim 27
Dependent Claim
63 words
A process for manufacturing a semiconductor device according to claim 23, wherein the further step of forming a refractory metal silicide film includes sub-steps of forming a refractory metal film on the polycrystalline silicon film and silicifying the refractory metal film to form the refractory metal silicide film, whereby the refractory metal silicide film is formed in self-alignment with the polycrystalline silicon film.
Claim 28
Dependent Claim
31 words
A process for manufacturing a semiconductor device according to claim 24, wherein the refractory metal film is made of a metal selected from the group consisting of titanium, nickel and cobalt.
Claim 29
Dependent Claim
46 words
A process for manufacturing a semiconductor device according to claim 1, wherein the semiconductor substrate has a groove therein, an inner surface of the semiconductor substrate forming surfaces of the groove, and the first electrode comprised of the first film is formed over said inner surface.
Claim 30
Dependent Claim
22 words
A process for manufacturing a semiconductor device according to claim 11, wherein said first electrode is formed to overlap said gate electrode.
Claim 31
Dependent Claim
41 words
A process for manufacturing a semiconductor device according to claim 7, wherein said semiconductor substrate has a groove therein, an inner surface of the semiconductor substrate forming surfaces of the groove, and the first electrode is formed overlying said inner surface.
Claim 32
Dependent Claim
28 words
A process for manufacturing a semiconductor device according to claim 11, wherein said first electrode, dielectric film and second electrode form a capacitor element of the semiconductor device.
References Cited (Backward Citations)
JPS5629340A
Cited
US4495219A
Cited
US5035957A
Cited
US4437139A
Cited
JPS61101069A
Cited
US5079191A
Cited
US4891684A
Cited
JPS63312664A
Cited
US4962414A
Cited
JPH02151060A
Cited
US5070379A
Cited
US4999155A
Cited
US5126283A
Cited
US5142438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-08 | 1998-02-07 | 1998-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-08 | 2002-02-07 | 2002-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-08 | 2006-02-07 | 2006-08-09 | $7700.00 | Window Closed / Lapsed |