Methods of manufacturing porous metal alloy fuel cell components
Assignee: Electric Power Research Institute
•
Filing: 1992-05-12
•
Granted: 1994-05-17
•
Expires: 2012-05-12
Abstract
Abstract Porous metal components for high temperature fuel cells which are made by integrating the heretofore employed, separate tape casting and pack cementation processes. Particles of a base metal and a master alloy are suspended in a liquid medium in which a binding agent and a halide activator are dispersed. The suspension is cast into the shape wanted in the component, typically by tape casting; and the cast structure is heated to remove the liquid medium, leaving a flexible, green cast structure commonly referred to as a tape. The green tape is so heated as to: (a) burn out the binder in the tape; (b) form an alloy of the base metal and an alloying metal in the master alloy; and (c) sinter the alloy particles into a porous, coherent metal structure.
Inventors
- 👤 Diane S. Erickson
- 👤 Estela T. Ong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:23
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/8605; H01M4/8621; B; B22; B22F; B22F3/00; B22F3/10; B22F3/1003; B22F3/11; B22F3/1121; B22F3/22; H01M4/88; H01M4/8825; H01M4/8857; H01M4/8878; H01M4/8882; H01M4/8885; H01M4/90; H01M4/9041; B22F2998/00; B22F2999/00; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M2300/0051; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
217 words
A method of manufacturing a porous metal alloy component for a high temperature fuel cell, said method comprising the steps of: suspending particles of a base metal and a master alloy in a liquid medium which has dispersed therein a binding agent and a halide activator; casting the suspension thus formed; removing the liquid medium from the cast suspension to form a porous green structure in which the particles of base metal and master alloy and the halide activator are uniformly distributed; and so heat treating the green structure as to: (a) burn out the binder phase of the structure, (b) form an alloy of the master alloy and the base metal, and (c) sinter together into a coherent, porous, metallic structure the particles of the alloy formed by heat treating the green component structure, the green structure being heat treated in an environment effective to prevent oxidation of the alloy or its constituents and by heating said structure at atmospheric pressure to a temperature in the range of 800° C. to 1200° C. over a period of 3 to 15 hours, holding the structure at the temperature to which it is heated for a period of 30 to 120 minutes, and then cooling the structure to ambient temperature over a period of 2 to 8 hours.
Claim 2
Independent Claim
217 words
A method of manufacturing a porous metal alloy component for a high temperature fuel cell, said method comprising the steps of: suspending particles of a base metal and a master alloy in a liquid medium which has dispersed therein a binding agent and a halide activator; casting the suspension thus formed; removing the liquid medium from the cast suspension to form a porous green structure in which the particles of base metal and master alloy and the halide activator are uniformly distributed; and so heat treating the green structure as to: (a) burn out the binder phase of the structure, (b) form an alloy of the master alloy and the base metal, and (c) sinter together into a coherent, porous, metallic structure the particles of the alloy formed by heat treating the green component structure, the green structure being heat treated in an environment effective to prevent oxidation of the alloy or its constituents and by heating said structure at atmospheric pressure to a temperature in the range of 800° C. to 1200° C. over a period of 3 to 15 hours, holding the structure at the temperature to which it is heated for a period of 30 to 120 minutes, and then cooling the structure to ambient temperature over a period of 2 to 8 hours.
Claim 3
Dependent Claim
35 words
A method as defined in claim 1 in which the base metal is selected from the group consisting of nickel, iron, cobalt, copper, silver, chromium, platinum, palladium, neodymium, rhodium, ruthenium, gold, cadmium, zinc, and molybdenum.
Claim 4
Dependent Claim
14 words
A method as defined in claim 2 in which the base metal is nickel.
Claim 5
Dependent Claim
30 words
A method as defined in claim 1 in which the master alloy comprises an alloying element selected from the group consisting of aluminum, titanium, iron, silicon, beryllium, yttrium, and thorium.
Claim 6
Dependent Claim
22 words
A method as defined in claim 1 in which the base metal is nickel and the master alloy is a nickel-aluminum alloy.
Claim 7
Dependent Claim
22 words
A method as defined in claim 1 in which the liquid medium is removed from the cast suspension by heating the casting.
Claim 8
Dependent Claim
19 words
A method as defined in claim 1 in which the activator is a metal or ammonium chloride or fluoride.
Claim 9
Dependent Claim
90 words
A method as defined in claim 1 in which, in the course of heat treating the dried casting, said casting is heated to a temperature which is effective to: (a) effect a reaction between the activator and master alloy which results in the generation of a halide of the alloying element in vapor form and the depositing of the vapor on the particles of base metal; and (b) the subsequent inward diffusion of the alloying metal into the particles of base metal and the consequent formation of the metal alloy.
Claim 10
Dependent Claim
23 words
A method as defined in claim 1 in which the heat treating of the dried casting is carried out in a reducing atmosphere.
Claim 11
Dependent Claim
20 words
A method as defined in claim 1 in which the suspension is formed into a wanted shape by tape casting.
References Cited (Backward Citations)
US3471287A
Cited
US3617389A
Cited
US3711279A
Cited
US3658597A
Cited
US3681146A
Cited
US3661648A
Cited
US3799808A
Cited
US3802878A
Cited
US4273582A
Cited
US4206271A
Cited
US4977036A
Cited
US4386960A
Cited
US4569821A
Cited
US4444718A
Cited
US4507262A
Cited
US4659379A
Cited
US4772449A
Cited
US4664883A
Cited
US4780437A
Cited
US5028367A
Cited
US4999155A
Cited
US5110541A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-16 | 1997-11-15 | 1998-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-16 | 2001-11-15 | 2002-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-16 | 2005-11-15 | 2006-05-17 | $7700.00 | Window Closed / Lapsed |