US4780437A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fabrication of catalytic electrodes for molten carbonate fuel cells
Assignee: United States Department of Energy
•
Filing: 1987-02-11
•
Granted: 1988-10-25
•
Expires: 2007-02-11
Abstract
Abstract A porous layer of catalyst material suitable for use as an electrode in a molten carbonate fuel cell includes elongated pores substantially extending across the layer thickness. The catalyst layer is prepared by depositing particulate catalyst material into polymeric flocking on a substrate surface by a procedure such as tape casting. The loaded substrate is heated in a series of steps with rising temperatures to set the tape, thermally decompose the substrate with flocking and sinter bond the catalyst particles into a porous catalytic layer with elongated pores across its thickness. Employed as an electrode, the elongated pores provide distribution of reactant gas into contact with catalyst particles wetted by molten electrolyte.
Inventors
- 👤 James L. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:46
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/88; H01M4/8825; H01M4/8857; H01M4/8878; H01M4/8882; H01M4/8885; H01M4/90; H01M4/9016; H01M4/9041; H01M8/00; H01M8/14; H01M2008/147; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M2300/0051; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
117 words
A method of forming a porous catalytic layer having elongated pores in general alignment along the thickness thereof for use as an electrode in a molten carbonate fuel cell comprising: providing a substrate of heat consumable material with flocking on an exposed surface thereof, said flocking comprising, fibers of about 5-20 microns diameter, 0.2-5 millimeters length and at a distribution of about 5,000-50,000 per cm 2 aligned generally normal to the substrate surface; depositing particulate catalyst of no more than 100 microns particle size into the flocking on the substrate; heating the substrate with catalyst to consume the flocking a sintering, thereby leaving a porous catalytic layer with elongated pores in general alignment along the thickness thereof.
Claim 2
Independent Claim
117 words
A method of forming a porous catalytic layer having elongated pores in general alignment along the thickness thereof for use as an electrode in a molten carbonate fuel cell comprising: providing a substrate of heat consumable material with flocking on an exposed surface thereof, said flocking comprising, fibers of about 5-20 microns diameter, 0.2-5 millimeters length and at a distribution of about 5,000-50,000 per cm 2 aligned generally normal to the substrate surface; depositing particulate catalyst of no more than 100 microns particle size into the flocking on the substrate; heating the substrate with catalyst to consume the flocking a sintering, thereby leaving a porous catalytic layer with elongated pores in general alignment along the thickness thereof.
Claim 3
Dependent Claim
36 words
The method of claim 1 wherein the flocking on the substrate is formed by applying an adhesive to a substrate layer and applying flocking fibers to the adhesive in a generally normal alignment to the substrate.
Claim 4
Dependent Claim
34 words
The method of claim 2 wherein the flocking, substrate and the adhesive each consist essentially of heat-consumable organic material and leave essentially no solid residue to the porous catalytic layer following said heating step.
Claim 5
Dependent Claim
31 words
The method of claim 2 wherein the flocking and the substrate are composed of a material selected from the group of organic materials consisting of nylon, polyesters, cellulose, acetates, and cotton.
Claim 6
Dependent Claim
33 words
The method of claim 2 wherein the substrate, adhesive and the flocking are each of a different material but each having a thermal decomposition temperature less than the melting temperature of the catalyst.
Claim 7
Dependent Claim
36 words
The method of claim 1 wherein heating is conducted to a temperature in excess of 200° C. but below the catalyst melting or decomposition temperature to consume the substrate with flocking leaving substantially no solid residue.
Claim 8
Dependent Claim
30 words
The method of claim 1 wherien the particulate catalyst is dispersed into a volatile liquid forming a slip and the slip is cast as a tape into the substrate flocking.
Claim 9
Dependent Claim
35 words
The method of claim 7 wherein a heat consumable binder and plasticizer are included in the slip for tape casting and the binder and plasticizer consumed during the heating step leaving substantially no solid residue.
Claim 10
Dependent Claim
65 words
The method of claim 7 wherein the substrate and flocking with tape cast catalyst is heated to a first temperature sufficient to vaporize the slip liquid setting the tape with catalyst, to a second temperature sufficient to consume the substrate with flocking and to a third temperature sufficient to sinter the catalyst into an intergal layer with elongated pores generally aligned along the thickness thereof.
Claim 11
Dependent Claim
88 words
The method of claim 1 including the additional steps of dispersing catalytic particles of 0.1 to 1.0 microns in a liquid solvent with a binder; extruding the dispersion and vaporizing the solvent to form green fibers; sintering the green fibers at not more than about 1,000° C.; breaking the sintered fibers into elongated pieces of 5-15 microns diameter and 20-100 microns length; dispersing the broken fibers into a liquid slip and tape casting the slip with fibers into the flocking, thereby depositing said particulate catalyst into said flocking.
Claim 12
Independent Claim
114 words
A method for forming an electrode for use in a molten carbonate fuel cell comprising; horizontally positioning a heat-consumable substrate having fiberous flocking on the upper surface thereof, the fibers being in general vertical alignment; preparing a slip of particulate catalyst in carrier liquid; casting the slip as a tape into the substrate flocking; heating the substrate with cast tape to a first temperature to set the tape, to a second temperature to consume the substrate and flocking and to a third temperature to sinter bond the particulate catalyst into a porous catalytic layer having elongated pores in general alignment along the layer thickness and having fine, random distributed pores among the catalytic particles.
Claim 13
Independent Claim
114 words
A method for forming an electrode for use in a molten carbonate fuel cell comprising; horizontally positioning a heat-consumable substrate having fiberous flocking on the upper surface thereof, the fibers being in general vertical alignment; preparing a slip of particulate catalyst in carrier liquid; casting the slip as a tape into the substrate flocking; heating the substrate with cast tape to a first temperature to set the tape, to a second temperature to consume the substrate and flocking and to a third temperature to sinter bond the particulate catalyst into a porous catalytic layer having elongated pores in general alignment along the layer thickness and having fine, random distributed pores among the catalytic particles.
Claim 14
Dependent Claim
22 words
The method of claim 11 wherein the slip includes a heat-consumable binder and plasticizer which are driven off during the heating step.
Claim 15
Dependent Claim
23 words
The method of claim 11 wherein the elongated pores have diameters of about 5-20 microns and length substantially across the catalyst layer thickness.
References Cited (Backward Citations)
US2928891A
Cited
US3395049A
Cited
US3379570A
Cited
US3533753A
Cited
DE2445310A1
Cited
US4233181A
Cited
US4401519A
Cited
US4410607A
Cited
US4411968A
Cited
US4721513A
Cited
US4404267A
Cited
US4564567A
Cited
US4714586A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-25 | 1992-04-25 | 1992-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-25 | 1996-04-25 | 1996-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-25 | 2000-04-25 | 2000-10-25 | $7700.00 | Window Closed / Lapsed |