Single-cast, high-temperature, thin wall structures and methods of making the same
Assignee: Rolls Royce Corp
•
Filing: 1992-02-18
•
Granted: 1994-03-22
•
Expires: 2012-02-18
Abstract
Abstract Disclosed is a single-cast, thin wall structure capable of withstanding impinging gases at temperatures of 4300° F. and higher, and method of making the same. Using a bleed line of the instant invention allows for a decreasing metal pressure with respect to time which prevents any damage to the thin outer mold wall.
Inventors
- 👤 Kurt F. O'Connor
- 👤 James P. Hoff
- 👤 Donald J. Frasier
- 👤 Ralph E. Peeler
- 👤 Heidi Mueller-Largent
- 👤 Floyd F. Trees
- 👤 James R. Whetstone
- 👤 John H. Lane
- 👤 Ralph E. Jeffries
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:24
CPC Classifications
B; B22; B22C; B22C21/00; B22C21/12; B22C21/14; B22C19/00; B22C19/04; B22C9/00; B22C9/02; B22C9/04; B22C9/10; B22D; B22D19/00; B22D19/04; B22D19/16; F; F01; F01D; F01D5/00; F01D5/12; F01D5/14; F01D5/147; F01D5/18; F01D5/182; F01D5/184; F01D5/186; F05; F05D; F05D2230/00; F05D2230/20; F05D2230/21; F05D2230/30; F05D2230/31; F05D2260/00; F05D2260/20; F05D2260/202; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10T; Y10T428/00; Y10T428/12; Y10T428/12292; Y10T428/12361; Y10T428/12389; Y10T428/12493
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
203 words
A process of casting a molten alloy into a mold cavity having a thickness of less than about 0.03 inches, defined at least partially by a ceramic shell, so that said shell is not substantially distorted and said mold cavity is not substantially expanded during the casting step comprising; charging molten alloy into a mold reservoir which communicates with a charge line and a mold cavity defined by a ceramic shell and having a thickness less than about 0.03 inches, wherein the amount of molten alloy charged into the reservoir is sufficient for the molten alloy to flow by gravity from the reservoir through the charge line and to completely fill the mold cavity having a thickness less than about 0.03 inches; bleeding off molten alloy at a location above the mold cavity having a thickness less than about 0.03 inches so that the alloy pressure in the mold cavity is decreased over time and so that the ceramic shell is not substantially distorted and the mold cavity is not substantially expanded during the casting process; and solidifying the molten alloy to produce a solid metal part having a portion with a thickness less than about 0.03 inches corresponding to the mold cavity.
Claim 2
Dependent Claim
203 words
A process of casting a molten alloy into a mold cavity having a thickness of less than about 0.03 inches, defined at least partially by a ceramic shell, so that said shell is not substantially distorted and said mold cavity is not substantially expanded during the casting step comprising; charging molten alloy into a mold reservoir which communicates with a charge line and a mold cavity defined by a ceramic shell and having a thickness less than about 0.03 inches, wherein the amount of molten alloy charged into the reservoir is sufficient for the molten alloy to flow by gravity from the reservoir through the charge line and to completely fill the mold cavity having a thickness less than about 0.03 inches; bleeding off molten alloy at a location above the mold cavity having a thickness less than about 0.03 inches so that the alloy pressure in the mold cavity is decreased over time and so that the ceramic shell is not substantially distorted and the mold cavity is not substantially expanded during the casting process; and solidifying the molten alloy to produce a solid metal part having a portion with a thickness less than about 0.03 inches corresponding to the mold cavity.
Claim 3
Dependent Claim
79 words
A method as set forth in claim 1 further comprising the step of providing a mold apparatus including a molten alloy reservoir, a molten alloy charge line communicating with the reservoir and said mold cavity, and a bleed line communicating with said charge line and positioned to decrease the alloy charge pressure to the mold cavity over time so that the entire cavity is filled with molten alloy and the mold cavity does not expand during the casting process.
Claim 4
Dependent Claim
17 words
A method as set forth in claim 2 wherein said bleed line includes a restricted control orifice.
Claim 5
Dependent Claim
30 words
A method as set forth in claim 3 wherein said bleed line and restricted control orifice are above the mold cavity having a thickness of less than about 0.03 inches.
Claim 6
Dependent Claim
27 words
A method as set forth in claim 1 wherein the mold cavity is constructed an arranged to define a thin wall of a jet engine turbine blade.
Claim 7
Independent Claim
179 words
A method of making a multi-wall alloy structure comprising: providing a main core corresponding to a void in said structure; providing a first removable pattern material covering said main core corresponding to a first wall of said structure; providing a thin core having a density greater than 70 percent in fixed relationship to said main core so as to correspond to a thin passageway in said structure; providing a second removable pattern material covering said thin core so as to correspond to a thin wall in said structure having a thickness of less than 0.03 inches; surrounding said second removable pattern with a casting mold so as to define the outer surface of said thin wall; removing said patterns to leave said cores in fixed relationship with each other and said casting mold; charging said casting mold with molten alloy and varying the charge pressure with time so that said thin wall is formed without causing said casting mold to creep; solidifying said molten alloy and removing said casting mold and said cores to provide said multi-wall alloy structure.
Claim 8
Independent Claim
179 words
A method of making a multi-wall alloy structure comprising: providing a main core corresponding to a void in said structure; providing a first removable pattern material covering said main core corresponding to a first wall of said structure; providing a thin core having a density greater than 70 percent in fixed relationship to said main core so as to correspond to a thin passageway in said structure; providing a second removable pattern material covering said thin core so as to correspond to a thin wall in said structure having a thickness of less than 0.03 inches; surrounding said second removable pattern with a casting mold so as to define the outer surface of said thin wall; removing said patterns to leave said cores in fixed relationship with each other and said casting mold; charging said casting mold with molten alloy and varying the charge pressure with time so that said thin wall is formed without causing said casting mold to creep; solidifying said molten alloy and removing said casting mold and said cores to provide said multi-wall alloy structure.
Claim 9
Dependent Claim
29 words
A method as set forth in claim 6 wherein said step of solidifying is carried out so as to produce an alloy structure having a single crystal structure throughout.
Claim 10
Dependent Claim
40 words
A method as set forth in claim 6 wherein said thin core is held in a fixed position with said main core and said casting mold by thin rods having a diameter ranging from about 0.009 to about 0.55 inches.
Claim 11
Dependent Claim
33 words
A method as set forth in claim 8 wherein at least one of said rods extend through said thin core and has one end received in a pocket formed in said main core.
Claim 12
Dependent Claim
23 words
A method as set forth in claim 6 wherein the said thin core has a thickness ranging from about 0.005 to 0.03 inches.
Claim 13
Dependent Claim
20 words
A method as set forth in claim 6 wherein said thin core has a density of at least 99 percent.
Claim 14
Dependent Claim
16 words
A method as set forth in claim 10 wherein said thin core is radial in shape.
Claim 15
Dependent Claim
22 words
A method as set forth in claim 6 further comprising the step of laser patterning pedestals and indentations into said thin core.
Claim 16
Dependent Claim
19 words
A method as set forth in claim 11 further comprising laser patterning indentations and pedestals into said thin core.
Claim 17
Dependent Claim
69 words
A method as set forth in claim 6 further comprising forming a hole through the second pattern and a hole at least into the thin core, inserting a rod having a diameter ranging from 0.009 to 0.55 inches through the hole in second pattern and into the thin core, so that said rod forms a hole through the thin wall of the solidified alloy corresponding to the second pattern.
Claim 18
Dependent Claim
32 words
A method as set forth in claim 15 wherein said second pattern has a portion with a curved shape and said rod and second pattern hole are located in the curved portion.
Claim 19
Dependent Claim
40 words
A method as set forth in claim 6 wherein said second removable pattern comprises wax, and further comprising the step of said blasting the outer surface of the wax pattern prior to surrounding the second pattern with a casting mold.
Claim 20
Dependent Claim
15 words
A method as set forth in claim 6 wherein said main core is resin free.
Claim 21
Dependent Claim
22 words
A process as set forth in claim 1 wherein said mold cavity has a thickness ranging from about 0.005 to 0.012 inches.
Claim 22
Dependent Claim
14 words
A method as set forth in claim 10 wherein said thin core is contoured.
Claim 23
Dependent Claim
24 words
A method as set forth in claim 13 wherein said thin core has a thickness ranging from about 0.008 inches to about 0.012 inches.
Claim 24
Independent Claim
298 words
A method comprising: providing a main ceramic core; covering said main ceramic core with a first pattern where an alloy is to be cast; placing a very thin core on said pattern, said thin core having a thickness less than about 0.02 inches and a density greater than about 70 percent, and said thin core positioned to have a curved shape; providing a hole through said curved thin core, first pattern and into said main core to form a pocket in said main core to receive a portion of a first narrow rod; inserting a portion of a rod through said thin core so that the longitudinal axis of said rod and the outer surface of said thin core away from said main core are at substantially right angles, through said first pattern and so that a portion of said rod is firmly received in said pocket formed of said main core; covering said thin core with a second pattern where an alloy is to be cast; providing a hole through said second pattern and into said thin core but not extending therethrough to provide an angled pocket in said thin core for receiving a second rod at a predetermined position where force is needed to keep said thin core in a position such that said thin core has a curved shape; inserting a second rod in the hole in said second pattern and so that said second rod is received in the pocket of said thin core; surrounding said second pattern with a casting mold so that said casting mold carries one end of said second rod and so that upon removing said patterns said cores are held in a fixed relationship to each other and said casting mold, and said curved thin core retains its shape.
Claim 25
Independent Claim
298 words
A method comprising: providing a main ceramic core; covering said main ceramic core with a first pattern where an alloy is to be cast; placing a very thin core on said pattern, said thin core having a thickness less than about 0.02 inches and a density greater than about 70 percent, and said thin core positioned to have a curved shape; providing a hole through said curved thin core, first pattern and into said main core to form a pocket in said main core to receive a portion of a first narrow rod; inserting a portion of a rod through said thin core so that the longitudinal axis of said rod and the outer surface of said thin core away from said main core are at substantially right angles, through said first pattern and so that a portion of said rod is firmly received in said pocket formed of said main core; covering said thin core with a second pattern where an alloy is to be cast; providing a hole through said second pattern and into said thin core but not extending therethrough to provide an angled pocket in said thin core for receiving a second rod at a predetermined position where force is needed to keep said thin core in a position such that said thin core has a curved shape; inserting a second rod in the hole in said second pattern and so that said second rod is received in the pocket of said thin core; surrounding said second pattern with a casting mold so that said casting mold carries one end of said second rod and so that upon removing said patterns said cores are held in a fixed relationship to each other and said casting mold, and said curved thin core retains its shape.
Claim 26
Dependent Claim
13 words
A method as set forth in claim 22 wherein said rod comprises quartz.
Claim 27
Dependent Claim
14 words
A method as set forth in claim 22 wherein said thin core comprises quartz.
Claim 28
Dependent Claim
20 words
A method as set forth in claim 22 wherein said thin core has a tendency to move out of position.
Claim 29
Dependent Claim
32 words
A method as set forth in claim 22 further comprising removing said patterns, casting a molten alloy in said casting mold and solidifying said alloy, and removing said rods and casting mold.
Claim 30
Dependent Claim
49 words
A method as set forth in claim 22 wherein said second pattern has a thickness less than about 0.03 inches and further comprising decreasing the alloy charge pressure over time so that the void left by said second pattern is completely filled without causing the casting mold to creep.
Claim 31
Dependent Claim
59 words
A method as set forth in claim 22 further comprising the steps of placing a second rod having a thickness ranging from about 0.009 inches to about 0.55 inches through said first removable pattern material so that when said molten alloy is solidified said second rod provides a hole through the wall corresponding to the first removable pattern material.
Claim 32
Dependent Claim
39 words
A method as set forth in claim 22 further comprising the step of decreasing the alloy charge pressure over time so that the void left by said second pattern is completely filled without causing the mold cavity to expand.
Claim 33
Dependent Claim
176 words
A process of casting a molten alloy into a substantially long mold cavity defined at least partially by a ceramic shell, so that the ceramic shell defining the mold cavity is not substantially distorted and the mold cavity is not substantially expanded during the casting process comprising charging molten alloy into a mold reservoir which communicates with a charge line and a mold cavity defined by a ceramic shell wherein the amount of molten alloy charged into the reservoir is sufficient for the molten alloy to flow by gravity from the reservoir through the charge line and to completely fill the mold cavity; bleeding off molten alloy at a location above the mold cavity though a bleed line having a control orifice therein so that the alloy pressure in the mold cavity is decreased over time and so that the ceramic shell is not substantially distorted and the mold cavity is not substantially expanded during the casting process; and solidifying the molten alloy to produce a solid metal part having dimensions corresponding to the mold cavity.
Claim 34
Dependent Claim
176 words
A process of casting a molten alloy into a substantially long mold cavity defined at least partially by a ceramic shell, so that the ceramic shell defining the mold cavity is not substantially distorted and the mold cavity is not substantially expanded during the casting process comprising charging molten alloy into a mold reservoir which communicates with a charge line and a mold cavity defined by a ceramic shell wherein the amount of molten alloy charged into the reservoir is sufficient for the molten alloy to flow by gravity from the reservoir through the charge line and to completely fill the mold cavity; bleeding off molten alloy at a location above the mold cavity though a bleed line having a control orifice therein so that the alloy pressure in the mold cavity is decreased over time and so that the ceramic shell is not substantially distorted and the mold cavity is not substantially expanded during the casting process; and solidifying the molten alloy to produce a solid metal part having dimensions corresponding to the mold cavity.
References Cited (Backward Citations)
US3659645A
Cited
JPS5124976A
Cited
US4077458A
Cited
US4421153A
Cited
US4552198A
Cited
US4617977A
Cited
JPS60177946A
Cited
US4811778A
Cited
US4986333A
Cited
US5234045A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-21 | 1997-09-20 | 1998-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-21 | 2001-09-20 | 2002-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-21 | 2005-09-20 | 2006-03-22 | $7700.00 | Window Closed / Lapsed |