Removing refractory material from components
Assignee: Rolls Royce PLC
•
Filing: 1981-10-02
•
Granted: 1985-11-12
•
Expires: 2001-10-02
Abstract
Abstract A method of removing refractory material from a component comprises contacting the refractory material with a chemically active agent whereby to convert the refractory material to a more easily removable substance, and removing the more easily removable substance. The method enables alumina cores defining cooling passages in cast blades for use in gas turbine engines to be removed at practically useful rates.
Inventors
- 👤 David Mills
- 👤 Alan D. Kington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:37
CPC Classifications
B; B22; B22D; B22D29/00; B22D29/001; B22D29/002; B22C; B22C1/00; B22C9/00; B22C9/10
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
107 words
A method of casting a component having an opening therein comprising the steps of: inserting into a mold a refractory material of high temperature fired re-crystallized substantially 100% dense pure metal oxides defining the opening; introducing into the mold molten component material; solidifying the component; and removing the refractory material by chemically reacting it with nascent hydrogen produced by immersing the casting in an aqueous solution of a hydroxide or hydride of a metal selected from sodium, potassium and lithium and containing substantially 10-35% W/V of water and leaching the resultant products; all the while heating the solution to a temperature in the range of 150°-370° C.
Claim 2
Independent Claim
107 words
A method of casting a component having an opening therein comprising the steps of: inserting into a mold a refractory material of high temperature fired re-crystallized substantially 100% dense pure metal oxides defining the opening; introducing into the mold molten component material; solidifying the component; and removing the refractory material by chemically reacting it with nascent hydrogen produced by immersing the casting in an aqueous solution of a hydroxide or hydride of a metal selected from sodium, potassium and lithium and containing substantially 10-35% W/V of water and leaching the resultant products; all the while heating the solution to a temperature in the range of 150°-370° C.
Claim 3
Dependent Claim
19 words
A method according to claim 1 wherein the component is a blade for use in a gas turbine engine.
Claim 4
Independent Claim
85 words
A method of removing a casting core of high-temperature fired re-crystallized substantially 100% dense pure metal oxides from a metal casting, comprising the steps of: chemically reacting the core with nascent hydrogen produced by immersing the casting containing the core in an aqueous solution of a hydroxide or hydride of a metal selected from sodium, potassium and lithium and containing substantially 10-35% W/V of water and leaching the resultant products; all the while heating the solution to a temperature in the range of 150°-370° C.
Claim 5
Independent Claim
85 words
A method of removing a casting core of high-temperature fired re-crystallized substantially 100% dense pure metal oxides from a metal casting, comprising the steps of: chemically reacting the core with nascent hydrogen produced by immersing the casting containing the core in an aqueous solution of a hydroxide or hydride of a metal selected from sodium, potassium and lithium and containing substantially 10-35% W/V of water and leaching the resultant products; all the while heating the solution to a temperature in the range of 150°-370° C.
Claim 6
Dependent Claim
34 words
A method according to claim 3 wherein the method is carried out at a temperature in the range from substantially 200° C. to substantially 350° C. and at a pressure of substantially 1 atmosphere.
Claim 7
Dependent Claim
32 words
A method according to claim 3 wherein the solution comprises substantially 90% W/V potassium hydroxide and substantially 10% W/V water, the temperature is substantially 350° C. and the pressure is substantially atmospheric.
Claim 8
Dependent Claim
37 words
A method according to claim 3 wherein the solution contains substantially 65% W/V potassium hydroxide, substantially 15% W/V lithium hydroxide and substantially 20% W/V water, the temperature is substantially 350° C. and the pressure is substantially atmospheric.
Claim 9
Dependent Claim
32 words
A method according to claim 3 wherein the solution contains substantially 80% W/V sodium hydroxide and substantially 20% W/V water, the temperature is substantially 220° C. and the pressure is substantially atmospheric.
Claim 10
Dependent Claim
32 words
A method according to claim 3 wherein the solution contains substantially 65% W/V potassium hydroxide and substantially 35% W/V water, the temperature is substantially 200° C. and the pressure is substantially atmospheric.
Claim 11
Dependent Claim
33 words
A method according to claim 3 wherein the solution contains substantially 65% W/V potassium hydroxide and substantially 35% W/V water, the temperature is substantially 370° C. and the pressure is substantially 3 atmospheres.
Claim 12
Dependent Claim
33 words
A method according to claim 3 wherein the solution contains substantially 60% W/V potassium hydroxide and substantially 40% W/V water, the temperature is substantially 350° C. and the pressure is substantially 100 atmospheres.
Claim 13
Dependent Claim
45 words
A method according to claim 3 wherein the solution contains substantially 80% W/V sodium hydroxide and substantially 20% W/V water, the pressure is substantially 5 atmosphere and the temperature is repeatedly increased from substantially 150° C. to substantially 157° C. to boil the solution repeatedly.
Claim 14
Dependent Claim
14 words
A method according to claim 3 wherein the refractory material is of tubular form.
Claim 15
Dependent Claim
12 words
A method according to claim 3 wherein the refractory material is alumina.
Claim 16
Dependent Claim
12 words
A method according to claim 3 wherein the refractory material is magnesia.
Claim 17
Dependent Claim
12 words
A method according to claim 3 wherein the refractory material is steatite.
Claim 18
Dependent Claim
12 words
A method according to claim 3 wherein the metal oxide is spinel.
Claim 19
Dependent Claim
18 words
A method according to claim 1 wherein the step of solidifying the component comprises directionally solidifying the component.
Claim 20
Dependent Claim
19 words
A method according to claim 3 wherein the component is a blade for use in a gas turbine engine.
Claim 21
Dependent Claim
14 words
A method according to claim 3 wherein the solution is heated in an autoclave.
References Cited (Backward Citations)
GB926012A
Cited
US3044087A
Cited
GB1211824A
Cited
SU370281A1
Cited
GB1419896A
Cited
US4043377A
Cited
US4102689A
Cited
US4162173A
Cited
US4134777A
Cited
US4141781A
Cited
GB2005169A
Cited
US4184885A
Cited
US4372805A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |