Laser transfer process
Assignee: TE Connectivity Corp
•
Filing: 1992-01-10
•
Granted: 1994-03-08
•
Expires: 2012-01-10
Abstract
Abstract This invention relates to a method for producing a smooth continuous and adherent pressure bonded or cold welded layer of a metal containing composite on a base or target material through the driving force of a pulsed laser. The method includes the steps of selecting a laser transparent substrate, applying thereto a thin laser absorptive polymeric film characterized by a high optical coefficient of absorption to the wavelength of said laser, applying the metal containing composite to the absorptive polymeric film, and placing the base or target material in close proximity to said composite. The composite is a multilayered composite comprising laser absorptive polymer, gold, nickel and gold-flash, and the pulsed laser energy is directed through the transparent substrate toward said composite and is absorbed by the polymeric film causing heating and vaporization thereof while leaving portions of the polymeric film unvaporized. The vaporization provides the necessary pressure to blowoff the unvaporized portions of the absorptive polymeric film so as to propel the composite onto the base or target material.
Inventors
- 👤 James L. Joyce, Jr.
- 👤 Marlin R. McCleaf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:27
CPC Classifications
C; C23; C23C; C23C26/00; C23C26/02; H; H05; H05K; H05K3/00; H05K3/10; H05K3/20; H05K3/22; H05K3/24; H05K3/244; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12528; Y10T428/12535; Y10T428/12556; Y10T428/12569; Y10T428/12771; Y10T428/12861; Y10T428/12889
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
224 words
In a method for producing a smooth continuous and adherent pressure bonded or cold welded layer of a metal containing composite on a base metal through the driving force of a pulsed laser, which includes the steps of selecting a laser transparent substrate, applying to said substrate a thin polymeric film characterized by a high optical coefficient of absorption to the wavelength of said laser, applying said metal containing composite onto said thin polymeric film, and placing said base metal in close proximity to said thin polymeric film containing composite, the improvement comprising in combination therewith the steps of a) preparing said thin polymeric film containing composite as a multilayered composite comprising an absorptive polymer, a metal, nickel and a metal flash layer, and b) directing pulsed laser energy at an energy density of between about 12 and 18 J/cm 2 through said transparent substrate toward said thin polymeric film containing composite whereby said laser energy is absorbed by said thin polymeric film causing heating and vaporization of said film to a controlled depth of said film, leaving remaining portions of said film unvaporized after said depth to act as support for said composite to be pressure bonded or cold welded, said vaporization providing the necessary pressure to blowoff said remaining unvaporized portions of said film, thereby propelling said composite onto said base metal.
Claim 2
Dependent Claim
224 words
In a method for producing a smooth continuous and adherent pressure bonded or cold welded layer of a metal containing composite on a base metal through the driving force of a pulsed laser, which includes the steps of selecting a laser transparent substrate, applying to said substrate a thin polymeric film characterized by a high optical coefficient of absorption to the wavelength of said laser, applying said metal containing composite onto said thin polymeric film, and placing said base metal in close proximity to said thin polymeric film containing composite, the improvement comprising in combination therewith the steps of a) preparing said thin polymeric film containing composite as a multilayered composite comprising an absorptive polymer, a metal, nickel and a metal flash layer, and b) directing pulsed laser energy at an energy density of between about 12 and 18 J/cm 2 through said transparent substrate toward said thin polymeric film containing composite whereby said laser energy is absorbed by said thin polymeric film causing heating and vaporization of said film to a controlled depth of said film, leaving remaining portions of said film unvaporized after said depth to act as support for said composite to be pressure bonded or cold welded, said vaporization providing the necessary pressure to blowoff said remaining unvaporized portions of said film, thereby propelling said composite onto said base metal.
Claim 3
Dependent Claim
25 words
The method according to claim 1 wherein said metal of said metal containing composite is gold, gold alloy, or a plural layered composite containing gold.
Claim 4
Dependent Claim
18 words
The method according to claim 1 wherein the metal flash layer is a metal relatively inert to oxidation.
Claim 5
Dependent Claim
24 words
The method according to claim 3 wherein the metal relatively inert to oxidation is selected from the group consisting of gold, indium or palladium.
Claim 6
Dependent Claim
18 words
The method according to claim 1 wherein the multilayered composite is prepared by sputter deposition in a vacuum.
Claim 7
Dependent Claim
25 words
The method according to claim 4 wherein the metal relatively inert to oxidation is gold having a thickness on the order of about 120 angstroms.
Claim 8
Dependent Claim
18 words
The method according to claim 1 wherein the multilayered composite is prepared by arc deposition in a vacuum.
Claim 9
Dependent Claim
17 words
The method according to claim 1 wherein the multilayered composite is prepared by evaporation in a vacuum.
References Cited (Backward Citations)
US4427498A
Cited
US4534843A
Cited
US4666796A
Cited
US4929516A
Cited
US4752455A
Cited
US4895771A
Cited
US5066550A
Cited
US4987006A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-07 | 1997-09-06 | 1998-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-07 | 2001-09-06 | 2002-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-07 | 2005-09-06 | 2006-03-08 | $7700.00 | Window Closed / Lapsed |