US5291575A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manufacturing method for waveguide-type optical components
Assignee: Furukawa Electric Co Ltd
•
Filing: 1992-07-21
•
Granted: 1994-03-01
•
Expires: 2012-07-21
Abstract
Abstract A method for manufacturing waveguide-type optical components featuring a lower propagation loss at low cost in which a lower clad section (2) made of silica glass is formed on a substrate (1), and an antistatic layer and a mask layer having a desired pattern are formed on the surface of the lower clad section (2) in the order they are listed. Then, an electron beam is irradiated from above the mask layer to produce a core (6) of the desired pattern in the lower clad section (2), the mask layer and the antistatic layer are removed to expose the surface of the lower clad section (2), and an upper clad section (7) having a lower refractive index than the core (6) is formed on the exposed surface of the lower clad section (2), thus producing an optical component. The surface of the whole optical component is at a distance from the core; therefore, the scattering loss caused by minute irregularities on the surface of the optical component is reduced.
Inventors
- 👤 Hisaharu Yanagawa
- 👤 Ken Ueki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:58
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
158 words
A manufacturing method for waveguide-type optical components, comprising: (a) forming a lower clad section, which is made of silica glass, on a substrate; (b) forming an antistatic layer and a mask layer, which has a desired pattern, on the surface of said lower clad section in the order listed; (c) forming a core of said desired pattern in said lower clad section by irradiating an electron beam from above said mask layer toward said lower clad section; (d) removing said mask layer and said antistatic layer, after said core is formed, to expose the surface of said lower clad section; and (e) forming an upper clad section, which has a lower refractive index than said core, on the exposed surface of said lower clad section and over said core, said upper clad section having a thickness of at least 0.1 μm to reduce scattering loss caused by minute irregularities produced on a surface of said upper clad section.
Claim 2
Dependent Claim
158 words
A manufacturing method for waveguide-type optical components, comprising: (a) forming a lower clad section, which is made of silica glass, on a substrate; (b) forming an antistatic layer and a mask layer, which has a desired pattern, on the surface of said lower clad section in the order listed; (c) forming a core of said desired pattern in said lower clad section by irradiating an electron beam from above said mask layer toward said lower clad section; (d) removing said mask layer and said antistatic layer, after said core is formed, to expose the surface of said lower clad section; and (e) forming an upper clad section, which has a lower refractive index than said core, on the exposed surface of said lower clad section and over said core, said upper clad section having a thickness of at least 0.1 μm to reduce scattering loss caused by minute irregularities produced on a surface of said upper clad section.
Claim 3
Dependent Claim
24 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said upper clad section is formed by a flame hydrolysis deposition method.
Claim 4
Dependent Claim
26 words
The manufacturing method for waveguide-type optical components according to claim 1, comprising forming said upper clad section to have a thickness of at least 20 μm.
Claim 5
Dependent Claim
19 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said antistatic layer is an aluminum layer.
Claim 6
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 4, wherein said mask layer is a thin gold layer.
Claim 7
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said mask layer is a thin gold layer.
Claim 8
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said mask layer is a metallic thin-film layer.
Claim 9
Dependent Claim
21 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said upper clad section is made of silica glass.
Claim 10
Dependent Claim
32 words
The manufacturing method for waveguide-type optical components according to claim 1, wherein said removing step comprises removing said mask layer and said antistatic layer in sequence, said mask layer being removed first.
Claim 11
Dependent Claim
158 words
A manufacturing method for waveguide-type optical components, comprising: (a) forming a lower clad section, which is made of silica glass, on a substrate; (b) forming an antistatic layer and a mask layer, which has a desired pattern, on the surface of said lower clad section in the order listed; (c) forming a core of said desired pattern in said lower clad section by irradiating an electron beam from above said mask layer toward said lower clad section; (d) removing said mask layer and said antistatic layer, after said core is formed, to expose the surface of said lower clad section; and (e) forming an upper clad section, which has a lower refractive index than said core, on the exposed surface of said lower clad section; and wherein said upper clad section is formed to have a thickness which is sufficient to substantially reduce scattering loss caused by minute irregularities produced on a surface of said upper clad section.
Claim 12
Dependent Claim
158 words
A manufacturing method for waveguide-type optical components, comprising: (a) forming a lower clad section, which is made of silica glass, on a substrate; (b) forming an antistatic layer and a mask layer, which has a desired pattern, on the surface of said lower clad section in the order listed; (c) forming a core of said desired pattern in said lower clad section by irradiating an electron beam from above said mask layer toward said lower clad section; (d) removing said mask layer and said antistatic layer, after said core is formed, to expose the surface of said lower clad section; and (e) forming an upper clad section, which has a lower refractive index than said core, on the exposed surface of said lower clad section; and wherein said upper clad section is formed to have a thickness which is sufficient to substantially reduce scattering loss caused by minute irregularities produced on a surface of said upper clad section.
Claim 13
Dependent Claim
24 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said upper clad section is formed by a flame hydrolysis deposition method.
Claim 14
Dependent Claim
26 words
The manufacturing method for waveguide-type optical components according to claim 10, comprising forming said upper clad section to have a thickness of at least 0.1 μm.
Claim 15
Dependent Claim
26 words
The manufacturing method for waveguide-type optical components according to claim 10, comprising forming said upper clad section to have a thickness of at least 20 μm.
Claim 16
Dependent Claim
19 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said antistatic layer is an aluminum layer.
Claim 17
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 14, wherein said mask layer is a thin gold layer.
Claim 18
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said mask layer is a thin gold layer.
Claim 19
Dependent Claim
20 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said mask layer is a metallic thin-film layer.
Claim 20
Dependent Claim
21 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said upper clad section is made of silica glass.
Claim 21
Dependent Claim
32 words
The manufacturing method for waveguide-type optical components according to claim 10, wherein said removing step comprises removing said mask layer and said antistatic layer in sequence, said mask layer being removed first.
References Cited (Backward Citations)
JPS602906A
Cited
US4831628A
Cited
JPS6145202A
Cited
JPS61204603A
Cited
US4789642A
Cited
US5178658A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-28 | 1997-08-30 | 1998-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-28 | 2001-08-30 | 2002-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-28 | 2005-08-30 | 2006-03-01 | $7700.00 | Window Closed / Lapsed |