Abstract
Abstract Disclosed is an ink composition comprising an aqueous liquid vehicle and pigment particles having attached to the surfaces thereof a polymerized vinyl aromatic salt. In one embodiment, the polymeric vinyl aromatic salt is chemically grafted to the surfaces of the pigment particles; in another embodiment, the polymeric vinyl aromatic salt is adsorbed onto the surfaces of the pigment particles. Preferably, the modified pigment particles have an average particle diameter of less than about 1 micron. The ink composition is suitable for applications such as ink jet printing processes, particularly thermal ink jet printing processes. Images generated with ink compositions of the present invention are sharp, waterfast, lightfast, and of high optical density, exhibiting no feathering, and can be electrically conductive.
Inventors
- 👤 John W. Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:55
CPC Classifications
C; C08; C08F; C08F290/00; C08F290/02; B; B82; B82Y; B82Y30/00; C09; C09B; C09B67/00; C09B67/0001; C09B67/0004; C09B67/0008; C09B67/0013; C09B68/00; C09B68/20; C09B68/26; C09B68/40; C09B68/42; C09B68/425; C09B68/4253; C09B68/46; C09C; C09C1/00; C09C1/44; C09C1/48; C09C1/56; C09C3/00; C09C3/10; C09D; C09D11/00; C09D11/30; C09D11/32; C09D11/322; C01; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/64; C01P2006/00; C01P2006/22; C01P2006/60; C01P2006/80
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
41 words
An ink jet ink composition comprising an aqueous liquid vehicle which comprises water and a humectant and pigment particles having chemically grafted to the surfaces thereof a polymerized vinyl aromatic salt, said ink having a viscosity of 10 centipoise or less.
Claim 2
Dependent Claim
41 words
An ink jet ink composition comprising an aqueous liquid vehicle which comprises water and a humectant and pigment particles having chemically grafted to the surfaces thereof a polymerized vinyl aromatic salt, said ink having a viscosity of 10 centipoise or less.
Claim 3
Dependent Claim
15 words
An ink jet ink composition according to claim 1 wherein the pigment is carbon black.
Claim 4
Dependent Claim
32 words
An ink jet ink composition according to claim 1 wherein the pigment particles are nonmutagenic nontoxic carbon black particles with a polyaromatic hydrocarbon content of less than about 1 part per million.
Claim 5
Dependent Claim
36 words
An ink jet ink composition according to claim 1 wherein the pigment is selected from the group consisting of cyan pigments, magenta pigments, yellow pigments, red pigments, blue pigments, green pigments, orange pigments, and mixtures thereof.
Claim 6
Dependent Claim
67 words
An ink jet ink composition according to claim 1 wherein the vinyl aromatic salt is of the formula ##STR2## wherein R is an aromatic moiety, X is an acid salt functional group, and R 1 , R 2 , and R 3 are independently selected from the group consisting of hydrogen, alkyl groups, substituted alkyl groups, aromatic groups, substituted aromatic groups, heterocyclic groups, and substituted heterocyclic groups.
Claim 7
Dependent Claim
55 words
An ink jet ink compositon according to claim 1 wherein the humectant is selected from the group consisting of ethylene glycol, propylene glycol, diethylene glycols, glycerine, dipropylene glycols, polyethylene glycols, polypropylene glycols, amides, ethers, carboxylic acids, esters, alcohols, organosulfides, organosulfoxides, sulfones, alcohol derivatives, carbitol, butyl carbitol, cellusolve, ether derivatives, amino alcohols, ketones, and mixtures thereof.
Claim 8
Dependent Claim
44 words
An ink jet ink composition according to claim 1 wherein the liquid vehicle comprises water in an amount of from about 40 to about 97 percent by weight and a humectant in an amount of from about 3 to about 60 percent by weight.
Claim 9
Dependent Claim
26 words
An ink jet ink composition according to claim 1 wherein the pigment particles have an average particle diameter of from about 0.001 to about 10 microns.
Claim 10
Dependent Claim
24 words
An ink jet ink composition according to claim 1 wherein the pigment particles have an average particle diameter of less than about 1 micron.
Claim 11
Dependent Claim
40 words
An ink jet ink composition according to claim 1 wherein the pigment particles having the polymerized vinyl aromatic salt attached thereto are present in the ink composition in an amount of from about 0.1 to about 15 percent by weight.
Claim 12
Dependent Claim
89 words
An ink jet ink composition according to claim 1 wherein the vinyl aromatic salt is of the formula ##STR3## wherein R is an aromatic moiety with from 6 to about 20 carbon atoms, X is an acid salt functional group consisting of both cation and anion moieties, and R 1 , R 2 , and R 3 are independently selected from the group consisting of hydrogen, alkyl groups with from 1 to about 20 carbon atoms, aromatic groups with from 6 to about 20 carbon atoms, and heterocyclic groups.
Claim 13
Dependent Claim
31 words
An ink jet ink composition according to claim 11 wherein R is selected from the group consisting of phenyl, substituted phenyl, naphthyl, substituted naphthyl, anthracenyl, substituted anthracenyl, and heterocyclic aromatic rings.
Claim 14
Dependent Claim
60 words
An ink jet ink composition according to claim 11 wherein X is a salt functional group wherein the cation is selected from the group consisting of Rb + , Cs + , K + , Na + , Li + , ammonium, and substituted ammonium, and the anion is selected from the group consisting of sulfonate, carboxylate, phosphate, and borate.
Claim 15
Dependent Claim
19 words
An ink jet ink composition according to claim 1 wherein the vinyl aromatic salt is of the formula ##STR4##
Claim 16
Dependent Claim
19 words
An ink jet ink composition according to claim 1 wherein the vinyl aromatic salt is a styrene sulfonate salt.
Claim 17
Dependent Claim
14 words
An ink jet ink composition according to claim 1 which also contains a dye.
Claim 18
Dependent Claim
26 words
An ink jet ink composition according to claim 16 wherein the dye is present in an amount of no more than about 15 percent by weight.
Claim 19
Dependent Claim
31 words
An ink jet ink composition according to claim 1 which also contains a dispersing agent selected from the group consisting of cationic dispersing agents, anionic dispersing agents, and nonionic dispersing agents.
Claim 20
Dependent Claim
27 words
An ink jet ink composition according to claim 18 wherein the dispersing agent is present in an amount of no more than about 40 percent by weight.
Claim 21
Dependent Claim
17 words
An ink jet ink composition according to claim 1 which also contains a water soluble polymeric additive.
Claim 22
Dependent Claim
53 words
An ink jet ink composition according to claim 20 wherein the polymeric additive is selected from the group consisting of Gum Arabic, polyacrylate salts, polymethacrylate salts, polyvinyl alcohols, polyethylene oxides, poyethylene glycols, polypropylene glycols, hydroxy propylcellulose, hydroxyethylcellulose; polyvinylpyrrolidinone, polyvinylether, starch, polyacrylamide, lignin sulfonate salts, copolymers of naphthalene sulfonate salts and formaldehyde, and polysaccharides.
Claim 23
Dependent Claim
28 words
An ink jet ink composition according to claim 20 wherein the polymeric additive is present in an amount of from about 0.01 to about 5 percent by weight.
Claim 24
Dependent Claim
20 words
An ink jet ink composition according to claim 1 wherein the ink has a viscosity of less than 5 centipoise.
Claim 25
Dependent Claim
20 words
An ink jet ink composition according to claim 1 wherein the ink has a viscosity of less than 3 centipoise.
Claim 26
Dependent Claim
16 words
An ink jet ink composition according to claim 1 wherein the ink also contains a biocide.
Claim 27
Dependent Claim
115 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises mixing in water a pigment and a vinyl aromatic salt, attriting the mixture until the pigment particles have an average particle diameter of from about 0.001 to about 20 microns, adding to the mixture a water soluble free radical polymerization initiator and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt and chemically grafting it to the pigment particle surfaces, separating the pigment particles from the mixture, and admixing the pigment particles with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
Claim 28
Dependent Claim
115 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises mixing in water a pigment and a vinyl aromatic salt, attriting the mixture until the pigment particles have an average particle diameter of from about 0.001 to about 20 microns, adding to the mixture a water soluble free radical polymerization initiator and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt and chemically grafting it to the pigment particle surfaces, separating the pigment particles from the mixture, and admixing the pigment particles with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
Claim 29
Dependent Claim
41 words
A process according to claim 26 wherein subsequent to admixing the pigment particles with the liquid vehicle, the ink composition is subjected to centrifugation and filtration to remove pigment particles with an average particle diameter of greater than about 1 micron.
Claim 30
Dependent Claim
28 words
A process according to claim 26 wherein polymerization of the monomeric vinyl aromatic salt is carried out at a temperature of from about 20° to about 120° C.
Claim 31
Dependent Claim
30 words
A process according to claim 26 wherein the mixture of water, pigment, and monomeric vinyl aromatic salt is attrited for a period of from about 0.25 to about 28 hours.
Claim 32
Dependent Claim
92 words
A process according to claim 26 wherein prior to polymerization the mixture comprises water in an amount of from about 35 to about 98 percent by weight, pigment particles in an amount of from about 2 to about 65 percent by weight, monomeric vinyl aromatic salt in an amount of from about 0.02 to about 50 percent by weight, free radical polymerization initiator in an amount of from about 0.01 to about 15 percent by weight, and a wetting agent in an amount of from 0 to about 50 percent by weight.
Claim 33
Dependent Claim
64 words
A process according to claim 26 wherein the vinyl aromatic salt is of the formula ##STR5## wherein R is an aromatic moiety, X is an acid salt functional group, and R 1 , R 2 , and R 3 are independently selected from the group consisting of hydrogen, alkyl groups, substituted alkyl groups, aromatic groups, substituted aromatic groups, heterocyclic groups, and substituted heterocyclic groups.
Claim 34
Dependent Claim
28 words
A process according to claim 31 wherein R is selected from the group consisting of phenyl, substituted phenyl, naphthyl, substituted naphthyl, anthracenyl, substituted anthracenyl, and heterocyclic aromatic rings.
Claim 35
Dependent Claim
34 words
A process according to claim 26 wherein the pigment particles having attached to the surfaces thereof the polymerized vinyl aromatic salts have an average particle diameter of from about 0.001 to about 10 microns.
Claim 36
Dependent Claim
32 words
A process according to claim 26 wherein the pigment particles having attached to the surfaces thereof the polymerized vinyl aromatic salts have an average particle diameter of less than about 1 micron.
Claim 37
Dependent Claim
37 words
A process according to claim 26 wherein the pigment particles having the polymerized vinyl aromatic salt attached thereto are present in the ink composition in an amount of from about 0.1 to about 15 percent by weight.
Claim 38
Dependent Claim
86 words
A process according to claim 26 wherein the vinyl aromatic salt is of the formula ##STR6## wherein R is an aromatic moiety with from 6 to about 20 carbon atoms, X is an acid salt functional group consisting of both cation and anion moieties, and R 1 , R 2 , and R 3 are independently selected from the group consisting of hydrogen, alkyl groups with from 1 to about 20 carbon atoms, aromatic groups with from 6 to about 20 carbon atoms, and heterocyclic groups.
Claim 39
Dependent Claim
16 words
A process according to claim 26 wherein the vinyl aromatic salt is of the formula ##STR7##
Claim 40
Dependent Claim
16 words
A process according to claim 26 wherein the vinyl aromatic salt is a styrene sulfonate salt.
Claim 41
Dependent Claim
147 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises: a. preparing modified pigment particles by: i. first mixing together in water a free radical polymerization initiator and a monomeric vinyl aromatic salt and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt; and ii. subsequently adding to the polymerized vinyl aromatic salt pigment particles with an average particle diameter of from about 0.001 to about 10 microns, additional vinyl aromatic salt monomers, and, optionally, additional free radical polymerization initiator, thereby further polymerizing the vinyl aromatic salt and resulting in chemical grafting of the polymerized vinyl aromatic salt to the surfaces of the pigment particles; and b. admixing the modified pigment particles thus prepared with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
Claim 42
Dependent Claim
147 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises: a. preparing modified pigment particles by: i. first mixing together in water a free radical polymerization initiator and a monomeric vinyl aromatic salt and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt; and ii. subsequently adding to the polymerized vinyl aromatic salt pigment particles with an average particle diameter of from about 0.001 to about 10 microns, additional vinyl aromatic salt monomers, and, optionally, additional free radical polymerization initiator, thereby further polymerizing the vinyl aromatic salt and resulting in chemical grafting of the polymerized vinyl aromatic salt to the surfaces of the pigment particles; and b. admixing the modified pigment particles thus prepared with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
Claim 43
Dependent Claim
142 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises: a. preparing modified pigment particles by: i. first mixing together in water pigment particles with an average particle diameter of from about 0.001 to about 10 microns, a monomeric vinyl aromatic salt, and a free radical polymerization initiator and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt; and ii. subsequently adding to the mixture additional vinyl aromatic salt monomers and, optionally, additional free radical polymerization initiator, thereby further polymerizing the vinyl aromatic salt, wherein the polymerized vinyl aromatic salt is chemically grafted to the surfaces of the pigment particles; and b. admixing the modified pigment particles thus prepared with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
Claim 44
Dependent Claim
142 words
A process for preparing an ink composition suitable for ink jet printing processes which comprises: a. preparing modified pigment particles by: i. first mixing together in water pigment particles with an average particle diameter of from about 0.001 to about 10 microns, a monomeric vinyl aromatic salt, and a free radical polymerization initiator and heating the mixture under vacuum or inert atmosphere, thereby polymerizing the vinyl aromatic salt; and ii. subsequently adding to the mixture additional vinyl aromatic salt monomers and, optionally, additional free radical polymerization initiator, thereby further polymerizing the vinyl aromatic salt, wherein the polymerized vinyl aromatic salt is chemically grafted to the surfaces of the pigment particles; and b. admixing the modified pigment particles thus prepared with an aqueous liquid vehicle comprising water and a humectant to result in an ink having a viscosity of 10 centipoise or less.
References Cited (Backward Citations)
US2335505A
Cited
US2629697A
Cited
US2913429A
Cited
US3687887A
Cited
US3846141A
Cited
US3705043A
Cited
US3844994A
Cited
US3950290A
Cited
US3884871A
Cited
US4161405A
Cited
US4165399A
Cited
US4273847A
Cited
US4409039A
Cited
US4597794A
Cited
US4314931A
Cited
US4421660A
Cited
US4409040A
Cited
US4508570A
Cited
US4659773A
Cited
JPS599376A
Cited
US4530961A
Cited
US4713083A
Cited
US4680057A
Cited
US4846893A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-24 | 1997-07-26 | 1998-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-24 | 2001-07-26 | 2002-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-24 | 2005-07-26 | 2006-01-25 | $7700.00 | Window Closed / Lapsed |