Integrated circuit metallization with zero contact enclosure requirements and method of making the same
Assignee: STMicroelectronics lnc USA
•
Filing: 1991-03-27
•
Granted: 1993-12-14
•
Expires: 2011-03-27
Abstract
Abstract A method for forming aluminum metallization for contacting a conductive element in an integrated circuit, and an integrated circuit formed according to the same, is disclosed. According to a first disclosed embodiment, a first aluminum alloy layer is formed within the contact, optionally with a barrier layer between it and the underlying electrode. An etch stop layer is formed thereover, of a material which has a low etch rate to an aluminum etchant species. A second, thicker, aluminum alloy layer is formed thereover. The second aluminum layer is etched until the etch stop layer is reached; the mask for defining the metal line may have an edge within the dimensions of the contact opening. After removal of the exposed etch stop layer, a timed etch removes the first aluminum alloy layer, without exposing the bottom of the contact. The metal line may thus be safely formed, without requiring an enclosure around the contact opening. According to an alternate embodiment, conductive or semiconductive sidewall spacers may be formed, upon which the metal etch can stop, leaving a metal line within the contact dimensions. A further alternative embodiment uses a conductive etch stop layer which covers the entire contact, and upon which the metal etch can stop within the contact opening.
Inventors
- 👤 Fusen E. Chen
- 👤 Fu-Tai Liou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:51
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033; H10W20/036; H10W20/034; H10W20/054; H10W20/056; H10W20/063; H10W20/0633; H10W20/40; H10W20/41; H10W20/425; Y; Y10; Y10S; Y10S438/00; Y10S438/97
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
186 words
A method of forming an interconnection in an integrated circuit through a contact opening in an insulating layer to an underlying conductive element, comprising: forming an etch stop layer within the sidewalls of the contact opening; forming a metal layer over said etch stop layer, said metal layer comprising aluminum, in such a manner that a portion of said metal layer is disposed within said contact opening between portions of said etch stop layer within the sidewalls of the contact opening; defining a mask over a portion of said metal layer, said mask overlying said contact opening; and etching portions of said metal layer not covered by said mask, with an etchant which removes said metal layer at a significantly greater rate than it removes said etch stop layer, to expose portions of said etch stop layer thereunder; wherein said mask is sized in such a manner that said metal layer, after said etching step, has an edge which is within the dimensions of said contact opening; and wherein the portion of said conductive element within said contact opening is not exposed after said etching step.
Claim 2
Independent Claim
186 words
A method of forming an interconnection in an integrated circuit through a contact opening in an insulating layer to an underlying conductive element, comprising: forming an etch stop layer within the sidewalls of the contact opening; forming a metal layer over said etch stop layer, said metal layer comprising aluminum, in such a manner that a portion of said metal layer is disposed within said contact opening between portions of said etch stop layer within the sidewalls of the contact opening; defining a mask over a portion of said metal layer, said mask overlying said contact opening; and etching portions of said metal layer not covered by said mask, with an etchant which removes said metal layer at a significantly greater rate than it removes said etch stop layer, to expose portions of said etch stop layer thereunder; wherein said mask is sized in such a manner that said metal layer, after said etching step, has an edge which is within the dimensions of said contact opening; and wherein the portion of said conductive element within said contact opening is not exposed after said etching step.
Claim 3
Dependent Claim
47 words
The method of claim 1, wherein said step of forming said metal layer comprises: depositing said metal layer continuously on the integrated circuit during an increase in the temperature of the integrated circuit beginning below 350° C. and increasing to a deposition temperature less than 500° C.
Claim 4
Dependent Claim
70 words
The method of claim 1, further comprising: prior to said step of forming said etch stop layer, forming a lower metal layer comprising aluminum; after said step of etching said metal layer, etching exposed portions of said etch stop layer to expose portions of said lower metal layer; and after said step of etching exposed portions of said etch stop layer, etching said exposed portions of said lower metal layer.
Claim 5
Dependent Claim
21 words
The method of claim 3, wherein said step of etching exposed portions of said lower metal layer is a timed etch.
Claim 6
Dependent Claim
28 words
The method of claim 3, further comprising: prior to said step of forming said lower metal layer, forming a barrier layer having portions overlying said underlying conductive element.
Claim 7
Dependent Claim
22 words
The method of claim 5, wherein said step of etching exposed portions of said lower metal layer also etches said barrier layer.
Claim 8
Dependent Claim
45 words
The method of claim 1, wherein said step of forming an etch stop layer comprises: depositing said etch stop layer overall; and anisotropically etching said etch stop layer, so that sidewall spacers of said etch stop layer remain on the sides of said contact opening.
Claim 9
Dependent Claim
47 words
The method of claim 7, wherein said step of forming said metal layer comprises: depositing said metal layer continuously on the integrated circuit during an increase in the temperature of the integrated circuit beginning below 350° C. and increasing to a deposition temperature less than 500° C.
Claim 10
Dependent Claim
15 words
The method of claim 7, wherein said etch stop layer is comprised of conductive material.
Claim 11
Dependent Claim
15 words
The method of claim 7, wherein said etch stop layer is comprised of semiconductor material.
Claim 12
Dependent Claim
36 words
The method of claim 1, wherein said step of forming an etch stop layer comprises: forming a layer of a conductive material overall, so that said conductive material is in contact with said underlying conductive element.
Claim 13
Dependent Claim
47 words
The method of claim 11, wherein said step of forming said metal layer comprises: depositing said metal layer continuously on the integrated circuit during an increase in the temperature of the integrated circuit beginning below 350° C. and increasing to a deposition temperature less than 500° C.
Claim 14
Dependent Claim
18 words
The method of claim 11, further comprising: after said etching step, etching exposed portions of said conductive layer.
Claim 15
Independent Claim
274 words
A method of forming an interconnection in an integrated circuit through a contact opening in an insulative layer to an underlying conductive element, comprising: forming a first metal layer comprising aluminum in said contact opening and in electrical contact with said conductive element; forming an etch stop layer within the sidewalls of the contact opening and adjacent said first metal layer; forming a second metal layer over said etch stop layer, said metal layer comprising aluminum, in such a manner that a portion of said second metal layer is disposed within said contact opening between portions of said etch stop layer within the sidewalls of the contact opening; defining a mask over a portion of said second metal layer, said mask overlying said contact opening; etching portions of said second metal layer not covered by said mask, with an etchant which removes said metal layer at a significantly greater rate than it removes said etch stop layer, to expose portions of said etch stop layer thereunder; after said step of etching portions of said second metal layer, etching exposed portions of said etch stop layer to expose portions of said first metal layer; and after said step of etching portions of said etch stop layer and prior to removing said mask, etching exposed portions of said first metal layer; wherein said mask is sized in such a manner that said second metal layer, after said etching step, has an edge which is within the dimensions of said contact opening; and wherein said portion of said conductive element within said contact opening is not exposed after said step of etching said second metal layer. PG,33
Claim 16
Independent Claim
274 words
A method of forming an interconnection in an integrated circuit through a contact opening in an insulative layer to an underlying conductive element, comprising: forming a first metal layer comprising aluminum in said contact opening and in electrical contact with said conductive element; forming an etch stop layer within the sidewalls of the contact opening and adjacent said first metal layer; forming a second metal layer over said etch stop layer, said metal layer comprising aluminum, in such a manner that a portion of said second metal layer is disposed within said contact opening between portions of said etch stop layer within the sidewalls of the contact opening; defining a mask over a portion of said second metal layer, said mask overlying said contact opening; etching portions of said second metal layer not covered by said mask, with an etchant which removes said metal layer at a significantly greater rate than it removes said etch stop layer, to expose portions of said etch stop layer thereunder; after said step of etching portions of said second metal layer, etching exposed portions of said etch stop layer to expose portions of said first metal layer; and after said step of etching portions of said etch stop layer and prior to removing said mask, etching exposed portions of said first metal layer; wherein said mask is sized in such a manner that said second metal layer, after said etching step, has an edge which is within the dimensions of said contact opening; and wherein said portion of said conductive element within said contact opening is not exposed after said step of etching said second metal layer. PG,33
Claim 17
Dependent Claim
50 words
The method of claim 14, further comprising: prior to said step of forming said first metal layer, forming a barrier layer having portions overlying and in contact with said underlying conductive element; and wherein said step of etching exposed portions of said first metal layer also etches said barrier layer.
Claim 18
Dependent Claim
21 words
The method of claim 14, wherein the step of etching exposed portions of said first metal layer is a timed etch.
References Cited (Backward Citations)
US3801880A
Cited
JPS5319774A
Cited
US4454166A
Cited
JPS5750429A
Cited
US4720908A
Cited
US4656732A
Cited
US4677739A
Cited
JPS62133713A
Cited
US4924295A
Cited
US4960732A
Cited
JPS63275113A
Cited
US4994410A
Cited
US4837183A
Cited
US5106781A
Cited
US5094979A
Cited
EP0388563A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-13 | 1997-06-14 | 1997-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-13 | 2001-06-14 | 2001-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-13 | 2005-06-14 | 2005-12-14 | $7700.00 | Window Closed / Lapsed |