High density CMOS integrated circuit manufacturing process

Claim 1

A method of making a CMOS twin-well semiconductor device, comprising the steps of: implanting N impurity into a selected area of a face of a P type silicon body creating an N well area and growing a first oxide over said N well area. implanting P impurity into said face using said first oxide as a mask to create a P well area, and subjecting said body to heat treatment to drive both said N well and P well into said face, forming an oxidation mask over said face and opening a hole in said mask within said P well area, then etching a recess into the silicon of said face in said hole, oxidizing said silicon in said recess to create a field oxide isolation area extending into said face, the field oxide having a top surface about level with said face, applying a layer of conductive material on said face and patterning said layer to leave gates for transistors on said N well and P well areas, implanting N+ impurity into both the N well and P well areas to create N+ source/drain for an N channel transistor in the P well area, using said gates as a mask, implanting P+ impurity into only the N well area, using the gates and a photoresist coating as a mask, to create P+ source/drain regions in the N well area, at a concentration much higher than that in said N+ source/drain regions, including the step of forming sidewall spacers on said gate layers prior to said steps of implanting, and including the step of forming direct-reacted silicide on said source/drain regions, said step of forming direct-reacted silicide being masked by said sidewall spacers on said gates.

Claim 2

A method of making a CMOS twin-well semiconductor device, comprising the steps of: implanting N impurity into a selected area of a face of a P type silicon body creating an N well area and growing a first oxide over said N well area. implanting P impurity into said face using said first oxide as a mask to create a P well area, and subjecting said body to heat treatment to drive both said N well and P well into said face, forming an oxidation mask over said face and opening a hole in said mask within said P well area, then etching a recess into the silicon of said face in said hole, oxidizing said silicon in said recess to create a field oxide isolation area extending into said face, the field oxide having a top surface about level with said face, applying a layer of conductive material on said face and patterning said layer to leave gates for transistors on said N well and P well areas, implanting N+ impurity into both the N well and P well areas to create N+ source/drain for an N channel transistor in the P well area, using said gates as a mask, implanting P+ impurity into only the N well area, using the gates and a photoresist coating as a mask, to create P+ source/drain regions in the N well area, at a concentration much higher than that in said N+ source/drain regions, including the step of forming sidewall spacers on said gate layers prior to said steps of implanting, and including the step of forming direct-reacted silicide on said source/drain regions, said step of forming direct-reacted silicide being masked by said sidewall spacers on said gates.

Claim 6

A method of making a semiconductor device, comprising the steps of: implanting impurity of one type into a selected area of a face of a semiconductor body of the opposite type creating a first well area and growing a first oxide over said first well area, implanting impurity of the opposite type into said face using said first oxide as a mask to create a second well area, and subjecting said body to heat treatment to drive both said first well and second well into said face and to establish threshold voltages for transistors subsequently formed in said first and second areas. forming an oxidation mask over said face and opening a hole in said mask within said second well area, then etching a recess into said face in said hole, oxidizing said semiconductor material of said face in said recess to create a field oxide isolation area extending into said face, the field oxide having a top surface about level with said face, applying a layer of conductive material on said face and patterning said layer to leave gates for transistors on said first well and second well areas, implanting impurity of said one type into both the first well and second well areas to create source/drain regions for a transistor in the second well area, using said gates as a mask, implanting impurity of said opposite type into only the first well area, to create source/drain regions for a transistor in the first well area, at a concentration much higher than that of said source/drain regions in the second well area. including the step of forming sidewall spacers on said gates prior to said steps of implanting, and including the step of forming direct-reacted silicide on said source/drain regions, wherein said step of forming direct-reacted silicide is masked by said sidewall spacers on said gates.

Claim 7

A method of making a semiconductor device, comprising the steps of: implanting impurity of one type into a selected area of a face of a semiconductor body of the opposite type creating a first well area and growing a first oxide over said first well area, implanting impurity of the opposite type into said face using said first oxide as a mask to create a second well area, and subjecting said body to heat treatment to drive both said first well and second well into said face and to establish threshold voltages for transistors subsequently formed in said first and second areas. forming an oxidation mask over said face and opening a hole in said mask within said second well area, then etching a recess into said face in said hole, oxidizing said semiconductor material of said face in said recess to create a field oxide isolation area extending into said face, the field oxide having a top surface about level with said face, applying a layer of conductive material on said face and patterning said layer to leave gates for transistors on said first well and second well areas, implanting impurity of said one type into both the first well and second well areas to create source/drain regions for a transistor in the second well area, using said gates as a mask, implanting impurity of said opposite type into only the first well area, to create source/drain regions for a transistor in the first well area, at a concentration much higher than that of said source/drain regions in the second well area. including the step of forming sidewall spacers on said gates prior to said steps of implanting, and including the step of forming direct-reacted silicide on said source/drain regions, wherein said step of forming direct-reacted silicide is masked by said sidewall spacers on said gates.