Method of growth-orientation of a crystal on a device using an oriented seed layer
Assignee: Motorola Solutions Inc
•
Filing: 1990-10-09
•
Granted: 1993-11-23
•
Expires: 2010-10-09
Abstract
Abstract Growth-orientation of a crystal on a semiconductor device is achieved by using an oriented seed layer to grow a monocrystalline layer of silicon on an oxide. The oriented seed layer is provided by a regimented layer of silicon precipitates, which are deposited onto a surface of the oxide in a conventional aluminum-silicon deposition process. A film of silicon is deposited onto the oriented seed layer to grow a monocrystalline layer of silicon. The monocrystalline layer of silicon is further coated with an oxide, and a further seed layer is deposited. In this manner, a plurality of monocrystalline layers of silicon can be deposited on and between insulating layers of oxide. The method can be used for the manufacture of silicon-on-oxide transistors, having a low density of crystalline defects.
Inventors
- 👤 Andrew J. Urquhart
- 👤 Ronald E. Pyle
- 👤 Chi-Ming Hong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:31
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; C30B25/18; H; H10; H10P; H10P14/00; H10P14/20; H10P14/27; H10P14/271; H10P14/29; H10P14/2901; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3204; H10P14/3211; H10P14/3238; H10P14/3242; H10P14/3244; H10P14/3248; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3456
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
119 words
A method of growth-orientation of a crystal on a device using an oriented seed layer comprising the steps of: providing a substrate material, the substrate having a surface; depositing a first layer which has a crystalline precipitant which overlies the surface of the substrate; removing substantially all the first layer overlying and adjacent the precipitants to expose substantially all of each of the precipitants overlying the substrate as the seed layer, the precipitants having uniform crystal orientation which are each orthogonal to the surface of the substrate; and depositing at least one additional layer of material overlying the first layer, the at least one additional layer also having a uniform crystal orientation orthogonal to the surface of the substrate.
Claim 2
Independent Claim
119 words
A method of growth-orientation of a crystal on a device using an oriented seed layer comprising the steps of: providing a substrate material, the substrate having a surface; depositing a first layer which has a crystalline precipitant which overlies the surface of the substrate; removing substantially all the first layer overlying and adjacent the precipitants to expose substantially all of each of the precipitants overlying the substrate as the seed layer, the precipitants having uniform crystal orientation which are each orthogonal to the surface of the substrate; and depositing at least one additional layer of material overlying the first layer, the at least one additional layer also having a uniform crystal orientation orthogonal to the surface of the substrate.
Claim 3
Dependent Claim
49 words
The method of claim 1 wherein the precipitants have uniform crystal orientation which is both orthogonal and parallel to the substrate and the step of depositing at least one additional layer of material overlying the first layer further comprises depositing a layer of silicon to form a polysilicon layer.
Claim 4
Dependent Claim
101 words
The method of claim 1 wherein prior to the removal of the first layer, the method further comprises the steps of: patterning the first layer so as to form discrete lines and spaces in the first layer, the spaces exposing the precipitants overlying the surface of the substrate; removing the precipitates within the spaces; treating the patterned first layer to align grains of the first layer in a uniform direction having uniform crystal orientation both orthogonal and parallel to the surface of the substrate; and removing substantially all the first layer overlying the precipitants to expose the precipitants overlying the substrate.
Claim 5
Dependent Claim
66 words
The method of claim 3 wherein the precipitants have uniform crystal orientation which is both orthogonal and parallel to the substrate and the step of depositing the at least one additional layer of material to overlie the seed layer further comprises depositing a layer of silicon to form a polysilicon layer having a uniform crystal orientation both orthogonal and parallel to the surface of the substrate.
Claim 6
Dependent Claim
46 words
The method of claim 3 wherein the step of depositing the at least one additional layer of material overlying the first layer further comprises providing the at least one additional layer having a uniform crystal orientation both orthogonal and parallel to the surface of the substrate.
Claim 7
Independent Claim
124 words
A method of growth-orientation of a crystal on a semiconductor device using an oriented seed layer comprising the steps of: providing an insulating substrate, the insulating substrate having a surface; depositing a binary alloy layer which has a crystalline precipitant which overlies the surface of the insulating substrate; removing substantially all the binary alloy layer overlying and adjacent the precipitants to expose substantially only the precipitants overlying the substrate as the seed layer, the precipitants having uniform crystal orientation which are each orthogonal to the surface of the insulating substrate; and depositing at least one additional layer of material overlying the binary alloy layer, the at least one additional layer also having a uniform crystal orientation orthogonal to the surface of the insulating substrate.
Claim 8
Independent Claim
124 words
A method of growth-orientation of a crystal on a semiconductor device using an oriented seed layer comprising the steps of: providing an insulating substrate, the insulating substrate having a surface; depositing a binary alloy layer which has a crystalline precipitant which overlies the surface of the insulating substrate; removing substantially all the binary alloy layer overlying and adjacent the precipitants to expose substantially only the precipitants overlying the substrate as the seed layer, the precipitants having uniform crystal orientation which are each orthogonal to the surface of the insulating substrate; and depositing at least one additional layer of material overlying the binary alloy layer, the at least one additional layer also having a uniform crystal orientation orthogonal to the surface of the insulating substrate.
Claim 9
Dependent Claim
35 words
The method of claim 6 wherein the step of depositing the at least one additional layer of material to overlie the seed layer further comprises depositing a layer of silicon to form a polysilicon layer.
Claim 10
Dependent Claim
109 words
The method of claim 6 wherein prior to the removal of the binary alloy layer the method further comprises the steps of: patterning the binary alloy layer so as to form discrete lines and spaces in the binary alloy, the spaces exposing the precipitants overlying the surface of the insulating substrate; removing the precipitates within the spaces; treating the patterned binary alloy layer to align grains of the binary alloy layer in a uniform direction having uniform crystal orientation both orthogonal and parallel to the surface of the insulating substrate; and removing substantially all the binary alloy layer overlying the precipitants to expose the precipitants overlying the insulating substrate.
Claim 11
Dependent Claim
35 words
The method of claim 8 wherein the step of depositing the at least one additional layer of material to overlie the seed layer further comprises depositing a layer of silicon to form a polysilicon layer.
Claim 12
Dependent Claim
66 words
The method of claim 8 wherein the precipitants have uniform crystal orientation which is both orthogonal and parallel to the substrate and the step of depositing the at least one additional layer of material overlying the binary alloy layer further comprises depositing a layer of silicon to form a polysilicon layer having a uniform crystal orientation both orthogonal and parallel to the surface of the substrate.
Claim 13
Independent Claim
129 words
A method of growth-orientation of a crystal on a semiconductor device using an oriented silicon seed layer comprising the steps of: providing an oxide substrate, the oxide having a surface; depositing an aluminum-silicon layer which has a silicon crystalline precipitant which overlies the surface of the oxide substrate; removing substantially all the aluminum-silicon layer overlying and adjacent the silicon precipitants to expose substantially only the silicon precipitants overlying the oxide substrate as the seed layer, the silicon precipitants having uniform crystal orientation which are each orthogonal to the surface of the substrate; and depositing at least one additional silicon layer overlying the silicon layer which overlies the seed layer, the at least one additional silicon layer also having a uniform crystal orientation orthogonal to the surface of the substrate.
Claim 14
Independent Claim
129 words
A method of growth-orientation of a crystal on a semiconductor device using an oriented silicon seed layer comprising the steps of: providing an oxide substrate, the oxide having a surface; depositing an aluminum-silicon layer which has a silicon crystalline precipitant which overlies the surface of the oxide substrate; removing substantially all the aluminum-silicon layer overlying and adjacent the silicon precipitants to expose substantially only the silicon precipitants overlying the oxide substrate as the seed layer, the silicon precipitants having uniform crystal orientation which are each orthogonal to the surface of the substrate; and depositing at least one additional silicon layer overlying the silicon layer which overlies the seed layer, the at least one additional silicon layer also having a uniform crystal orientation orthogonal to the surface of the substrate.
Claim 15
Dependent Claim
56 words
The method of claim 11 wherein the precipitants have uniform crystal orientation which is both orthogonal and parallel to the substrate and the step of depositing a silicon layer to overlie the silicon seed layer further comprises depositing a polysilicon layer having a uniform crystal orientation both orthogonal and parallel to the surface of the substrate.
Claim 16
Dependent Claim
106 words
The method of claim 11 wherein prior to the removal of the aluminum-silicon layer the method further comprises the steps of: patterning the aluminum-silicon layer so as to form discrete lines and spaces in the aluminum-silicon to expose the silicon precipitants overlying the surface of the oxide substrate in the spaces; removing the silicon precipitates within the space; treating the patterned aluminum-silicon layer to align grains of the aluminum-silicon in a uniform direction having uniform crystal orientation both orthogonal and parallel to the surface of the substrate; and removing substantially all the aluminum-silicon layer overlying the silicon precipitants to expose the silicon precipitants overlying the substrate.
Claim 17
Dependent Claim
31 words
The method of claim 13 wherein the step of depositing a silicon layer to overlie the silicon seed layer further comprises depositing a layer of silicon to form a polysilicon layer.
Claim 18
Dependent Claim
63 words
The method of claim 13 wherein the precipitants have uniform crystal orientation which is both orthogonal and parallel to the substrate and the step of depositing at least one additional silicon layer overlying the silicon layer further comprises depositing a layer of silicon to form a polysilicon layer having a uniform crystal orientation both orthogonal and parallel to the surface of the substrate.
References Cited (Backward Citations)
US3929528A
Cited
US3918149A
Cited
US4027053A
Cited
US4274890A
Cited
US4359486A
Cited
US4399605A
Cited
US4515642A
Cited
US4772564A
Cited
US4781766A
Cited
US4989064A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-22 | 1997-05-24 | 1997-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-22 | 2001-05-24 | 2001-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-22 | 2005-05-24 | 2005-11-23 | $7700.00 | Window Closed / Lapsed |