US5250206A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Rare earth element-Fe-B or rare earth element-Fe-Co-B permanent magnet powder excellent in magnetic anisotropy and corrosion resistivity and bonded magnet manufactured therefrom
Assignee: Mitsubishi Materials Corp
•
Filing: 1991-09-19
•
Granted: 1993-10-05
•
Expires: 2011-09-19
Abstract
Abstract A R-Fe-B or R-Fe-Co-B permanent magnet powder excellent in magnetic anisotropy and corrosion resistivity, having powder particles. The powder particles each consist essentially of, in atomic percentage: R: 10-20% B: 3-20%; at least one element selected from the group consisting of Ti, V, Nb, Ta, Al, and Si: 0.001-5.0%; and Fe and inevitable impurities: the balance, The R-Fe-Co-B magnet powder further contains 0.1-50% Co. The powder particles each have an aggregated recrystallized structure having a main phase thereof formed by a R 2 Fe 14 B or R 2 (Co,Fe) 14 B type intermetallic compound phase having a tetragonal structure. The intermetallic compound phase is formed of recrystallized grains aggregated therein and includes at least 50 volumetric % of recrystallized grains having a ratio b/a smaller than 2 provided that a is designated by the smallest diameter of each of the recrystallized grains, and b is by the largest diameter thereof. The recrystallized grains form the aggregated recrystallized structure having an average grain size within a range of 0.05-20 μm.
Inventors
- 👤 Ryoji Nakayama
- 👤 Takuo Takeshita
- 👤 Tamotsu Ogawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:30
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/023; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0572; H01F1/0573; H01F1/0575; H01F1/0578
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
174 words
A rare earth element-Fe-B permanent magnet power excellent in magnetic anisotropy and corrosion resistivity, consisting essentially of powder particles, wherein said powder particles each consist essentially of, in atomic percentage: at least one element selected from the group consisting of yttrium and rare earth elements: 10-20%; B: 3-20%; at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si: 0.001-5.0%; and Fe and inevitable impurities: the balance, said powder particles each having an aggregated recrystallized structure having a main phase thereof formed of a R 2 Fe 14 B intermetallic compound phase having a tetragonal structure, wherein R is a rare earth element, said intermetallic compound phase being formed of recrystallized grains aggregated therein and including at least 50 volumetric % of recrystallized grains having a ratio of b/a smaller than 2, provided that a is the smallest diameter of each of said recrystallized grains, and b is the largest diameter thereof, said recrystallized grains forming said aggregated recrystallized structure having an average grain size of 0.05-20 μm.
Claim 2
Dependent Claim
174 words
A rare earth element-Fe-B permanent magnet power excellent in magnetic anisotropy and corrosion resistivity, consisting essentially of powder particles, wherein said powder particles each consist essentially of, in atomic percentage: at least one element selected from the group consisting of yttrium and rare earth elements: 10-20%; B: 3-20%; at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si: 0.001-5.0%; and Fe and inevitable impurities: the balance, said powder particles each having an aggregated recrystallized structure having a main phase thereof formed of a R 2 Fe 14 B intermetallic compound phase having a tetragonal structure, wherein R is a rare earth element, said intermetallic compound phase being formed of recrystallized grains aggregated therein and including at least 50 volumetric % of recrystallized grains having a ratio of b/a smaller than 2, provided that a is the smallest diameter of each of said recrystallized grains, and b is the largest diameter thereof, said recrystallized grains forming said aggregated recrystallized structure having an average grain size of 0.05-20 μm.
Claim 3
Dependent Claim
23 words
The rare earth element-Fe-B permanent magnet powder as claimed in claim 1, wherein said average size of said recrystallized grains is 0.05-3 μm.
Claim 4
Dependent Claim
40 words
The rare earth element-Fe-B permanent magnet powder as claimed in claim 1 or 2, wherein said aggregated recrystallized structure in which said recrystallized grains are aggregated is formed substantially solely of a R 2 Fe 14 B intermetallic compound phase.
Claim 5
Dependent Claim
35 words
The rare earth element-Fe-B permanent magnet powder as claimed in claim 1, wherein part of said B is replaced by at least one element selected from the group consisting of C, N, O and F.
Claim 6
Dependent Claim
34 words
A rare earth element-Fe-B permanent magnet powder as claimed in claim 1, further including at least one element selected from the group consisting of Ni, Cu, Zn, Ga, Ge, Zr, Mo, Hf and W.
Claim 7
Dependent Claim
27 words
A rare earth element-Fe-B bonded magnet manufactured from said rare earth element-Fe-B permanent magnet powder as claimed in any one of claims 1, 2, 4 or 5.
Claim 8
Dependent Claim
20 words
A rare earth element-Fe-B bonded magnet manufactured from said rare earth element-Fe-B permanent magnet powder as claimed in claim 3.
Claim 9
Dependent Claim
176 words
A rare earth element-Fe-Co-B permanent magnet powder excellent in magnetic anisotropy and corrosion resistivity, consisting essentially of powder particles, wherein said powder particles each consist essentially of, in atomic percentage: at least one element selected from the group consisting of yttrium and rare earth elements: 10-20%; Co: 0.1-50%; B: 3-20%; at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si: 0.001-5.0%; and Fe and inevitable impurities: the balance, said powder particles each having an aggregated recrystallized structure having a main phase thereof formed of a R 2 (Fe,Co) 14 B intermetallic compound phase having a tetragonal structure, wherein R is a rare earth element, said intermetallic compound phase being formed of recrystallized grains aggregated therein and including at least 50 volumetric % of recrystallized grains having a ratio of b/a smaller than 2, provided that a is the smallest diameter of each of said recrystallized grains, and b is the largest diameter thereof, said recrystallized grains forming said aggregated recrystallized structure having an average grain size of 0.05-20 μm.
Claim 10
Dependent Claim
176 words
A rare earth element-Fe-Co-B permanent magnet powder excellent in magnetic anisotropy and corrosion resistivity, consisting essentially of powder particles, wherein said powder particles each consist essentially of, in atomic percentage: at least one element selected from the group consisting of yttrium and rare earth elements: 10-20%; Co: 0.1-50%; B: 3-20%; at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si: 0.001-5.0%; and Fe and inevitable impurities: the balance, said powder particles each having an aggregated recrystallized structure having a main phase thereof formed of a R 2 (Fe,Co) 14 B intermetallic compound phase having a tetragonal structure, wherein R is a rare earth element, said intermetallic compound phase being formed of recrystallized grains aggregated therein and including at least 50 volumetric % of recrystallized grains having a ratio of b/a smaller than 2, provided that a is the smallest diameter of each of said recrystallized grains, and b is the largest diameter thereof, said recrystallized grains forming said aggregated recrystallized structure having an average grain size of 0.05-20 μm.
Claim 11
Dependent Claim
23 words
The rare earth element-Fe-Co-B permanent magnet powder as claimed in claim 8, wherein said average size of said recrystallized grains is 0.05-3 μm.
Claim 12
Dependent Claim
40 words
The rare earth element-Fe-Co-B permanent magnet powder as claimed in claim 8 or 9, wherein said aggregated recrystallized structure in which said recrystallized grains are aggregated is formed substantially solely of a R 2 (Fe,Co) 14 N intermetallic compound phase.
Claim 13
Dependent Claim
35 words
The rare earth element-Fe-Co-B permanent magnet powder as claimed in claim 8, wherein part of said B is replaced by at least one element selected from the group consisting of C, N, O and F.
Claim 14
Dependent Claim
15 words
The rare earth element-Fe-Co-B permanent magnet powder as claimed in claim 8, wherein Co: 0.1-20%.
Claim 15
Dependent Claim
40 words
The rare earth element-Fe-Co-B permanent magnet powder as claimed in claim 8, wherein the powder particles further consist essentially of at least one element selected from the group consisting of Ni, Cu, Zn, Ga, Ge, Zr, Mo, Hf and W.
Claim 16
Dependent Claim
28 words
A rare earth element-Fe-Co-B bonded magnet manufactured from said rare earth element-Fe-B permanent magnet powder as claimed in any one of claims 8, 9, 11, 12 or 13.
Claim 17
Dependent Claim
20 words
A rare earth element-Fe-B bonded magnet manufactured from said rare earth element-Fe-B permanent magnet powder as claimed in claim 10.
Claim 18
Dependent Claim
69 words
The rare earth element-Fe-B permanent magnet powder as claimed in claim 2, wherein the at least one rare earth element is in an amount of 11 to 15 atomic percentage; boron is in an amount of 4 to 8 atomic percentage; the at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si is in an amount of 0.01 to 3.0 atomic percentage.
Claim 19
Dependent Claim
81 words
The rare earth element-Fe-B permanent magnet powder as claimed in claim 9, wherein the at least one rare earth element is in an amount of 11 to 15 atomic percentage; boron is in an amount of 4 to 8 atomic percentage; cobalt is in an amount of 0.1 to 20 atomic percentage; and the at least one element selected from the group consisting of Ti, V, Nb, Ta, Al and Si is in an amount of 0.01 to 3.0 atomic percentage.
References Cited (Backward Citations)
US4792368A
Cited
US4770723A
Cited
US4802931A
Cited
US4975130A
Cited
JPS6063304A
Cited
US4663066A
Cited
US4921553A
Cited
US4842656A
Cited
US5049208A
Cited
US5022939A
Cited
JPS6447841A
Cited
JPS6445103A
Cited
JPH01132106A
Cited
US4981532A
Cited
US5110374A
Cited
US4891532A
Cited
JPH02164007A
Cited
EP0411571A2
Cited
US5147473A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-10-04 | 1997-04-05 | 1997-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-10-04 | 2001-04-05 | 2001-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-10-04 | 2005-04-05 | 2005-10-05 | $7700.00 | Window Closed / Lapsed |