High energy product rare earth-iron magnet alloys
Assignee: Magnequench International LLC
•
Filing: 1983-10-26
•
Granted: 1989-02-07
•
Expires: 2003-10-26
Abstract
Abstract Magnetically hard compositions having high values of coercivity, remanence and energy product contain rare earth elements, transition metal elements and boron in suitable proportions. The preferred rare earth elements are neodymium and praseodymium, and the preferred transition metal element is iron. The magnetic alloys have characteristic very finely crystalline microstructures.
Inventors
- 👤 John J. Croat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:33
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; C; C22; C22C; C22C45/00; C22C45/02
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
171 words
A permanent magnet in which the predominant phase is (RE 1-a RE' a ) 2 (Fe 1-b TM b ) 14 B 1 where RE is neodymium and/or praseodymium and comprises at least about 6 atomic percent of the magnet; RE' is one or more rare earth elements taken from the group consisting of yttrium, lanthanum, cerium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium and lutetium and where a is from 0 to about 0.4 and RE and RE' together comprise up to about 40 atomic percent of the magnet; TM is one or more transition metal elements taken from the group consisting of cobalt, nickel, manganese, chromium and copper where b is from 0 to about 0.4 and Fe comprises at least about 40 atomic percent, and Fe and T, together comprise up to about 90 atomic percent of the magnet; and B comprises at least from about 0.5 to about 10 atomic percent of the magnet, the magnet having intrisic magnetic coercivity of at least 1,000 Oersteds.
Claim 2
Dependent Claim
171 words
A permanent magnet in which the predominant phase is (RE 1-a RE' a ) 2 (Fe 1-b TM b ) 14 B 1 where RE is neodymium and/or praseodymium and comprises at least about 6 atomic percent of the magnet; RE' is one or more rare earth elements taken from the group consisting of yttrium, lanthanum, cerium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium and lutetium and where a is from 0 to about 0.4 and RE and RE' together comprise up to about 40 atomic percent of the magnet; TM is one or more transition metal elements taken from the group consisting of cobalt, nickel, manganese, chromium and copper where b is from 0 to about 0.4 and Fe comprises at least about 40 atomic percent, and Fe and T, together comprise up to about 90 atomic percent of the magnet; and B comprises at least from about 0.5 to about 10 atomic percent of the magnet, the magnet having intrisic magnetic coercivity of at least 1,000 Oersteds.
Claim 3
Dependent Claim
113 words
A permanent magnet having an energy product at magnetic saturation of at least about 5 megaGaussOersteds comprising at least about 10 to about 40 atomic percent of one or more rare earth elements at least about 6 percent of the magnet consisting of neodymium and/or praseodymium; at least about 0.5 to about 10 atomic percent boron; and at least about 50 to 90 atomic percent total transition metal elements taken from the group consisting of iron and mixtures of iron and cobalt where the amount of said cobalt in said mixture is less than about 40 percent of the iron and wherein the predominant phase is RE 2 TM 14 B 1 .
Claim 4
Dependent Claim
113 words
A permanent magnet having an energy product at magnetic saturation of at least about 5 megaGaussOersteds comprising at least about 10 to about 40 atomic percent of one or more rare earth elements at least about 6 percent of the magnet consisting of neodymium and/or praseodymium; at least about 0.5 to about 10 atomic percent boron; and at least about 50 to 90 atomic percent total transition metal elements taken from the group consisting of iron and mixtures of iron and cobalt where the amount of said cobalt in said mixture is less than about 40 percent of the iron and wherein the predominant phase is RE 2 TM 14 B 1 .
Claim 5
Dependent Claim
100 words
A magnetically hard alloy composition comprising at least about 10 to about 40 atomic percent of one or more rare earth elements and wherein at least about 60 atomic percent of the total said rare earth elements is taken from the group consisting of praseodymium and neodymium; at least about 0.5 to about 10 atomic percent boron; and up to about 90 total atomic percent of one or more transition metal elements including iron in an amount of at least about 40 atomic percent of the alloy and wherein the predominant phase is RE 2 TM 14 B 1 .
Claim 6
Dependent Claim
100 words
A magnetically hard alloy composition comprising at least about 10 to about 40 atomic percent of one or more rare earth elements and wherein at least about 60 atomic percent of the total said rare earth elements is taken from the group consisting of praseodymium and neodymium; at least about 0.5 to about 10 atomic percent boron; and up to about 90 total atomic percent of one or more transition metal elements including iron in an amount of at least about 40 atomic percent of the alloy and wherein the predominant phase is RE 2 TM 14 B 1 .
Claim 7
Dependent Claim
19 words
The composition of claim 3 characterized by the inclusion of a heavy rare earth element to increase magnetic coercivity.
Claim 8
Dependent Claim
30 words
The composition of claim 3 characterized by an intrinsic magnetic coercivity of at least about 5 kiloOersteds and an energy product at magnetic saturation of at least about 10 megaGaussOersteds.
Claim 9
Dependent Claim
18 words
The composition of claim 3 characterized by a magnetic remanence at saturation of at least about 7 kiloGauss.
Claim 10
Dependent Claim
23 words
The composition of claim 3 wherein the transition metal cobalt is present in an amount up to about 40 percent of the iron.
Claim 11
Dependent Claim
21 words
The composition of claim 3 wherein the transition metal elements include cobalt and the rare earth elements include terbium and/or dysprosium.
Claim 12
Dependent Claim
105 words
A permanent magnet which comprises an overquenched and annealed alloy of about 10-40 atomic percent of one or more rare earth elements including at least about 6 to about 40 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron, at least about 40 to 90 total atomic percent iron and cobalt where cobalt is present in an amount greater than zero but less than about 40 atomic percent based on iron in the alloy, the predominant phase in said alloy being RE 2 TM 14 B 1 which constitutes at least about 70 percent by weight of the alloy.
Claim 13
Dependent Claim
105 words
A permanent magnet which comprises an overquenched and annealed alloy of about 10-40 atomic percent of one or more rare earth elements including at least about 6 to about 40 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron, at least about 40 to 90 total atomic percent iron and cobalt where cobalt is present in an amount greater than zero but less than about 40 atomic percent based on iron in the alloy, the predominant phase in said alloy being RE 2 TM 14 B 1 which constitutes at least about 70 percent by weight of the alloy.
Claim 14
Dependent Claim
126 words
A permanent magnet having a coercivity of at least about 1,000 Oersteds at room temperature and which comprises about 10-40 atomic percent of one or more rare earth elements including at least about 6 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron, from zero to less than about 20 total atomic percent based on iron in the alloy of one or more additive metals taken from the group consisting of titanium, nickel, chromium, zirconium and manganese, and up to about 90 atomic percent total of one or more transition metals including at least about 40 atomic percent iron and in which magnet the predominant magnetically hard constituent is the tetragonal crystal phase RE 2 TM 14 B 1 .
Claim 15
Dependent Claim
126 words
A permanent magnet having a coercivity of at least about 1,000 Oersteds at room temperature and which comprises about 10-40 atomic percent of one or more rare earth elements including at least about 6 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron, from zero to less than about 20 total atomic percent based on iron in the alloy of one or more additive metals taken from the group consisting of titanium, nickel, chromium, zirconium and manganese, and up to about 90 atomic percent total of one or more transition metals including at least about 40 atomic percent iron and in which magnet the predominant magnetically hard constituent is the tetragonal crystal phase RE 2 TM 14 B 1 .
Claim 16
Dependent Claim
117 words
An overquenched and annealed RE 2 TM 14 B 1 type permanent magnet material comprising from about 10-40 atomic percent of one or more rare earth elements including at least about 6 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron and from zero to less than about 20 total atomic percent based on iron in the material of one or more additive metals taken from the group consisting of titanium, nickel, chromium, zirconium and manganese and from about 50 to 90 total atomic percent iron which material has an average crystallite size less than or about equal to 500 nanometers and an energy product of at least about 10 megaGaussOersteds.
Claim 17
Dependent Claim
117 words
An overquenched and annealed RE 2 TM 14 B 1 type permanent magnet material comprising from about 10-40 atomic percent of one or more rare earth elements including at least about 6 atomic percent neodymium and/or praseodymium, at least about 0.5 to about 10 atomic percent boron and from zero to less than about 20 total atomic percent based on iron in the material of one or more additive metals taken from the group consisting of titanium, nickel, chromium, zirconium and manganese and from about 50 to 90 total atomic percent iron which material has an average crystallite size less than or about equal to 500 nanometers and an energy product of at least about 10 megaGaussOersteds.
Claim 18
Dependent Claim
74 words
A permanent magnet alloy which consists essentially of about 50 to 90 atomic percent iron, about 0.5 to 10 atomic percent boron and about 10 to 40 atomic percent of one or more rare earth elements including more than 6 atomic percent Nd and/or Pr which has a predominant crystal phase RE 2 TM 14 B 1 and has an average crystallite size less than or about equal to optimum single magnetic domain size.
Claim 19
Dependent Claim
74 words
A permanent magnet alloy which consists essentially of about 50 to 90 atomic percent iron, about 0.5 to 10 atomic percent boron and about 10 to 40 atomic percent of one or more rare earth elements including more than 6 atomic percent Nd and/or Pr which has a predominant crystal phase RE 2 TM 14 B 1 and has an average crystallite size less than or about equal to optimum single magnetic domain size.
Claim 20
Dependent Claim
83 words
A hot-worked permanent magnet alloy which comprises, based on the alloy composition, up to about 90 atomic percent total of one or more transition metals including at least about 40 atomic percent iron, at least about 0.5 to about 10 atomic percent boron and up to about 40 atomic percent of one or more rare earth elements including more than 6 atomic percent Nd and/or Pr which alloy has a predominant phase of tetragonal crystals of RE 2 TM 14 B 1 .
Claim 21
Dependent Claim
83 words
A hot-worked permanent magnet alloy which comprises, based on the alloy composition, up to about 90 atomic percent total of one or more transition metals including at least about 40 atomic percent iron, at least about 0.5 to about 10 atomic percent boron and up to about 40 atomic percent of one or more rare earth elements including more than 6 atomic percent Nd and/or Pr which alloy has a predominant phase of tetragonal crystals of RE 2 TM 14 B 1 .
Claim 22
Dependent Claim
80 words
A RE 2 TM 14 B 1 type permanent magnet alloy comprising at least about 10 to about 40 atomic percent neodymium and/or praseodymium, at least about 50 to about 90 atomic percent iron, at least about 0.5 to about 10 atomic percent boron, and up to about 20 atomic percent of one or more heavy rare earth elements based on the neodymium and praseodymium, the magnetic coercivity of said alloy being at least about 5,000 Oersteds at room temperature.
Claim 23
Dependent Claim
80 words
A RE 2 TM 14 B 1 type permanent magnet alloy comprising at least about 10 to about 40 atomic percent neodymium and/or praseodymium, at least about 50 to about 90 atomic percent iron, at least about 0.5 to about 10 atomic percent boron, and up to about 20 atomic percent of one or more heavy rare earth elements based on the neodymium and praseodymium, the magnetic coercivity of said alloy being at least about 5,000 Oersteds at room temperature.
Claim 24
Dependent Claim
16 words
The magnet alloy of claim 14 where the heavy rare earth element is terbium and/or dysprosium.
Claim 25
Dependent Claim
101 words
A permanent magnet composition comprised predominantly of the tetragonal crystal phase RE 2 TM 14 B 1 where RE is one or more rare earth elements and TM is one or more transition metal elements and where said composition comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and up to about 90 atomic percent total transition metals including Fe, said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 26
Dependent Claim
101 words
A permanent magnet composition comprised predominantly of the tetragonal crystal phase RE 2 TM 14 B 1 where RE is one or more rare earth elements and TM is one or more transition metal elements and where said composition comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and up to about 90 atomic percent total transition metals including Fe, said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 27
Dependent Claim
108 words
A permanent magnet composition comprised predominantly of the tetragonal crystal phase RE 2 TM 14 B 1 where RE is one or more rare earth elements and TM is one or more transition metal elements and where said composition is rapidly solidified and annealed and comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent total rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and up to about 90 atomic percent total transition metals including Fe, said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 28
Dependent Claim
108 words
A permanent magnet composition comprised predominantly of the tetragonal crystal phase RE 2 TM 14 B 1 where RE is one or more rare earth elements and TM is one or more transition metal elements and where said composition is rapidly solidified and annealed and comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent total rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and up to about 90 atomic percent total transition metals including Fe, said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 29
Dependent Claim
100 words
A permanent magnet composition in which the predominant phase is RE 2 Fe 1-x Co x14 B 1 where RE is one or more rare earth elements and x is from about zero to 0.4, and where said composition comprises at least about 6 atomic percent Nd and/or Pr and from about 10-40 percent total rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and from about 50 to 90 percent total transition metals including iron said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 30
Dependent Claim
100 words
A permanent magnet composition in which the predominant phase is RE 2 Fe 1-x Co x14 B 1 where RE is one or more rare earth elements and x is from about zero to 0.4, and where said composition comprises at least about 6 atomic percent Nd and/or Pr and from about 10-40 percent total rare earths, at least about 0.5 to about 10 atomic percent boron and at least about 50 atomic percent Fe and from about 50 to 90 percent total transition metals including iron said composition having an intrinsic magnetic coercivity of at least about 1,000 Oersteds.
Claim 31
Dependent Claim
129 words
A permanent magnet alloy in which the predominant phase is RE 2 (Fe 1-x TM x ) 14 B 1 where x<0.4 and which phase has a tetragonal crystal structure where RE is one or more rare earth elements, TM is one or more transition metal elements and wherein the crystallographic c-axis is the preferred axis of magnetization and has a length of about 12.2 angstroms and the a-axis has a length of about 8.78 angstroms, and said alloy comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earth elements, at least about 40 atomic percent Fe, and up to about 90 atomic percent total transition metals including Fe and at least about 0.5 to about 10 atomic percent boron.
Claim 32
Dependent Claim
129 words
A permanent magnet alloy in which the predominant phase is RE 2 (Fe 1-x TM x ) 14 B 1 where x<0.4 and which phase has a tetragonal crystal structure where RE is one or more rare earth elements, TM is one or more transition metal elements and wherein the crystallographic c-axis is the preferred axis of magnetization and has a length of about 12.2 angstroms and the a-axis has a length of about 8.78 angstroms, and said alloy comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earth elements, at least about 40 atomic percent Fe, and up to about 90 atomic percent total transition metals including Fe and at least about 0.5 to about 10 atomic percent boron.
Claim 33
Dependent Claim
106 words
A permanent magnet alloy in which the predominant phase is RE 2 Fe 14-x TM x B 1 which has a tetragonal crystal structure where RE is one or more rare earth elements, TM is one or more transition metal elements and wherein the crystallographic c-axis is the preferred axis of magnetization, and which alloy comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earth elements, at least about 40 atomic percent Fe and up to about 90 atomic percent total transition metal elements including Fe, and at least about 0.5 to about 10 atomic percent boron.
Claim 34
Dependent Claim
106 words
A permanent magnet alloy in which the predominant phase is RE 2 Fe 14-x TM x B 1 which has a tetragonal crystal structure where RE is one or more rare earth elements, TM is one or more transition metal elements and wherein the crystallographic c-axis is the preferred axis of magnetization, and which alloy comprises at least about 6 atomic percent Nd and/or Pr and up to about 40 atomic percent rare earth elements, at least about 40 atomic percent Fe and up to about 90 atomic percent total transition metal elements including Fe, and at least about 0.5 to about 10 atomic percent boron.
References Cited (Backward Citations)
US3821035A
Cited
SU420695A1
Cited
CH617529A5
Cited
JPS5250598A
Cited
US4192696A
Cited
JPS5328018A
Cited
JPS5476419A
Cited
JPS55115304A
Cited
JPS5629639A
Cited
JPS5647542A
Cited
JPS5647538A
Cited
US4308474A
Cited
US4382061A
Cited
JPS57141901A
Cited
US4374665A
Cited
US4402770A
Cited
US4409043A
Cited
JPS58123853A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-07 | 1992-08-08 | 1993-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-07 | 1996-08-08 | 1997-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-07 | 2000-08-08 | 2001-02-07 | $7700.00 | Window Closed / Lapsed |