Apparatus for and a method of growing thin films of elemental semiconductors
Assignee: United States Department of the Navy
•
Filing: 1990-06-22
•
Granted: 1993-07-06
•
Expires: 2010-06-22
Abstract
Abstract An apparatus for and a method of growing thin films of the elemental semiconductors (group IVB), i.e., silicon, germanium, tin, lead, and, especially diamond, using modified atomic layer epitaxial (ALE) growth techniques are disclosed. In addition, stoichiometric and nonstoichiometric compounds of the group IVB elements are also grown by a variation of the method according to the present invention. The ALE growth of diamond thin films is carried-out, inter alia, by exposing a plurality of diamond or like substrates alternately to a halocarbon reactant gas, e.g., carbon tetrafluoride (CF4), and a hydrocarbon reactant gas, e.g., methane (CH4), at substrate temperatures between 300 and 650 Celsius. A stepping motor device portion of the apparatus is controlled by a programmable controller portion such that the surfaces of the plurality of substrates are given exposures of at least 1015 molecules/cm2 of each of the reactant gases. The chemical reaction time to complete the growth of an individual atom layer is approximately 25x10-6 second.
Inventors
- 👤 Max N. Yoder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:23
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/06; C30B25/00; C30B25/02; C30B25/14; C30B25/18; C30B29/04; C30B29/08; C30B29/10; C30B29/36; C30B29/52; Y; Y10; Y10S; Y10S438/00; Y10S438/909; Y10S438/931; Y10S438/974
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
225 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of an elemental semiconductor selected from the group consisting of silicon, germanium, tin, lead and diamond comprising the steps of: hydrogenating said surface of said substrate; in a first exposing step, exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer, said first exposing step including the steps of resetting the pressure acting upon and the temperature of said surface of said substrate to a growth pressure within a range of growth pressures, and to a growth temperature within a range of growth temperatures, respectively, and then exposing said surface of said substrate to a halogen-group IVB containing gas; desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; in a second exposing step, exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer, said second exposing step including the steps of maintaining the pressure acting upon and the temperature of said first layer on said substrate to said growth pressure and temperature, respectively, and then exposing said first layer on said substrate to a hydrogen-group IVB containing gas; and desorbing said second layer on said substrate of all physisorbed species of said second reactant gas.
Claim 2
Independent Claim
225 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of an elemental semiconductor selected from the group consisting of silicon, germanium, tin, lead and diamond comprising the steps of: hydrogenating said surface of said substrate; in a first exposing step, exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer, said first exposing step including the steps of resetting the pressure acting upon and the temperature of said surface of said substrate to a growth pressure within a range of growth pressures, and to a growth temperature within a range of growth temperatures, respectively, and then exposing said surface of said substrate to a halogen-group IVB containing gas; desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; in a second exposing step, exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer, said second exposing step including the steps of maintaining the pressure acting upon and the temperature of said first layer on said substrate to said growth pressure and temperature, respectively, and then exposing said first layer on said substrate to a hydrogen-group IVB containing gas; and desorbing said second layer on said substrate of all physisorbed species of said second reactant gas.
Claim 3
Dependent Claim
45 words
The method of claim 1 wherein said hydrogen-group IVB containing gas for the ALE growth of silicon is SiH 4 , of germanium is GeH 4 , of tin is SnH 4 , of lead is PbH 4 and of diamond is CH 4 .
Claim 4
Dependent Claim
81 words
The method of claim 1 wherein said hydrogenating step includes the steps of: setting the pressure acting on said surface of said substrate to a purge pressure within a range of purge pressures; setting the temperature of said surface of said substrate to a purge temperature within a range of purge temperatures; exposing said surface of said substrate to a purge gas; and striking a plasma in said purge gas to purge clean and, accordingly, hydrogenate said surface of said substrate.
Claim 5
Dependent Claim
27 words
The method of claim 3 wherein said range of purge pressures for purge clean of silicon, germanium, tin, lead and of diamond is 20 to 100 Torr.
Claim 6
Dependent Claim
24 words
The method of claim 4 wherein said predetermined purge pressure for purge clean of silicon, germanium, tin, lead and of diamond is 40 Torr.
Claim 7
Dependent Claim
50 words
The method of claim 3 wherein said range of purge temperatures for purge clean of silicon is 240 to 350 Celsius, of germanium is 200 to 320 Celsius, of tin is 100 to 260 Celsius, of lead is 75 to 200 Celsius and of diamond is 300 to 650 Celsius.
Claim 8
Dependent Claim
37 words
The method of claim 6 wherein said purge temperature for purge clean of silicon is 240 Celsius, of germanium is 200 Celsius, of tinis 100 Celsius, of lead is 75 Celsius and of diamond is 300 Celsius.
Claim 9
Dependent Claim
12 words
The method of claim 3 wherein said purge gas is molecular hydrogen.
Claim 10
Dependent Claim
18 words
The method of claim 8 wherein said plasma of said molecular hydrogen is struck for about 30 seconds.
Claim 11
Dependent Claim
23 words
The method of claim 1 wherein said range of growth pressures for silicon, germanium, tin, lead and diamond is 40 to 400 Torr.
Claim 12
Dependent Claim
19 words
The method of claim 10 wherein said growth pressure for silicon, germanium, tin, lead and diamond is 40 Torr.
Claim 13
Dependent Claim
43 words
The method of claim 1 wherein said range of growth temperatures for silicon is 240 to 350 Celsius, germanium is 200 to 320 Celsius, tin is 100 to 260 Celsius, lead is 75 to 115 Celsius and diamond is 300 to 650 Celsius.
Claim 14
Dependent Claim
31 words
The method of claim 12 wherein said growth temperature for silicon is 325 Celsius, germanium is 290 Celsius, tin is 200 Celsius, lead is 170 Celsius and diamond is 600 Celsius.
Claim 15
Dependent Claim
45 words
The method of claim 5 wherein said halogen-group IVB containing gas for the ALE growth of silicon is SiCl 4 , of germanium is GeCl 4 , of tin is SnBr 4 , of lead is PbI 4 and of diamond is CF 4 .
Claim 16
Dependent Claim
26 words
The method of claim 1 wherein said desorbing steps comprise removing all of the physisorbed species of said first and second reactant gases by vacuum evacuation.
Claim 17
Independent Claim
232 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a stoichiometric compound of an elemental semiconductor selected from the group consisting of silicon carbide, germanium silicide, germanium carbide and tin germanide comprising the steps of: hydrogenating said surface of said substrate; in a first exposing step, exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer, said first exposing step including the steps of resetting the pressure acting upon and the temperature of said surface of said substrate to a growth pressure within a range of growth pressures, and to a growth temperature within a range of growth temperatures, respectively, and then exposing said surface of said substrate to a halogen-group IVB containing gas; desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; in a second exposing step, exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer, said second exposing step including the steps of maintaining the pressure acting upon and the temperature of said first layer on said substrate to said growth pressure and temperature, respectively, and then exposing said first layer on said substrate to a hydrogen-group IVB containing gas; and desorbing said second layer on said substrate of all physisorbed species of said second reactant gas.
Claim 18
Independent Claim
232 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a stoichiometric compound of an elemental semiconductor selected from the group consisting of silicon carbide, germanium silicide, germanium carbide and tin germanide comprising the steps of: hydrogenating said surface of said substrate; in a first exposing step, exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer, said first exposing step including the steps of resetting the pressure acting upon and the temperature of said surface of said substrate to a growth pressure within a range of growth pressures, and to a growth temperature within a range of growth temperatures, respectively, and then exposing said surface of said substrate to a halogen-group IVB containing gas; desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; in a second exposing step, exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer, said second exposing step including the steps of maintaining the pressure acting upon and the temperature of said first layer on said substrate to said growth pressure and temperature, respectively, and then exposing said first layer on said substrate to a hydrogen-group IVB containing gas; and desorbing said second layer on said substrate of all physisorbed species of said second reactant gas.
Claim 19
Dependent Claim
43 words
The method of claim 16 wherein said hydrogen-group IVB containing gas for the ALE growth of silicon carbide is CH 4 , of germanium silicide is SiH 4 , of tin germanide is GeH 4 and of germanium carbide is CH 4 .
Claim 20
Dependent Claim
81 words
The method of claim 16 wherein said hydrogenating step includes the steps of: setting the pressure acting on said surface of said substrate to a purge pressure within a range of purge pressures; setting the temperature of said surface of said substrate to a purge temperature within a range of purge temperatures; exposing said surface of said substrate to a purge gas; and striking a plasma in said purge gas to purge clean and, accordingly, hydrogenate said surface of said substrate.
Claim 21
Dependent Claim
30 words
The method of claim 18 wherein said range of purge pressures for purge clean of silicon carbide, germanium silicide, germanium carbide, and tin germanide compounds is 20 to 100 Torr.
Claim 22
Dependent Claim
26 words
The method of claim 19 wherein said purge pressure for purge clean of silicon carbide, germanium silicide, germanium carbide, and tin germanide compound is 40 Torr.
Claim 23
Dependent Claim
47 words
The method of claim 18 wherein said range of purge temperatures for purge clean of silicon carbide is 240 to 350 Celsius, of germanium silicide is 200 to 320 Celsius, of tin germanide is 100 to 260 Celsius, and of germanium carbide is 200 to 300 Celsius.
Claim 24
Dependent Claim
37 words
The method of claim 21 wherein said purge temperature for purge clean of silicon carbide is 300 Celsius, of germanium silicide is 280 Celsius, of tim germanide is 240 Celsius, and of germanium carbide is 300 Celsius.
Claim 25
Dependent Claim
12 words
The method of claim 18 wherein said purge gas is molecular hydrogen.
Claim 26
Dependent Claim
18 words
The method of claim 23 wherein said plasma of said molecular hydrogen is struck for about 30 seconds.
Claim 27
Dependent Claim
26 words
The method of claim 16 wherein said range of growth pressures for silicon carbide, germanium silicide, tin germanide, and germanium carbide is 40 to 400 Torr.
Claim 28
Dependent Claim
22 words
The method of claim 25 wherein said growth pressure for silicon carbide, germanium silicide, tin germanide, and germanium carbide is 40 Torr.
Claim 29
Dependent Claim
41 words
The method of claim 16 wherein said range of growth temperatures for silicon carbide is 400 to 600 Celsius, germanium silicide is 275 to 400 Celsius, tin germanide is 180 to 240 Celsius and germanium carbide is 260 to 500 Celsius.
Claim 30
Dependent Claim
31 words
The method of claim 27 wherein said growth temperature for silicon carbide is 525 Celsius, germanium silicide is 310 Celsius, tin germanide is 270 Celsius and germanium Carbide is 450 Celsius.
Claim 31
Dependent Claim
43 words
The method of claim 16 wherein said halogen-group IVB containing gas for the ALE growth of silicon carbide is SiCl 4 , of germanium silicide is GeBr 4 , of tin germanide is SnI 4 and of germanium is carbide GeF 4 .
Claim 32
Dependent Claim
26 words
The method of claim 16 wherein said desorbing steps comprise removing all of the physisorbed species of said first and second reactant gases by vacuum evacuation.
Claim 33
Independent Claim
183 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a non-stoichiometric compound of an elemental semiconductor comprising the steps of: (1) hydrogenating said surface of said substrate; (2) exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer; (3) desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; (4) exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer; (5) desorbing said second layer on said substrate of all physisorbed species of said second reactant gas; (6) repeating step (2) thereby growing a third layer; (7) repeating step (3); (8) repeating step (4) thereby growing a fourth layer; (9) repeating step (5); (10) repeating step (2) thereby growing a fifth layer; (11) repeating step (3); (12) exposing said fifth layer on said substrate to a third reactant gas thereby growing a sixth layer; and (13) desorbing said sixth layer on said substrate of all physisorbed species of said third reactant gas.
Claim 34
Independent Claim
183 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a non-stoichiometric compound of an elemental semiconductor comprising the steps of: (1) hydrogenating said surface of said substrate; (2) exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer; (3) desorbing said first layer on said substrate of all physisorbed species of said first reactant gas; (4) exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer; (5) desorbing said second layer on said substrate of all physisorbed species of said second reactant gas; (6) repeating step (2) thereby growing a third layer; (7) repeating step (3); (8) repeating step (4) thereby growing a fourth layer; (9) repeating step (5); (10) repeating step (2) thereby growing a fifth layer; (11) repeating step (3); (12) exposing said fifth layer on said substrate to a third reactant gas thereby growing a sixth layer; and (13) desorbing said sixth layer on said substrate of all physisorbed species of said third reactant gas.
Claim 35
Dependent Claim
12 words
The method of claim 31 wherein said non-stoichiometric compound is Si.sub..8 C.sub..2.
Claim 36
Dependent Claim
30 words
The method of claim 32 wherein said first reactant gas is SiF 4 , said second reactant gas is SiH 4 and said third reactant gas is CH 4 .
Claim 37
Independent Claim
259 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a non-stoichiometric compound of an elemental semiconductor comprising the steps of: (1) hydrogenating said surface of said substrate; (2) exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer; (3) desorbing said first layer of said substrate of all physisorbed species on said first reactant gas; (4) exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer; (5) desorbing said second layer on said substrate of all physisorbed species of said second reactant gas; (6) exposing said second layer on said substrate to a third reactant gas thereby growing thereon a third layer; (7) desorbing said third layer on said substrate of all physisorbed species of said third reactant gas; (8) exposing said third layer on said substrate to a fourth reactant gas thereby growing thereon a fourth layer; (9) desorbing said fourth layer on said substrate of all physisorbed species of said fourth reactant gas; (10) repeating step (6) thereby growing a fifth layer; (11) repeating step (7); (12) repeating step (4) thereby growing a sixth layer; (13) repeating step (5); (14) repeating step (2) thereby growing a seventh layer; (15) repeating step (3); (16) repeating step (8) thereby growing an eighth layer; (17) repeating step (9); (18) repeating step (6) thereby growing a ninth layer; (19) repeating step (7); (20) repeating step (8) thereby growing a tenth layer; and (21) repeating step (9).
Claim 38
Independent Claim
259 words
A method of atomic layer epitaxial (ALE) growth of a thin film upon a surface of a substrate of a non-stoichiometric compound of an elemental semiconductor comprising the steps of: (1) hydrogenating said surface of said substrate; (2) exposing said surface of said substrate to a first reactant gas thereby growing thereon a first layer; (3) desorbing said first layer of said substrate of all physisorbed species on said first reactant gas; (4) exposing said first layer on said substrate to a second reactant gas thereby growing thereon a second layer; (5) desorbing said second layer on said substrate of all physisorbed species of said second reactant gas; (6) exposing said second layer on said substrate to a third reactant gas thereby growing thereon a third layer; (7) desorbing said third layer on said substrate of all physisorbed species of said third reactant gas; (8) exposing said third layer on said substrate to a fourth reactant gas thereby growing thereon a fourth layer; (9) desorbing said fourth layer on said substrate of all physisorbed species of said fourth reactant gas; (10) repeating step (6) thereby growing a fifth layer; (11) repeating step (7); (12) repeating step (4) thereby growing a sixth layer; (13) repeating step (5); (14) repeating step (2) thereby growing a seventh layer; (15) repeating step (3); (16) repeating step (8) thereby growing an eighth layer; (17) repeating step (9); (18) repeating step (6) thereby growing a ninth layer; (19) repeating step (7); (20) repeating step (8) thereby growing a tenth layer; and (21) repeating step (9).
Claim 39
Dependent Claim
12 words
The method of claim 34 wherein said non-stoichiometric compound is Si.sub..4 Ge.sub..6.
Claim 40
Dependent Claim
38 words
The method of claim 35 wherein said first reactant gas is SiCl 4 , said second reactant gas is SiH 4 , said third reactant gas is GeCl 4 and said fourth reactant gas is GeH 4 .
References Cited (Backward Citations)
US4058430A
Cited
JPS58137218A
Cited
US4477311A
Cited
US4579609A
Cited
GB2162206A
Cited
US4829022A
Cited
JPS62179113A
Cited
JPS62189721A
Cited
US4859625A
Cited
US4933300A
Cited
US4845049A
Cited
US4859627A
Cited
JPH0260827A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-05 | 1997-01-04 | 1997-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-05 | 2001-01-04 | 2001-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-05 | 2005-01-04 | 2005-07-06 | $7700.00 | Window Closed / Lapsed |