Multi-layer photoresist air bridge fabrication method
Assignee: Conexant Systems LLC
•
Filing: 1990-12-17
•
Granted: 1993-06-15
•
Expires: 2010-12-17
Abstract
Abstract The method of constructing an air bridge on a substrate between spaced apart conductors on the substrate with the bridge spanning the distance between the conductors, by using PMGI to build a bridge pad on the substrate; using PMMA to build a bridge pattern over the pad with the ends of said conductors extending into said pattern; depositing titanium and gold over said pad within said pattern by directing the titanium and gold into said pattern onto said pad and conductor ends using relative motion between the substrate and the titanium and gold; and removing the PMGI and PMMA.
Inventors
- 👤 Gerald D. Robinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:23
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/094; H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/063; H10W20/071; H10W20/072; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4432; H10W20/45; H10W20/46; H10W20/482; H10W20/483
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
277 words
The method of constructing an air bridge on a substrate electrically interconnecting a first conductor and a second conductor on the substrate and spanning one or more objects on substrate, comprising the steps of: depositing a layer of PMGI on the substrate; depositing a first layer of photoresist over the PMGI layer; photolithographically defining a bridge pad region in the first photoresist layer; exposing the PMGI layer to deep ultra violet radiation and developing the PMGI layer through the first photoresist layer; removing the exposed and developed portions of the PMGI layer and the first photoresist layer, leaving a bridge pad formed on the substrate; heating the bridge pad to the transitional temperature of PMGI to round the corners and taper the edges of the pad; depositing a layer of PMMA over the substrate and the bridge pad; depositing a second layer of photoresist over the PMMA layer; photolithographically defining a bridge pattern in the second photoresist layer over the bridge pad; exposing the PMMA layer to deep ultra violet radiation and overdeveloping the PMMA layer through the second photoresist layer; removing the exposed and overdeveloped portions of the PMMA layer to form a first undercut in the PMMA layer under the second photoresist layer and over at least a portion of the first conductor and to form a second undercut in the PMMA layer under the second photoresist layer and over at least a portion of the second conductor; evaporation titanium and gold to deposit a conductive layer over the bridge pad and connecting to the first conductor and to the second conductor; and removing the second photoresist layer, the PMMA layer, and the PMGI layer.
Claim 2
Independent Claim
277 words
The method of constructing an air bridge on a substrate electrically interconnecting a first conductor and a second conductor on the substrate and spanning one or more objects on substrate, comprising the steps of: depositing a layer of PMGI on the substrate; depositing a first layer of photoresist over the PMGI layer; photolithographically defining a bridge pad region in the first photoresist layer; exposing the PMGI layer to deep ultra violet radiation and developing the PMGI layer through the first photoresist layer; removing the exposed and developed portions of the PMGI layer and the first photoresist layer, leaving a bridge pad formed on the substrate; heating the bridge pad to the transitional temperature of PMGI to round the corners and taper the edges of the pad; depositing a layer of PMMA over the substrate and the bridge pad; depositing a second layer of photoresist over the PMMA layer; photolithographically defining a bridge pattern in the second photoresist layer over the bridge pad; exposing the PMMA layer to deep ultra violet radiation and overdeveloping the PMMA layer through the second photoresist layer; removing the exposed and overdeveloped portions of the PMMA layer to form a first undercut in the PMMA layer under the second photoresist layer and over at least a portion of the first conductor and to form a second undercut in the PMMA layer under the second photoresist layer and over at least a portion of the second conductor; evaporation titanium and gold to deposit a conductive layer over the bridge pad and connecting to the first conductor and to the second conductor; and removing the second photoresist layer, the PMMA layer, and the PMGI layer.
Claim 3
Dependent Claim
51 words
The method of claim 1, wherein: the PMGI layer is established by spinning onto the substrate PMGI at about 4,000 rpm for about 40 seconds, baking the spun on PMGI at about 190° C. for approximately 30 minutes, and repeating the above until approximately 2 microns of PMGI comprise said layer.
Claim 4
Dependent Claim
31 words
The method of claim 1, wherein: the deep ultra violet radiation applied to the PMGI layer requires about 10 milliwatts per square centimeter at about 248 nanometer for about 10 minutes.
Claim 5
Dependent Claim
35 words
The method of claim 1, wherein: the deep ultra violet radiation applied to the PMMA layer requires about 10 milliwatts per square centimeter at a wave length of about 248 nanometers for about 5 minutes.
Claim 6
Dependent Claim
38 words
The method of claim 1, wherein the step of removing the exposed and developed portions of the PMGI layer and the first photoresist layer further comprises removing the first photoresist layer with acetone followed by an isopropyl rinse.
Claim 7
Dependent Claim
95 words
The method of claim 1, wherein the step of evaporating titanium and gold to deposit a conductive layer over the bridge pad further comprises mounting the substrate on an evaporation tilt fixture with the long bridge dimension perpendicular to the tilt axis if the bridges are all oriented in the same direction and at 45° to the tilt axis if the bridges are both horizontal and vertical and evaporating the titanium and gold conductive layer using an E-beam source while tilting the substrate through approximately 20° positive and negative angles relative to the beam source.
Claim 8
Dependent Claim
25 words
The method of claim 1, wherein the step of heating the bridge pad is done in an oven at about 250° C. for 10-60 seconds.
References Cited (Backward Citations)
US3331125A
Cited
US3932226A
Cited
JPS5448181A
Cited
US4289846A
Cited
JPS57104665A
Cited
US4601915A
Cited
US4642259A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-14 | 1996-12-14 | 1997-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-14 | 2000-12-14 | 2001-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-14 | 2004-12-14 | 2005-06-15 | $7700.00 | Window Closed / Lapsed |