Method of fabricating air supported crossovers
Assignee: General Dynamics Mission Systems Inc
•
Filing: 1984-09-24
•
Granted: 1986-07-22
•
Expires: 2004-09-24
Abstract
Abstract A method is disclosed for the fabrication of an air supported crossover bridge which consists of a polyimide coating being set over the metalized device. Then, supports are defined for the crossover and the crossover is added. Once the crossover has been added the excess is removed and the polyimide layer is removed leaving the air supported bridge.
Inventors
- 👤 Donald E. Allen
- 👤 Richard A. Gross
- 👤 Howard D. Knuth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:18
CPC Classifications
H; H03; H03H; H03H3/00; H03H3/007; H03H3/08; H03H9/00; H03H9/02; H03H9/02535; H03H9/02992; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/072; H10W20/40; H10W20/45; H10W20/46; H03H9/125; H03H9/145; H03H9/14502; H03H9/14508
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
110 words
A method of fabricating an air supported crossover device comprising the steps of: providing a substrate; cleaning said substrate; depositing aluminum on said substrate; masking said aluminum with a first photoresist defining a conductor; removing said aluminum about said first photoresist removing said first photoresist providing a metalized substrate; coating said metalized substrate with a polyimide; curing said polyimide partially; delineating a via pattern on said polyimide; curing said polimide totally; coating said polyimide coated metalized substrate with a metal layer; delineating a support pattern on said metal layer; delineating a crossover pattern on the support pattern; and removing an excess of said metal layer, leaving said crossover and support.
Claim 2
Independent Claim
110 words
A method of fabricating an air supported crossover device comprising the steps of: providing a substrate; cleaning said substrate; depositing aluminum on said substrate; masking said aluminum with a first photoresist defining a conductor; removing said aluminum about said first photoresist removing said first photoresist providing a metalized substrate; coating said metalized substrate with a polyimide; curing said polyimide partially; delineating a via pattern on said polyimide; curing said polimide totally; coating said polyimide coated metalized substrate with a metal layer; delineating a support pattern on said metal layer; delineating a crossover pattern on the support pattern; and removing an excess of said metal layer, leaving said crossover and support.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein said steps of delineating a via of said polyimide coat comprises the steps of: masking a pattern defining said via with a second photoresist; removing said polyimide from said via; and removing said second photoresist.
Claim 4
Dependent Claim
53 words
The method of claim 1 wherein said step of coating said polyimide coated metalized substrate with a metal layer comprises the steps of: depositing a layer of chrome on said polyimide coated metalized substrate; depositing a layer of nickel on said chrome layer; and depositing a layer of gold on said nickel layer.
Claim 5
Dependent Claim
57 words
The method of claim 3 wherein said step of delineating said support pattern on said metal layer comprises the steps of: masking a pattern defining said support with a third photoresist; plating a layer of copper on said device; and removing said third photoresist thereby exposing a portion of said metal layer which will become said support.
Claim 6
Dependent Claim
41 words
The method of claim 4 wherein said step of delineating a crossover pattern on the support pattern comprises the steps of: masking a pattern defining a crossover with a fourth photoresist; plating said crossover with gold; and removing said fourth photoresist.
Claim 7
Dependent Claim
83 words
The method of claim 5 wherein said step of removing said excess of said metal layer comprises the steps of; removing said copper leaving an air gap below a portion of said crossover; removing a portion of said gold layer, leaving said gold crossover and a gold portion of said support; removing a potion of said nickel layer, leaving a nickel portion of said support; removing a portion of said chrome layer, leaving a chrome portion of said support; and removing said polyimide.
Claim 8
Dependent Claim
29 words
The method of claim 1 wherein said step of coating said device with a polyimide is accomplished through a spin application to obtain an even flow over said device.
Claim 9
Independent Claim
231 words
A method of fabricating an air supported crossover device comprising the steps of: providing a substrate definfing a base of said device; cleaning said substrate; depositing aluminum on said substrate; masking said aluminum with a first photoresist defining aconductor; removing said aluminum about said first photoresist; removing said first photoresist; coating the conductor and substrate with a polyimide; curing said polimide partially; masking a pattern defining a via with a second photoresist; removing said polyimide from said via; removing said second photoresist; curing said polyimide totally; depositing a layer of chrome on said polyimide layer; depositing a layer of nickel on said chrome layer; depositing a layer of gold on said nickel layer; masking a pattern defining a support with a third photoresist said support being comprised of portions of said chrome, nickel and gold layers; plating a layer of copper on said third photoresist; removing said third photoresist; masking a pattern defining a crossover with a fourth photoresist; plating said crossover area with gold; removing said fourth photoresist; removing said copper leaving an air gap below a portion of said crossover; removing a portion of said gold layer, leaving said gold crossover and said gold portion of said support; removing a portion of said nickel layer, leaving said nickel portion of said support; removing a portion of said chrome, leaving said chrome portion of said support; and removing said polyimide.
Claim 10
Independent Claim
231 words
A method of fabricating an air supported crossover device comprising the steps of: providing a substrate definfing a base of said device; cleaning said substrate; depositing aluminum on said substrate; masking said aluminum with a first photoresist defining aconductor; removing said aluminum about said first photoresist; removing said first photoresist; coating the conductor and substrate with a polyimide; curing said polimide partially; masking a pattern defining a via with a second photoresist; removing said polyimide from said via; removing said second photoresist; curing said polyimide totally; depositing a layer of chrome on said polyimide layer; depositing a layer of nickel on said chrome layer; depositing a layer of gold on said nickel layer; masking a pattern defining a support with a third photoresist said support being comprised of portions of said chrome, nickel and gold layers; plating a layer of copper on said third photoresist; removing said third photoresist; masking a pattern defining a crossover with a fourth photoresist; plating said crossover area with gold; removing said fourth photoresist; removing said copper leaving an air gap below a portion of said crossover; removing a portion of said gold layer, leaving said gold crossover and said gold portion of said support; removing a portion of said nickel layer, leaving said nickel portion of said support; removing a portion of said chrome, leaving said chrome portion of said support; and removing said polyimide.
Claim 11
Dependent Claim
29 words
The method of claim 8 wherein said step of coating said device with a polyimide is accomplished through a spin application to obtain an even flow over said device.
References Cited (Backward Citations)
US4054484A
Cited
US4436766A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-21 | 1990-01-20 | 1990-07-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-21 | 1994-01-20 | 1994-07-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-21 | 1998-01-20 | 1998-07-22 | $7700.00 | Window Closed / Lapsed |