Abstract
Abstract Disclosed is a crossover fabrication technique which is compatible with interconnect metallization for thin film and hybrid circuits which comprises a layer of copper. In one embodiment, evaporated layers of Ti and Cu are used as the base layers to build up the crossover spacing layer. A nickel protective layer is formed over the evaporated layers and the interconnect metallization. A copper spacing layer is then formed over the nickel layer by plating. Pillar holes are etched over selected areas of the interconnect metal preferably using an etchant which removes both the copper spacing layer and nickel protective layer, followed by forming the gold crossovers. The remaining copper spacing layer is removed by an etchant which preferentially attacks copper, and the nickel protective layer and copper base layers are preferably removed by a single etchant.
Inventors
- 👤 Nathan George Lesh, deceased
- 👤 executor by William B. Ketterer
- 👤 Joseph Michael Morabito
- 👤 John Henry Thomas, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:00
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H05; H05K; H05K3/00; H05K3/46; H05K3/4685
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
186 words
A method of forming a conductive crossover connection between at least two conductors formed on an insulating substrate over an area separating said conductors comprising the steps of: forming over said substrate a first copper layer; forming on selected areas of said layer at least two conductors including a second layer of copper; forming a layer of nickel over said first copper layer and said conductors; plating over said nickel layer a third copper layer; removing selected areas of said third copper layer and said nickel layer over at least two of said conductors so as to expose said conductors in said areas, forming over the conductors in said selected areas and over the remaining third copper layer in the space between conductors a conductive metal so as to form a conductive connection between said conductors; removing said third copper layer with an etchant which does not significantly etch the nickel layer such that the first and second copper layers in the conductors are protected from the etchant; removing said nickel layer; and removing the areas of said first copper layer not covered by said conductors.
Claim 2
Independent Claim
186 words
A method of forming a conductive crossover connection between at least two conductors formed on an insulating substrate over an area separating said conductors comprising the steps of: forming over said substrate a first copper layer; forming on selected areas of said layer at least two conductors including a second layer of copper; forming a layer of nickel over said first copper layer and said conductors; plating over said nickel layer a third copper layer; removing selected areas of said third copper layer and said nickel layer over at least two of said conductors so as to expose said conductors in said areas, forming over the conductors in said selected areas and over the remaining third copper layer in the space between conductors a conductive metal so as to form a conductive connection between said conductors; removing said third copper layer with an etchant which does not significantly etch the nickel layer such that the first and second copper layers in the conductors are protected from the etchant; removing said nickel layer; and removing the areas of said first copper layer not covered by said conductors.
Claim 3
Dependent Claim
26 words
The method according to claim 1 further comprising the step of, prior to forming said first copper layer, forming a layer of titanium over said substrate.
Claim 4
Dependent Claim
17 words
The method according to claim 2 wherein said titanium and first copper layers are formed by evaporation.
Claim 5
Dependent Claim
23 words
The method according to claim 1 wherein the layer of nickel is formed by plating to a thickness of at least 6,000 A.
Claim 6
Dependent Claim
21 words
The method according to claim 1 wherein said third copper layer is plated to a thickness in the range 1-2 mils.
Claim 7
Dependent Claim
23 words
The method according to claim 4 wherein the third copper layer is plated over said nickel layer before said nickel layer is dry.
Claim 8
Dependent Claim
24 words
The method according to claim 1 wherein the third copper layer and nickel layer are removed in said selected areas by a single etchant.
Claim 9
Dependent Claim
12 words
The method according to claim 1 wherein the conductive metal comprises gold.
Claim 10
Dependent Claim
18 words
The method according to claim 1 wherein the etchant for removing the third copper layer comprises ammonium persulfate.
Claim 11
Dependent Claim
21 words
The method according to claim 1 wherein said nickel layer and said first copper layer are removed by a single etchant.
Claim 12
Independent Claim
257 words
A method of forming a conductive crossover connection between at least two conductors formed on an insulating substrate over an area separating said conductors, comprising the steps of: forming a layer of titanium over said substrate; forming a first copper layer over said titanium layer; forming on selected areas of said first copper layer at least two conductors comprising successively a second layer of copper, a first layer of nickel and a layer of gold; plating a second layer of nickel over said first copper layer and said conductors to a thickness of at least 6,000 A; plating a third copper layer over said second nickel layer to a thickness in the range 1-2 mils before said nickel layer dries; removing by a single etchant selected areas of said third copper layer and said second nickel layer over said conductors to be connected so as to expose said conductors in said areas; plating over the conductors in said selected areas and over the remaining third copper layer in the space between conductors a conductive metal comprising gold to a thickness in the range 1-2 mils so as to form a conductive connection between said conductors; removing said third copper layer with an etchant which does not significantly etch the said second nickel layer such that the first and second copper layers in the conductors are protected from the etchant; removing said second nickel layer and the area of said first copper layer not covered by said conductors with a single etchant; and removing said layer of titanium.
Claim 13
Independent Claim
257 words
A method of forming a conductive crossover connection between at least two conductors formed on an insulating substrate over an area separating said conductors, comprising the steps of: forming a layer of titanium over said substrate; forming a first copper layer over said titanium layer; forming on selected areas of said first copper layer at least two conductors comprising successively a second layer of copper, a first layer of nickel and a layer of gold; plating a second layer of nickel over said first copper layer and said conductors to a thickness of at least 6,000 A; plating a third copper layer over said second nickel layer to a thickness in the range 1-2 mils before said nickel layer dries; removing by a single etchant selected areas of said third copper layer and said second nickel layer over said conductors to be connected so as to expose said conductors in said areas; plating over the conductors in said selected areas and over the remaining third copper layer in the space between conductors a conductive metal comprising gold to a thickness in the range 1-2 mils so as to form a conductive connection between said conductors; removing said third copper layer with an etchant which does not significantly etch the said second nickel layer such that the first and second copper layers in the conductors are protected from the etchant; removing said second nickel layer and the area of said first copper layer not covered by said conductors with a single etchant; and removing said layer of titanium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-17 | 1981-04-18 | 1981-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-17 | 1985-04-18 | 1985-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-17 | 1989-04-18 | 1989-10-18 | $7700.00 | Window Closed / Lapsed |