Hermetic package for an electronic device and method of manufacturing same
Assignee: International Business Machines Corp
•
Filing: 1989-10-06
•
Granted: 1993-03-16
•
Expires: 2009-10-06
Abstract
Abstract A hermetic package for an electronic device is manufactured by providing a green glass ceramic body with a green via to produce a workpiece. The workpiece is sintered at a temperature at or above 500° C., while compressing the workpiece at a pressure at or above 100 pounds per square inch, so as to obtain a hermetic package. The green via comprises a mixture of copper and a glass ceramic material with a sufficient volume of glass to produce a hermetic package, yet with sufficient copper to have a suitable electrical conductivity. The hermetic package thus produced comprises a sintered glass ceramic body having an electrically conductive sintered via which is hermetically bonded to the glass ceramic body and which comprises a mixture of an electrically conductive material and a glass ceramic material. The electrically conductive material forms at most 50 volume percent of the via. The workpiece may be sintered in a sintering fixture having a frame and a compensating insert. The compensating insert and frame bound a sintering chamber for accommodating the workpiece. By providing a frame having a thermal expansion coefficient greater than that of the workpiece, and by providing a compensating insert having a thermal expansion coefficient greater than that of the frame, a close fit can be assured between the workpiece and the sintering fixture over a large range of temperatures.
Inventors
- 👤 Dudley A. Chance
- 👤 David B. Goland
- 👤 Ho-Ming Tong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 01:06
CPC Classifications
H; H10; H10W; H10W95/00; H10W70/00; H10W70/01; H10W70/05; H10W70/095; H10W99/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
172 words
A method of manufacturing a hermetic package for an electronic device, said method comprising the steps of: providing a green glass ceramic body, wherein the glass is a crystallizable glass, having first and second opposite surface and an axis extending from the first surface to the second surface, said green glass ceramic body having a thickness in the direction of the axis, said green glass ceramic body having an edge connecting the first and second opposite surfaces, said green glass ceramic body being substantially electrically insulating; providing a green via in the green glass ceramic body, said green via extending from the first surface to the second surface, said green via comprising a mixture of an electrically conductive material and a glass ceramic material, said green glass ceramic body and green via forming a workpiece; sintering the workpiece at a temperature at or above 500° C.; and compressing the workpiece at a pressure at or above 100 pounds per square inch while sintering the workpiece, so as to obtain a hermetic package.
Claim 2
Independent Claim
172 words
A method of manufacturing a hermetic package for an electronic device, said method comprising the steps of: providing a green glass ceramic body, wherein the glass is a crystallizable glass, having first and second opposite surface and an axis extending from the first surface to the second surface, said green glass ceramic body having a thickness in the direction of the axis, said green glass ceramic body having an edge connecting the first and second opposite surfaces, said green glass ceramic body being substantially electrically insulating; providing a green via in the green glass ceramic body, said green via extending from the first surface to the second surface, said green via comprising a mixture of an electrically conductive material and a glass ceramic material, said green glass ceramic body and green via forming a workpiece; sintering the workpiece at a temperature at or above 500° C.; and compressing the workpiece at a pressure at or above 100 pounds per square inch while sintering the workpiece, so as to obtain a hermetic package.
Claim 3
Dependent Claim
55 words
A method as claimed in claim 1, characterized in that: the workpiece has a free sintering densification rate when it is sintered without being compressed; the workpiece has a pressure sintering densification rate when it is sintered while being compressed; and the pressure sintering densification rate is much greater than the free sintering densification rate.
Claim 4
Dependent Claim
16 words
A method as claimed in claim 1, characterized in that the green via contains a metal.
Claim 5
Dependent Claim
31 words
A method as claimed in claim 3, characterized in that the green via consists essentially of: 20 to 50 volume percent metal; and 80 to 50 volume percent glass ceramic material.
Claim 6
Dependent Claim
14 words
A method as claimed in claim 4, characterized in that the metal is copper.
Claim 7
Dependent Claim
51 words
A method as claimed in claim 1, further comprising the steps of: measuring the thickness of the workpiece; measuring the edge bulge of the workpiece; and varying the pressure on the workpiece as a function of the measured thickness and as a function of the measured edge profile of the workpiece.
Claim 8
Dependent Claim
92 words
A method as claimed in claim 6, characterized in that the step of compressing the workpiece comprises compressing the workpiece at a pressure, P, substantially given by the equation ##EQU16## where γ is the surface tension of the workpiece at the sintering temperature, D is the ratio of the density of the workpiece divided by the theoretical maximum density of the workpiece, R O is the initial radius of the workpiece, θ is the edge bulge, h is the height of the workpiece, and n is the pore density in the workpiece.
Claim 9
Dependent Claim
49 words
A method as claimed in claim 1, further comprising the steps of: measuring the thickness of the workpiece; measuring the width of the workpiece; and varying the pressure on the workpiece as a function of the measured thickness and as a function of the measured width of the workpiece.
Claim 10
Dependent Claim
26 words
A method as claimed in claim 1, characterized in that the step of compressing the workpiece comprises compressing the workpiece until it has a selected thickness.
Claim 11
Dependent Claim
54 words
A method as claimed in claim 1, characterized in that: the step of compressing the workpiece comprises compressing the workpiece in the direction of the axis only; and during the step of compressing the workpiece, the edges of the workpiece are supported only by the workpiece itself in a direction transverse to the axis.
Claim 12
Dependent Claim
53 words
A method as claimed in claim 1, characterized in that: the step of sintering comprises sintering the workpiece at a temperature in the range from 750° C. to 960° C.; and the step of compressing comprises compressing the workpiece at a pressure in the range from 100 to 5000 pounds per square inch.
Claim 13
Dependent Claim
53 words
A method as claimed in claim 11, characterized in that: the step of sintering comprises sintering the workpiece at a temperature in the range from 850° C. to 870° C.; and the step of compressing comprises compressing the workpiece at a pressure in the range from 800 to 1000 pounds per square inch.
References Cited (Backward Citations)
US3436451A
Cited
GB1281899A
Cited
US4009238A
Cited
US3963449A
Cited
US3992160A
Cited
US4110084A
Cited
US4301324A
Cited
US4234367A
Cited
US4340436A
Cited
US4381931A
Cited
US4524138A
Cited
US4499049A
Cited
US4640711A
Cited
US4612689A
Cited
JPS6131361A
Cited
JPS61139438A
Cited
EP0243858A2
Cited
US4879156A
Cited
WO1989001461A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-03-15 | 1996-09-14 | 1997-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-03-15 | 2000-09-14 | 2001-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-03-15 | 2004-09-14 | 2005-03-16 | $7700.00 | Window Closed / Lapsed |