Method of making multilayered glass-ceramic structures having an internal distribution of copper-based conductors
Assignee: International Business Machines Corp
•
Filing: 1979-03-23
•
Granted: 1980-11-18
•
Expires: 1999-03-23
Abstract
Abstract The formation of sintered glass-ceramic substrates containing multi-level, interconnected thick-film circuit patterns of copper-based conductors obtained by firing in a controlled ambient of hydrogen and H2O at temperatures below the melting point of copper.
Inventors
- 👤 Lester W. Herron
- 👤 Raj N. Master
- 👤 Rao R. Tummala
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:38
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C27/00; H; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/098; H10W99/00; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629; H05K3/4644; H05K3/4673; H05K3/4676
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
191 words
A method of forming a glass-ceramic composite structure with copper based metallurgy comprising: forming at least one green sheet comprised of a thermoplastic organic binder having dispersed therein particles of a crystallizable glass having a crystallization temperature below the melting point of copper; forming on a surface of a first said green sheet a pattern of a nonrefractory copper based conductor forming composition wherein the predominant component of said conductor is copper; superimposing a second said sheet on said surface of said first sheet to sandwich said pattern therebetween; laminating said superimposed sheets together; heating said laminate in an ambient of hydrogen and H 2 O in a ratio of H 2 /H 2 O=about 10 -4 to about 10 -6 .5 to a burn-out temperature in the range between the anneal and softening points of said glass and maintained thereat for sufficient time to decompose and eliminate said binder, substituting an inert atmosphere for said ambient; and heating said laminate to the crystallization temperature of said glass for coalescence of said glass particles and crystallization thereof into a glass-ceramic structure have a copper-based conductor pattern extending within the interior thereof.
Claim 2
Independent Claim
191 words
A method of forming a glass-ceramic composite structure with copper based metallurgy comprising: forming at least one green sheet comprised of a thermoplastic organic binder having dispersed therein particles of a crystallizable glass having a crystallization temperature below the melting point of copper; forming on a surface of a first said green sheet a pattern of a nonrefractory copper based conductor forming composition wherein the predominant component of said conductor is copper; superimposing a second said sheet on said surface of said first sheet to sandwich said pattern therebetween; laminating said superimposed sheets together; heating said laminate in an ambient of hydrogen and H 2 O in a ratio of H 2 /H 2 O=about 10 -4 to about 10 -6 .5 to a burn-out temperature in the range between the anneal and softening points of said glass and maintained thereat for sufficient time to decompose and eliminate said binder, substituting an inert atmosphere for said ambient; and heating said laminate to the crystallization temperature of said glass for coalescence of said glass particles and crystallization thereof into a glass-ceramic structure have a copper-based conductor pattern extending within the interior thereof.
Claim 3
Dependent Claim
48 words
The method of claim 1 wherein said glass particles have the composition, by weight percent, ______________________________________
MgO 22 to 24.2 Al.sub.2 O.sub.3
21 to 22
SiO.sub.2 50.6 to 52.5 P.sub.2 O.sub.5
0 to 2
B.sub.2 O.sub.3
0.5 to 2 ZrO.sub.2 0 to 2
SnO.sub.2 0 to 2
______________________________________
Claim 4
Dependent Claim
21 words
The method of claim 1 including providing means for extending said pattern to at least one surface of said fired laminate.
Claim 5
Dependent Claim
24 words
The method of claim 3 including mounting an integrated semiconductor chip on said surface in electrical connection to a portion of said pattern extension.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein said glass is selected from the group of β-spdoumene or cordierite glasses.
Claim 7
Dependent Claim
27 words
The method of claim 5 wherein said laminate is heated in said ambient to a burn-out temperature in the range of about 720°±10° to about 785°±10° C.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein said laminate is heated to said burn-out temperature at a rate of about 1° to 3° C. per minute.
Claim 9
Dependent Claim
37 words
The method of claim 6 wherein the H 2 /H 2 O ratio of said ambient is continuously changed from about 10 -6 .5 to about 10 -4 over the course of said heating in said ambient.
Claim 10
Dependent Claim
27 words
The method of claim 8 wherein said laminate is preheated in an inert atmosphere to a temperature of about 100° C. prior to heating in said ambient.
Claim 11
Dependent Claim
29 words
The method of claim 6 wherein the H 2 /H 2 O ratio of said ambient is about 10 -4 over the course of said heating in said ambient.
Claim 12
Dependent Claim
29 words
The method of claim 10 wherein said laminate is preheated in an inert atmosphere to said burn-out temperature prior maintainance thereat in said ambient for burn-out of said binder.
Claim 13
Dependent Claim
20 words
The method of claim 5 wherein said crystallization temperature is in the range of about 920° to about 970° C.
Claim 14
Dependent Claim
25 words
The method of claim 12 wherein said laminate is heated to said crystallization temperature at a rate of about 1° to 3° C. per minute.
Claim 15
Dependent Claim
32 words
The method of claim 1 wherein said glass-ceramic selected from the group having Li 2 O.Al 2 O 3 .4SiO 2 β-spdoumene or 2MgO.2Al 2 O 3 .5SiO 2 alphacordierite crystalline phases.
Claim 16
Dependent Claim
26 words
The methods of claims 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14 wherein said conductor is a copper alloy.
Claim 17
Independent Claim
25 words
The method of claims 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14 wherein said conductor is substantially copper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-18 | 1984-05-19 | 1984-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-18 | 1988-05-19 | 1988-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-18 | 1992-05-19 | 1992-11-18 | $7700.00 | Window Closed / Lapsed |