Multilayered ceramic substrate having solid non-porous metal conductors
Assignee: International Business Machines Corp
•
Filing: 1988-03-14
•
Granted: 1989-11-07
•
Expires: 2008-03-14
Abstract
Abstract A multilayered ceramic (MLC) substrate having embedded and exposed conductors suitable for mounting and interconnecting a plurality of electronic devices exterior thereof. The horizontal planar conductors comprise substantially a plurality of solid, non-porous, homogeneous metal patterns, whereas the vertical interplanar connection conductors are substantially porous metal conductors that are formed by methods such as screening. The process to form the MLC substrate involves forming a pattern of solid, nonporous conductors to a backing sheet having a release layer, then transferring the pattern to a ceramic green sheet. Zero X-Y shrinkage sintering processes allow the MLC substrate and solid metal conductors to be densified without distortion of the solid metal patterns or the ceramic.
Inventors
- 👤 Lester W. Herron
- 👤 Robert O. Lussow
- 👤 Robert W. Nufer
- 👤 Bernard Schwartz
- 👤 John Acocella
- 👤 Srinivasa N. Reddy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:50
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H05; H05K; H05K3/00; H05K3/10; H05K3/20; H10W70/60; H10W70/611; H10W70/67; H10W70/68; H10W70/685; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/03; H05K2201/0302; H05K2201/0317; H05K2203/00; H05K2203/01; H05K2203/0147; H05K2203/0156; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24273; Y10T428/24322; Y10T428/24802; Y10T428/24917; Y10T428/24926; Y10T428/24942; Y10T428/26
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
159 words
A multilayer ceramic substrate having a network of exposed and encapsulated metal conductors adapted for mounting and interconnecting a plurality of electronic devices exterior thereof consisting solely of; a monolithic sintered ceramic body, an exposed pattern of solid metal conductors on the surface of said body, a plurality of spaced-apart planar patterns of solid metal conductors encapsulated in said body, each of which has a predetermined configuration, and means provided conducting pathways between predetermined areas of said spaced-apart planar patterns and between predetermined areas of said spaced-apart planar patterns and predetermined areas of said exposed pattern of solid metal conductors; wherein the ceramic material has a lower sintering temperature than the melting point of said metal conductors; and wherein said ceramic substrate has been sintered at a temperature less than the melting point of said metal conductors but high enough to densify the ceramic material, while simultaneously restraining the ceramic substrate from shrinkage in the X and Y directions.
Claim 2
Dependent Claim
159 words
A multilayer ceramic substrate having a network of exposed and encapsulated metal conductors adapted for mounting and interconnecting a plurality of electronic devices exterior thereof consisting solely of; a monolithic sintered ceramic body, an exposed pattern of solid metal conductors on the surface of said body, a plurality of spaced-apart planar patterns of solid metal conductors encapsulated in said body, each of which has a predetermined configuration, and means provided conducting pathways between predetermined areas of said spaced-apart planar patterns and between predetermined areas of said spaced-apart planar patterns and predetermined areas of said exposed pattern of solid metal conductors; wherein the ceramic material has a lower sintering temperature than the melting point of said metal conductors; and wherein said ceramic substrate has been sintered at a temperature less than the melting point of said metal conductors but high enough to densify the ceramic material, while simultaneously restraining the ceramic substrate from shrinkage in the X and Y directions.
Claim 3
Dependent Claim
32 words
The multilayer ceramic substrate of claim 1 wherein the ceramic material has a sintering temperature lower than 1000° C. and the solid metal conductors have a melting point greater than ° C.
Claim 4
Dependent Claim
14 words
The multilayer ceramic substrate of claim 1 wherein the ceramic is a glass ceramic.
Claim 5
Dependent Claim
19 words
The multilayer ceramic substrate of claim 1 wherein the metal conductors have a resistivity less than 2×10 -6 ohm-cm.
Claim 6
Dependent Claim
29 words
The multilayer ceramic of claim 4 wherein the solid metal of the conductor is selected from a group consisting of copper, silver, gold or alloys of silver and copper.
Claim 7
Dependent Claim
34 words
The multilayer ceramic substrate of claim 1 wherein said exposed pattern of solid metal conductors is provided with pads having patterns complementary to the exposed pads of semiconductor chips to be conductively affixed thereto.
Claim 8
Dependent Claim
25 words
The multilayer ceramic substrate of claim 1 wherein said planar patterns of solid metal conductors comprise a plurality of discrete spaced-apart linear conductors substantially co-planar.
Claim 9
Dependent Claim
34 words
The multilayer ceramic substrate of claim 7 wherein said linear conductors have a width in the range of 0.5 to 4 mils and an interconductor spacing in the range of 1 to 16 mils.
Claim 10
Dependent Claim
20 words
The multilayer ceramic substrate of claim 7 wherein said linear conductors have a width in the range of 2-10 micrometers.
Claim 11
Dependent Claim
49 words
The multilayer ceramic substrate of claim 1 wherein said means providing conducting pathways between said predetermined areas of said spaced-apart planar patterns and between predetermined areas of said spaced-apart planar patterns and predetermined areas of said exposed pattern of solid metal conductors, comprise sintered metal conductors in via holes.
Claim 12
Dependent Claim
47 words
The multilayer ceramic substrate of claim 1 wherein said means providing conducting pathways between adjacent spaced-apart planar patterns comprise thickened studs on the adjacent patterns and a metal interposed therebetween, said interposed metal having a melting point substantially equal to the sintering temperature of the selecting ceramic.
Claim 13
Dependent Claim
44 words
The multilayer ceramic substrate of claim 1 wherein the solid pattern of exposed metal conductors on the surface of said body comprise thickened studs raised from the pattern of the next adjacent planar pattern of solid conductors, said studs protruding outside of said body.
References Cited (Backward Citations)
US3852877A
Cited
US3879509A
Cited
US4301324A
Cited
US4221047A
Cited
US4234367A
Cited
US4642148A
Cited
US4761325A
Cited
US4766027A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-06 | 1993-05-08 | 1993-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-06 | 1997-05-08 | 1997-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-06 | 2001-05-08 | 2001-11-07 | $7700.00 | Window Closed / Lapsed |