Polymer gel manufacturing methods
Assignee: Canon Inc
•
Filing: 1989-10-19
•
Granted: 1993-02-02
•
Expires: 2009-10-19
Abstract
Abstract Disclosed are a polymer gel in which a phase transition occurs due to a stimulus, a method of manufacturing such a polymer gel, and an actuator which employs such a polymer gel. The polymer gel which is formed by polymerizing monomers at a temperature equal to or less than a phase transition temperature of the resultant polymer gel and separating and/or classifying the polymer gel into fractions according to its size at a temperature equal to or greater than the phase transition temperature thereof. Alternatively, the polymer gel is separated and/or classified into fractions by adding a low molecular weight compound that can dissolve and swell the polymer gel to separate the polymer gel into fractions based upon a difference in dissolving rate or swelling rate. Alternatively separation and/or classification of the polymer gel is performed by a combination of the above-described two methods. In consequence, the resultant polymer gel has an average particle size ranging from 0.1 μm to 100 μm, and exhibits standard deviation of within 25 % of the average particle size. The width of the phase transistion peak of the resultant polymer gel as measured by DSC at a heating rate of 1 °C./min is within 10 °C. % of the
Inventors
- 👤 Satoshi Yuasa
- 👤 Yoshinori Tomida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:17
CPC Classifications
C; C08; C08F; C08F6/00; C08F6/04; C08F20/00; C08F20/02; C08F20/04; C08F20/52; C08F20/54; C08F20/56; F; F03; F03G; F03G7/00; F03G7/06; F03G7/061; F03G7/06112; F03G7/06113; F03G7/0616; Y; Y10; Y10S; Y10S526/00; Y10S526/909; Y10S526/93
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
68 words
A method of manufacturing a polymer gel comprising the steps of: preparing a polymer gel by polymerizing monomers from which a polymer gel can be formed at temperature equal to or less than a phase transition temperature of the resultant polymer gel; and separating the resultant polymer gel into fractional portions thereof at a temperature equal to or greater than the phase transition temperature of said polymer gel.
Claim 2
Independent Claim
68 words
A method of manufacturing a polymer gel comprising the steps of: preparing a polymer gel by polymerizing monomers from which a polymer gel can be formed at temperature equal to or less than a phase transition temperature of the resultant polymer gel; and separating the resultant polymer gel into fractional portions thereof at a temperature equal to or greater than the phase transition temperature of said polymer gel.
Claim 3
Dependent Claim
16 words
The method according to claim 1, wherein said monomers are (meth)acrylic acid, (meth)acrylamide, or N-substituted (meth)acrylamides.
Claim 4
Dependent Claim
14 words
The method according to claim 1, wherein said monomers include an unsaturated carboxylic acid.
Claim 5
Dependent Claim
30 words
The method according to claim 1, wherein said polymer gel is prepared by copolymerizing monomers consisting of (meth)acrylic acid, (meth)acrylamide or N-substituted (meth)acrylamides and monomers consisting of unsaturated carboxylic acid.
Claim 6
Dependent Claim
19 words
The method according to claim 1, wherein said separating step is carried out according to polymer gel particle size.
Claim 7
Dependent Claim
19 words
The method according to claim 1, wherein said separating step is carried out according to polymer gel particle composition.
Claim 8
Dependent Claim
66 words
The method according to claim 1, wherein said separating step is carried out such that where the average polymer gel particle diameter of at least one of the fractional portions ranges from 0.1 μm to 100 μm, the standard deviation in the distribution of particle diameters in said at least one fractional portion is at most 25% of the average particle diameter in that fractional portion.
Claim 9
Dependent Claim
36 words
The method according to claim 1, wherein the width of the phase transition temperature of at least one of said fractional portions measured by DSC at a heating rate of 1° C./min is within 10° C.
Claim 10
Independent Claim
64 words
A method of manufacturing a polymer gel comprising the steps of: preparing the polymer gel by polymerizing monomers from which said polymer gel is formed; and separating the resultant polymer gel by adding a low molecular weight compound that can swell the polymer gel and separating the polymer gel into fractional portions thereof based on a difference in swelling rate or degree of swelling.
Claim 11
Independent Claim
64 words
A method of manufacturing a polymer gel comprising the steps of: preparing the polymer gel by polymerizing monomers from which said polymer gel is formed; and separating the resultant polymer gel by adding a low molecular weight compound that can swell the polymer gel and separating the polymer gel into fractional portions thereof based on a difference in swelling rate or degree of swelling.
Claim 12
Dependent Claim
34 words
The method according to claim 9, wherein said monomers from which the polymer gel is formed are polymerized at a temperature equal to or greater than a phase transition temperature of said polymer gel.
Claim 13
Dependent Claim
16 words
The method according to claim 9, wherein said monomers are (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides.
Claim 14
Dependent Claim
16 words
The method according to claim 10, wherein said monomers are (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides.
Claim 15
Dependent Claim
14 words
The method according to claim 9, wherein said monomers include an unsaturated carboxylic acid.
Claim 16
Dependent Claim
14 words
The method according to claim 10, wherein said monomers include an unsaturated carboxylic acid.
Claim 17
Dependent Claim
30 words
The method according to claim 9, wherein said polymer gel is prepared by copolymerizing monomers consisting of (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides and monomers consisting of unsaturated carboxylic acid.
Claim 18
Dependent Claim
30 words
The method according to claim 10, wherein said polymer gel is prepared by copolymerizing monomers consisting of (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides and monomers consisting of unsaturated carboxylic acid.
Claim 19
Dependent Claim
19 words
The method according to claim 9, wherein said separating step is carried out according to polymer gel particle size.
Claim 20
Dependent Claim
19 words
The method according to claim 9, wherein said separating step is carried out according to polymer gel particle composition.
Claim 21
Dependent Claim
66 words
The method according to claim 9, wherein said separating step is carried out such that where the average polymer gel particle diameter of at least one of the fractional portions ranges from 0.1 μm to 100 μm, the standard deviation in the distribution of particle diameters in said at least one fractional portion is at most 25% of the average particle diameter in that fractional portion.
Claim 22
Dependent Claim
36 words
The method according to claim 9, wherein the width of a phase transition temperature of at least one of said fractional portions measured by DSC at a heating rate of 1° C./min is within 10° C.
Claim 23
Dependent Claim
19 words
The method according to claim 10, wherein said separating step is carried out according to polymer gel particle size.
Claim 24
Dependent Claim
19 words
The method according to claim 10, wherein said separating step is carried out according to polymer gel particle composition.
Claim 25
Dependent Claim
66 words
The method according to claim 10, wherein said separating step is carried out such that where the average polymer gel particle diameter of at least one of the fractional portions ranges from 0.1 μm to 100 μm, the standard deviation in the distribution of particle diameters in said at least one fractional portion is at most 25% of the average particle diameter in that fractional portion.
Claim 26
Dependent Claim
36 words
The method according to claim 10, wherein the width of the phase transition temperature of at least one of said fractional portions measured by DSC at a heating rate of 1° C./min is within 10° C.
Claim 27
Independent Claim
121 words
A method of manufacturing a polymer gel comprising the steps of: preparing the polymer gel by polymerizing monomers from which the polymer gel is formed at a temperature equal to or less than a phase transition temperature of the resultant polymer gel; separating the resultant polymer gel into first fractional portions thereof at a temperature equal to or greater than the phase transition temperature; and further separating at least one of said first fractional portions of the polymer gel by adding a low molecular weight compound that can swell said at least one first fractional portion and separating said at least one first fractional portions into second fractional portions thereof based on a difference in swelling rate or degree of swelling.
Claim 28
Independent Claim
121 words
A method of manufacturing a polymer gel comprising the steps of: preparing the polymer gel by polymerizing monomers from which the polymer gel is formed at a temperature equal to or less than a phase transition temperature of the resultant polymer gel; separating the resultant polymer gel into first fractional portions thereof at a temperature equal to or greater than the phase transition temperature; and further separating at least one of said first fractional portions of the polymer gel by adding a low molecular weight compound that can swell said at least one first fractional portion and separating said at least one first fractional portions into second fractional portions thereof based on a difference in swelling rate or degree of swelling.
Claim 29
Dependent Claim
16 words
The method according to claim 25, wherein said monomers are (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides.
Claim 30
Dependent Claim
14 words
The method according to claim 25, wherein said monomers include an unsaturated carboxylic acid.
Claim 31
Dependent Claim
30 words
The method according to claim 25, wherein said polymer gel is prepared by copolymerizing monomers consisting of (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides and monomers consisting of unsaturated carboxylic acid.
Claim 32
Dependent Claim
19 words
The method according to claim 25, wherein said separating step is carried out according to polymer gel particle size.
Claim 33
Dependent Claim
20 words
The method according to claim 29, wherein said further separating step is carried out according to polymer gel particle size.
Claim 34
Dependent Claim
20 words
The method according to claim 29, wherein said further separating step is carried out according to polymer gel particle composition.
Claim 35
Dependent Claim
19 words
The method according to claim 25, wherein said separating step is carried out according to polymer gel particle composition.
Claim 36
Dependent Claim
20 words
The method according to claim 32, wherein said further separating step is carried out according to polymer gel particle size.
Claim 37
Dependent Claim
20 words
The method according to claim 32, wherein said further separating step is carried out according to polymer gel particle composition.
Claim 38
Dependent Claim
74 words
The method according to claim 25, wherein said separating step and said further separating step are carried out such that where the average polymer gel particle diameter of at least one of the second fractional portions ranges from 0.1 μm to 100 μm, the standard deviation in the distribution of particle diameters in said at least one second fractional portion is at most 25% of the average particle diameter in that second fractional portion.
Claim 39
Dependent Claim
37 words
The method according to claim 25, wherein the width of the phase transition temperature of at least one of said second fractional portions measured by DSC at a heating rate of 1° C./min is within 10° C.
Claim 40
Independent Claim
48 words
A method of manufacturing a polymer gel comprising: preparing a dispersion by dispersing a monomer solution from which the polymer gel can be formed in a dispersion medium; and polymerizing the resultant dispersion at a temperature equal to or less than the solidifying point of the monomer solution.
Claim 41
Independent Claim
48 words
A method of manufacturing a polymer gel comprising: preparing a dispersion by dispersing a monomer solution from which the polymer gel can be formed in a dispersion medium; and polymerizing the resultant dispersion at a temperature equal to or less than the solidifying point of the monomer solution.
Claim 42
Independent Claim
81 words
A method of manufacturing a polymer gel comprising: preparing a dispersion by dispersing monomers or a monomer solution from which the polymer gel can be formed in a dispersion medium; polymerizing the resultant dispersion at a temperature equal to or less than the solidifying point of the monomers or the monomer solution; and separating the resultant polymer gel into fractional portions thereof at a temperature equal to or greater than the solidifying point of the monomers or of the monomer solution.
Claim 43
Independent Claim
81 words
A method of manufacturing a polymer gel comprising: preparing a dispersion by dispersing monomers or a monomer solution from which the polymer gel can be formed in a dispersion medium; polymerizing the resultant dispersion at a temperature equal to or less than the solidifying point of the monomers or the monomer solution; and separating the resultant polymer gel into fractional portions thereof at a temperature equal to or greater than the solidifying point of the monomers or of the monomer solution.
Claim 44
Independent Claim
18 words
The method according to claims 37 or 38, wherein said monomers are (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides.
Claim 45
Independent Claim
16 words
The method according to claims 37 or 38, wherein said monomers include an unsaturated carboxylic acid.
Claim 46
Independent Claim
32 words
The method according to claims 37 or 38, wherein said polymer gel is prepared by copolymerizing monomers consisting of (meth)acrylic acid, (meth)acrylamides or N-substituted (meth)acrylamides and monomers consisting of unsaturated carboxylic acid.
Claim 47
Independent Claim
61 words
The method according to claims 37 or 38, wherein said polymerizing step is carried out such that where the average polymer gel particle diameter of said polymer gel ranges from 0.1 μm to 100 μm, the standard deviation in the distribution of particle diameters in said polymer gel is at most 25% of the average particle diameter in the polymer gel.
Claim 48
Independent Claim
34 words
The method according to claims 37 or 38, wherein the width of the phase transition temperature of the polymer gel measured by DSC at a heating rate of 1° C./min is within 10° C.
References Cited (Backward Citations)
US2953546A
Cited
US3720534A
Cited
US4059552A
Cited
EP0037138A2
Cited
JPS58215413A
Cited
EP0122797A1
Cited
US4981625A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-02-02 | 1996-08-03 | 1997-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-02-02 | 2000-08-03 | 2001-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-02-02 | 2004-08-03 | 2005-02-02 | $7700.00 | Window Closed / Lapsed |