Method for forming a buried contact in a semiconductor device
Assignee: Motorola Solutions Inc
•
Filing: 1991-02-04
•
Granted: 1992-11-10
•
Expires: 2011-02-04
Abstract
Abstract A process for forming a buried contact (50) in a semiconductor device (20) which avoids etch damage to the substrate and forms a self-aligned, low resistance contact to a silicon substrate (22) is provided. After forming a contact opening (32) through overlying insulating and conducting layers (24, 28,30), a silicide region (40) is formed in the substrate at the contact surface (34) exposed by the contact opening (32). A refractory metal silicide which provides high etching selectivity to polysilicon is formed in the substrate at the contact surface (34) by either a blanket deposition of a refractory metal into the contact opening (32), or alternatively, by a selective deposition process using contact surface (34) as a nucleation site. In a preferred embodiment, a cobalt or tantalum silicide region (40) is formed in the substrate at the contact surface (34) and a conductive layer (42) is deposited and etched to form an interconnect (48) contacting the silicide region (40). The high etching selectivity obtainable between the conductive layer ( 42) and the silicide region (40) avoids damage to the substrate surface providing improved device performance.
Inventors
- 👤 David G. Kolar
- 👤 Robert E. Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:00
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
116 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first conductive layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first conductive layer, and the dielectric layer exposing a selected portion of the silicon substrate; forming a metal silicide in the selected portion of the substrate; removing the insulating layer; depositing a second conductive layer onto the first conductive layer and the metal silicide; and selectively etching the second conductive layer preferentially to the metal silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the metal silicide.
Claim 2
Independent Claim
116 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first conductive layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first conductive layer, and the dielectric layer exposing a selected portion of the silicon substrate; forming a metal silicide in the selected portion of the substrate; removing the insulating layer; depositing a second conductive layer onto the first conductive layer and the metal silicide; and selectively etching the second conductive layer preferentially to the metal silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the metal silicide.
Claim 3
Dependent Claim
48 words
The method of claim 1 wherein selectively etching the conductor comprises: forming a photoresist pattern on the conductor aligned to the selected portion of the substrate; and anisotropically etching the conductor using the photoresist pattern as an etch mask and the refractory metal silicide as an etch stop.
Claim 4
Dependent Claim
31 words
The method of claim 1 wherein forming a metal silicide comprises; selectively depositing a refractory metal on the selected surface portion; and annealing the substrate to form a refractory metal silicide.
Claim 5
Independent Claim
175 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first conductive layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first conductive layer, and the dielectric layer exposing a selected portion of the silicon substrate; depositing a layer of cobalt to overlie the substrate; annealing the substrate at a temperature of about 430° to 470°C. for about 10 to 60 seconds to react a portion of the cobalt layer with silicon in the exposed portion of the substrate to form cobalt silicide; etching away unreacted cobalt; performing a second anneal at a temperature of about 650° to 750° C. for about 10 to 60 seconds; removing the insulating layer; depositing a second conductive layer onto the first conductive layer and the cobalt silicide; and selectively etching the second conductive layer preferentially to the cobalt silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the cobalt silicide.
Claim 6
Independent Claim
175 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first conductive layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first conductive layer, and the dielectric layer exposing a selected portion of the silicon substrate; depositing a layer of cobalt to overlie the substrate; annealing the substrate at a temperature of about 430° to 470°C. for about 10 to 60 seconds to react a portion of the cobalt layer with silicon in the exposed portion of the substrate to form cobalt silicide; etching away unreacted cobalt; performing a second anneal at a temperature of about 650° to 750° C. for about 10 to 60 seconds; removing the insulating layer; depositing a second conductive layer onto the first conductive layer and the cobalt silicide; and selectively etching the second conductive layer preferentially to the cobalt silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the cobalt silicide.
Claim 7
Independent Claim
127 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first polysilicon layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first polysilicon layer, and the dielectric layer exposing a selected portion of the silicon substrate; forming a metal silicide selected from the group consisting of cobalt silicide and tantalum silicide in the selected portion of the substrate; removing the insulating layer; depositing a second polysilicon layer onto the first conductive layer and the metal silicide; and selectively etching the second polysilicon layer preferentially to the metal silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the metal silicide.
Claim 8
Independent Claim
127 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having a dielectric layer, a first polysilicon layer and an insulating layer formed sequentially thereon; forming an opening through the insulating layer, the first polysilicon layer, and the dielectric layer exposing a selected portion of the silicon substrate; forming a metal silicide selected from the group consisting of cobalt silicide and tantalum silicide in the selected portion of the substrate; removing the insulating layer; depositing a second polysilicon layer onto the first conductive layer and the metal silicide; and selectively etching the second polysilicon layer preferentially to the metal silicide to form a portion thereof making an electrical contact to the substrate and leaving exposed a portion of the metal silicide.
Claim 9
Independent Claim
176 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having principal surface; forming a dielectric layer on the principal surface; depositing a first silicon layer onto the dielectric layer; depositing an insulating layer onto the first silicon layer; sequentially etching the insulating layer, the first silicon layer and the dielectric layer to form an opening exposing a contact region on the principal surface; forming a sidewall spacer on the perimeter of the opening; forming a refractory metal silicide in the contact region; removing the insulating layer and the sidewall spacer; depositing a second silicon layer onto the first silicon layer and the refractory metal silicide; forming a photoresist mask overlying the second silicon layer aligned to the contact region; and anisotropically etching the second silicon layer and the first silicon layer using the photoresist mask as an etch mask and the refractory metal silicide as an etch stop to form an electrical contact to the substrate while leaving exposed a portion of the contact region at the principal surface.
Claim 10
Independent Claim
176 words
A method for forming a buried contact in a semiconductor device comprising: providing a silicon substrate having principal surface; forming a dielectric layer on the principal surface; depositing a first silicon layer onto the dielectric layer; depositing an insulating layer onto the first silicon layer; sequentially etching the insulating layer, the first silicon layer and the dielectric layer to form an opening exposing a contact region on the principal surface; forming a sidewall spacer on the perimeter of the opening; forming a refractory metal silicide in the contact region; removing the insulating layer and the sidewall spacer; depositing a second silicon layer onto the first silicon layer and the refractory metal silicide; forming a photoresist mask overlying the second silicon layer aligned to the contact region; and anisotropically etching the second silicon layer and the first silicon layer using the photoresist mask as an etch mask and the refractory metal silicide as an etch stop to form an electrical contact to the substrate while leaving exposed a portion of the contact region at the principal surface.
Claim 11
Dependent Claim
77 words
The method of claim 6 wherein forming a refractory metal silicide comprises: depositing a layer of cobalt onto the contact region; annealing the substrate at a temperature of about 430° to 470° C. for about 10 to 60 seconds to react a portion of the cobalt layer with silicon in the contact region; etching away unreacted cobalt; and performing a second anneal at a temperature of about 650° to 750° C. for about 10 to 60 seconds.
Claim 12
Dependent Claim
31 words
The method of claim 6 wherein forming a metal silicide comprises; selectively depositing a refractory metal on the selected surface portion; and annealing the substrate to form a refractory metal silicide.
References Cited (Backward Citations)
JPS5539674A
Cited
US4289574A
Cited
JPS57104241A
Cited
US4551908A
Cited
JPH01241125A
Cited
JPH0297016A
Cited
US4966864A
Cited
US4992394A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |