Process for patterning metal connections on a semiconductor structure by using an aluminum oxide etch resistant layer
Assignee: National Semiconductor Corp
•
Filing: 1980-06-09
•
Granted: 1981-09-15
•
Expires: 2000-06-09
Abstract
Abstract A process for patterning plasma etchable regions on a semiconductor structure includes the steps of forming a layer of an oxide of aluminum over the surface of the semiconductor structure, forming an overlying layer of plasma etchable material on the layer of oxide, and removing undesired portions of the overlying layer by plasma etching to thereby expose portions of the layer of oxide. In some embodiments of the invention the thereby exposed portions of the layer of oxide are then removed, together with any underlying portions of the first layer, by isotropic etching.
Inventors
- 👤 Steven J. Radigan
- 👤 Robert L. Berry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:34
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P76/00; H10P76/40; Y; Y10; Y10S; Y10S438/00; Y10S438/97
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
111 words
A process for protecting selected portions of a semiconductor structure from a plasma etching process, the process for protecting comprising: depositing a layer of aluminum over at least the selected portions of the semiconductor structure; forming a layer of aluminum oxide over at least those portions of the layer of aluminum overlying the selected portions, the layer of aluminum oxide being plasma etchable at a selected power level; and plasma etching the semiconductor structure at a power level less than the selected power level to thereby remove material from the semiconductor structure except where the layer of aluminum oxide protects the underlying semiconductor structure by substantially stopping the plasma etching process.
Claim 2
Dependent Claim
111 words
A process for protecting selected portions of a semiconductor structure from a plasma etching process, the process for protecting comprising: depositing a layer of aluminum over at least the selected portions of the semiconductor structure; forming a layer of aluminum oxide over at least those portions of the layer of aluminum overlying the selected portions, the layer of aluminum oxide being plasma etchable at a selected power level; and plasma etching the semiconductor structure at a power level less than the selected power level to thereby remove material from the semiconductor structure except where the layer of aluminum oxide protects the underlying semiconductor structure by substantially stopping the plasma etching process.
Claim 3
Dependent Claim
146 words
A process for patterning aluminum layers on a semiconductor structure comprising: depositing a first relatively thin layer of aluminum on the semiconductor structure; creating a layer of an oxide of aluminum on the first layer of aluminum, the layer of an oxide of aluminum being plasma etchable at a selected power level; depositing a second relatively thicker layer of aluminum on the layer of an oxide of aluminum; removing undesired portions of the second layer of aluminum by plasma etching the second layer of aluminum at a power level less than the selected power level, the plasma etching process being effectively stopped by the layer of an oxide of aluminum; and removing at least part of the thereby exposed layer of an oxide of aluminum and the first relatively thin layer of aluminum by an isotropic process to thereby expose regions of the underlying semiconductor structure.
Claim 4
Dependent Claim
146 words
A process for patterning aluminum layers on a semiconductor structure comprising: depositing a first relatively thin layer of aluminum on the semiconductor structure; creating a layer of an oxide of aluminum on the first layer of aluminum, the layer of an oxide of aluminum being plasma etchable at a selected power level; depositing a second relatively thicker layer of aluminum on the layer of an oxide of aluminum; removing undesired portions of the second layer of aluminum by plasma etching the second layer of aluminum at a power level less than the selected power level, the plasma etching process being effectively stopped by the layer of an oxide of aluminum; and removing at least part of the thereby exposed layer of an oxide of aluminum and the first relatively thin layer of aluminum by an isotropic process to thereby expose regions of the underlying semiconductor structure.
Claim 5
Dependent Claim
44 words
A process as in claim 2 wherein the step of removing undesired portions of the second layer of aluminum is preceded by a step of forming a coating resistant to plasma etching over all but the undesired portions of the second layer of aluminum.
Claim 6
Dependent Claim
11 words
A process as in claim 3 wherein the coating is photoresist.
Claim 7
Dependent Claim
19 words
A process as in claim 2 wherein the oxide of aluminum is aluminum oxide (Al 2 O 3 ).
Claim 8
Dependent Claim
31 words
A process as in claim 5 wherein the aluminum oxide is formed by heating the layer of aluminum to a temperature of 500° C. or less in an atmosphere containing oxygen.
Claim 9
Dependent Claim
18 words
A process as in claim 5 wherein the plasma etching is accomplished using an etch gas containing chlorine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |