Laser crystallized cladding layers for improved amorphous silicon light-emitting diodes and radiation sensors
Assignee: Xerox Corp
•
Filing: 1990-12-27
•
Granted: 1992-11-10
•
Expires: 2010-12-27
Abstract
Abstract Scanning laser crystallization of p- and n-type hydrogenated amorphous silicon alloy cladding layers enhances the doping efficiency of such layers without changing the luminescence or other important properties of the middle i-layer in a p-i-n device. The dc dark conductivity of the doped layers increases by a factor of about 100 to about 10,000 above a sharp laser energy density threshold whose magnitude increases with decreasing impurity concentration. In one method, a doped amorphous silicon alloy layer is deposited on an amorphous glass substrate, scanned with laser irradiation, and then an intermediate i-layer is formed over this layer. Another doped amorphous silicon alloy layer is deposited on this layer, doped oppositely from the first doped layer. The second doped layer is then crystallized by scanning laser irradiation, leaving the underlying i-layer virtually unchanged in optical and electronic properties.
Inventors
- 👤 Kris A. Winer
- 👤 Robert L. Thornton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:48
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/81; H10H20/817; H10H20/818; H10F; H10F10/00; H10F10/10; H10F10/17; H10F71/00; H10F71/10; H10F71/103; H10F71/131; H10F71/134; H10H20/01; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/548; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
189 words
A method of increasing the conductivity of p- and n-type hydrogenated amorphous silicon alloys in a p-i-n device without substantially affecting the luminescence of the intermediate i-type hydrogenated amorphous silicon layer, comprising: (a) forming a first hydrogenated amorphous silicon doped alloy layer on an amorphous substrate, the layer having a preselected concentration of dopant; (b) forming an intrinsic hydrogenated amorphous silicon layer over the layer of step (a); (c) forming a second hydrogenated amorphous silicon alloy layer doped opposite of the layer of step (a) over said intrinsic hydrogenated amorphous silicon layer, the second hydrogenated amorphous silicon alloy layer having a preselected concentration of dopant; (d) irradiating the layers formed from steps (a)-(c) with a scanning radiation source of predetermined wavelength; (e) adjusting the energy density of said radiation source so that the rate of crystallization of the layers formed in steps (a) and (c) is substantially greater than the rate of crystallization of the intrinsic layer formed in step (b); and (f) terminating said irradiating when said first and second hydrogenated amorphous silicon alloy layers are substantially crystallized and said intrinsic hydrogenated amorphous silicon layer is essentially amorphous.
Claim 2
Independent Claim
189 words
A method of increasing the conductivity of p- and n-type hydrogenated amorphous silicon alloys in a p-i-n device without substantially affecting the luminescence of the intermediate i-type hydrogenated amorphous silicon layer, comprising: (a) forming a first hydrogenated amorphous silicon doped alloy layer on an amorphous substrate, the layer having a preselected concentration of dopant; (b) forming an intrinsic hydrogenated amorphous silicon layer over the layer of step (a); (c) forming a second hydrogenated amorphous silicon alloy layer doped opposite of the layer of step (a) over said intrinsic hydrogenated amorphous silicon layer, the second hydrogenated amorphous silicon alloy layer having a preselected concentration of dopant; (d) irradiating the layers formed from steps (a)-(c) with a scanning radiation source of predetermined wavelength; (e) adjusting the energy density of said radiation source so that the rate of crystallization of the layers formed in steps (a) and (c) is substantially greater than the rate of crystallization of the intrinsic layer formed in step (b); and (f) terminating said irradiating when said first and second hydrogenated amorphous silicon alloy layers are substantially crystallized and said intrinsic hydrogenated amorphous silicon layer is essentially amorphous.
Claim 3
Dependent Claim
35 words
A method in accordance with claim 1 wherein the steps (a) and (c) forming comprises first forming the hydrogenated amorphous silicon alloy layer, then doping the hydrogenated amorphous silicon layer to a preselected dopant concentration.
Claim 4
Dependent Claim
40 words
A method in accordance with claim 1 wherein said (a) and (c) layer alloys are silicon alloyed with an element selected from the group consisting of carbon and germanium, said (a) and (c) layers being the same or different alloys.
Claim 5
Dependent Claim
24 words
A method in accordance with claim 1 wherein said (a) and (c) layer alloys have dopant concentrations at least about 0.04 percent mole fraction.
Claim 6
Dependent Claim
28 words
A method in accordance with claim 1 wherein said (a) and said (c) layer alloys have dopant concentrations ranging from about 0.04 to about 3 percent mole fraction.
Claim 7
Dependent Claim
44 words
A method in accordance with claim 1 wherein said scanning is performed at temperatures ranging from about 0° to about 100° C.; pressure of at most about 1×10 -5 Torr; and average energy densities ranging from about 50 to about 200 mJ/cm 2 .
Claim 8
Dependent Claim
45 words
A method in accordance with claim 1 wherein said scanning is performed at temperature ranging from about 20° C. to about 25° C.; pressure of at most about 1×10 -6 Torr; and average energy density ranging from about 75 to about 200 mJ/cm 2 .
Claim 9
Dependent Claim
51 words
A method in accordance with claim 6 wherein said conductivity exhibits an increase ranging from a factor of about 100 to about 10,000 times the conductivity of the layers formed in steps (a) and (c), said increase attained at a known energy density threshold which increases as said dopant concentration decreases.
Claim 10
Dependent Claim
51 words
A method in accordance with claim 6 wherein said conductivity exhibits an increase ranging from a factor of about 100 to about 1,000 times the conductivity of the layers formed in steps (a) and (c), said increase attained at a known energy density threshold which increases as said dopant concentration decreases.
Claim 11
Dependent Claim
14 words
A method in accordance with claim 6 wherein said radiation source is a laser.
Claim 12
Dependent Claim
14 words
A method in accordance with claim 7 wherein said radiation source is a laser.
Claim 13
Dependent Claim
58 words
A method in accordance with claim 10 wherein said laser is an excimer laser scanning at about 512 to about 2,560 pulses per point, frequency ranging from about 24 to about 40 Hz, said wavelength ranging from about 155 nm to about 350 nm, and having a pulse time ranging from about 10 ns to about 25 ns.
Claim 14
Independent Claim
146 words
A method of increasing the conductivity of p- and n-type hydrogenated amorphous silicon alloy regions in a p-i-n device comprising: (a) forming a hydrogenated amorphous silicon alloy n- or p-type region on an amorphous substrate; (b) irradiating said n- or p-type region with a scanning laser, thereby crystallizing said region to a known degree and increasing the conductivity of the n- or p- type layer; (c) forming an i-type hydrogenated amorphous silicon region having a predetermined luminescence over said n- or p-type region; (d) forming a p- or n-type hydrogenated amorphous silicon alloy region doped oppositely from that of step (a) over said i-type region; and (e) irradiating said region formed in step (d) with a scanning laser, thereby crystallizing the p- or n- type region to a known degree and increasing the conductivity of the p- or n-type layer without substantially affecting the i-type region.
Claim 15
Independent Claim
146 words
A method of increasing the conductivity of p- and n-type hydrogenated amorphous silicon alloy regions in a p-i-n device comprising: (a) forming a hydrogenated amorphous silicon alloy n- or p-type region on an amorphous substrate; (b) irradiating said n- or p-type region with a scanning laser, thereby crystallizing said region to a known degree and increasing the conductivity of the n- or p- type layer; (c) forming an i-type hydrogenated amorphous silicon region having a predetermined luminescence over said n- or p-type region; (d) forming a p- or n-type hydrogenated amorphous silicon alloy region doped oppositely from that of step (a) over said i-type region; and (e) irradiating said region formed in step (d) with a scanning laser, thereby crystallizing the p- or n- type region to a known degree and increasing the conductivity of the p- or n-type layer without substantially affecting the i-type region.
Claim 16
Dependent Claim
35 words
A method in accordance with claim 13 wherein the steps (a) and (d) forming comprises first forming the hydrogenated amorphous silicon alloy layer, then doping the hydrogenated amorphous silicon layer to a preselected dopant concentration.
Claim 17
Dependent Claim
32 words
A method in accordance with claim 13 wherein said alloys are silicon alloyed with an element selected from the group consisting of carbon and germanium, said alloys being the same or different.
Claim 18
Dependent Claim
24 words
A method in accordance with claim 13 wherein said (a) and (d) layer alloys have dopant concentrations at least about 0.04 percent mole fraction.
Claim 19
Dependent Claim
27 words
A method in accordance with claim 13 wherein said (a) and (d) layer alloys have dopant concentrations ranging from about 0.04 to about 3 percent mole fraction.
Claim 20
Dependent Claim
43 words
A method in accordance with claim 13 wherein said scanning is performed at temperatures ranging from about 0° to about 100° C.; pressure at most about 1×10 -5 Torr; and average energy densities ranging from about 50 to about 200 mJ/cm 2 .
Claim 21
Dependent Claim
44 words
A method in accordance with claim 13 wherein said scanning is performed at temperature ranging from about 20° C. to about 25° C.; pressure at most about 1×10 -6 Torr; and average energy density ranging from about 75 to about 200 mJ/cm 2 .
Claim 22
Dependent Claim
52 words
A method in accordance with claim 18 wherein said conductivity exhibits an increase ranging from a factor of about 100 to about 10,000 times that of the conductivity of the layers formed in steps (a) and (d), said increase attained at known energy density threshold which increases as said dopant concentration decreases.
Claim 23
Dependent Claim
52 words
A method in accordance with claim 18 wherein said conductivity exhibits on increase ranging from a factor of about 100 to about 1,000 times that of the conductivity of the layers formed in steps (a) and (d), said increase attained at known energy density threshold which increases as said dopant concentration decreases.
Claim 24
Dependent Claim
57 words
A method in accordance with claim 13 wherein said laser is an excimer laser scanning at about 512 to about 2,560 pulses per point, frequency ranging from about 24 to about 40 Hz, wavelength ranging from about 155 nm to about 350 nm, and having a pulse time ranging from about 10 ns to about 25 ns.
Claim 25
Independent Claim
123 words
A method of increasing the conductivity and mobility of p- and n-type hydrogenated amorphous silicon alloy regions in a p-i-n device comprising: (a) forming a hydrogenated amorphous silicon alloy n- or p-type region on a transparent amorphous substrate; (b) forming a hydrogenated amorphous silicon i-type region having a predetermined luminescence over said n- or p-type region; (c) forming a hydrogenated amorphous silicon alloy region doped opposite of the layer formed in step (a) over said i-type region; and (d) irradiating both of said n- and p-type hydrogenated amorphous silicon alloy regions with a scanning laser, thereby crystallizing the n- and p- type regions to a known degree and increasing the conductivity of said p- and n-type layers without substantially affecting the i-type region.
Claim 26
Independent Claim
123 words
A method of increasing the conductivity and mobility of p- and n-type hydrogenated amorphous silicon alloy regions in a p-i-n device comprising: (a) forming a hydrogenated amorphous silicon alloy n- or p-type region on a transparent amorphous substrate; (b) forming a hydrogenated amorphous silicon i-type region having a predetermined luminescence over said n- or p-type region; (c) forming a hydrogenated amorphous silicon alloy region doped opposite of the layer formed in step (a) over said i-type region; and (d) irradiating both of said n- and p-type hydrogenated amorphous silicon alloy regions with a scanning laser, thereby crystallizing the n- and p- type regions to a known degree and increasing the conductivity of said p- and n-type layers without substantially affecting the i-type region.
Claim 27
Dependent Claim
35 words
A method in accordance with claim 23 wherein the steps (a) and (c) forming comprises first forming the hydrogenated amorphous silicon alloy layer, then doping the hydrogenated amorphous silicon layer to a preselected dopant concentration.
Claim 28
Dependent Claim
49 words
A method in accordance with claim 23 wherein said scanning of the region formed in step (a) is through said transparent substrate while said scanning of the region formed in step (c) is from a direction substantially opposite that of the scanning of the region formed in step (a).
Claim 29
Dependent Claim
37 words
A method in accordance with claim 23 wherein said n- and p-doped alloys comprise alloys of silicon and an element selected from the group consisting of germanium and carbon, said layers being the same or different alloys.
Claim 30
Dependent Claim
24 words
A method in accordance with claim 23 wherein said (a) and (c) layer alloys have dopant concentrations at least about 0.04 percent mole fraction.
Claim 31
Dependent Claim
27 words
A method in accordance with claim 23 wherein said (a) and (c) layer alloys have dopant concentrations ranging from about 0.04 to about 3 percent mole fraction.
Claim 32
Dependent Claim
43 words
A method in accordance with claim 23 wherein said scanning is performed at temperatures ranging from about 0 to about 100° C.; pressure at most about 1×10 -5 Torr; and average energy densities ranging from about 50 to about 200 mJ/cm 2 .
Claim 33
Dependent Claim
44 words
A method in accordance with claim 23 wherein said scanning is performed at temperature ranging from about 20° C. to about 25° C.; pressure at most about 1×10 -6 Torr; and average energy density ranging from about 75 to about 200 mJ/cm 2 .
Claim 34
Dependent Claim
50 words
A method in accordance with claim 29 wherein said conductivity exhibits on increase ranging from a factor of about 100 to about 10,000 times the conductivity of the layers formed in steps (a) and (c), said increase attained at known energy density threshold which increases as said dopant concentration decreases.
Claim 35
Dependent Claim
50 words
A method in accordance with claim 29 wherein said conductivity exhibits on increase ranging from a factor of about 100 to about 1,000 times the conductivity of the layers formed in steps (a) and (c), said increase attained at known energy density threshold which increases as said dopant concentration decreases.
Claim 36
Dependent Claim
57 words
A method in accordance with claim 23 wherein said laser is an excimer laser scanning at about 512 to about 2,560 pulses per point, frequency ranging from about 24 to about 40 Hz, wavelength ranging from about 155 nm to about 350 nm, and having a pulse time ranging from about 10 ns to about 25 ns.
References Cited (Backward Citations)
US4609407A
Cited
JPS5961138A
Cited
US4525375A
Cited
US4528082A
Cited
US4624862A
Cited
JPS61160979A
Cited
US4910153A
Cited
US4718947A
Cited
US4845043A
Cited
US4891330A
Cited
JPS6441278A
Cited
JPH02122574A
Cited
US5055416A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |