US5156934A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a rechargable modified manganese dioxide material and related compound and electrode material
Assignee: RBC UNIVERSAL Ltd A CORP OF NEVADA Corp
•
Filing: 1991-02-11
•
Granted: 1992-10-20
•
Expires: 2011-02-11
Abstract
Abstract A method of making a rechargeable modified manganese dioxide material for use as battery electrode is disclosed. The method includes mixing manganese dioxide with an aqueous solution of a water soluble salt component selected from the group consisting of bismuth nitrate, lead acetate, lead nitrate, copper sulfate, copper nitrate, copper chloride and mixtures thereof. An alkaline hydroxide solution is then added to establish precipitation of resultant product. The resultant product is washed, filtered and dried to obtain the modified manganese dioxide material. The material is combined with a suitable conducting reinforcement component and a binder to form a high density, low resistivity electrode material.
Inventors
- 👤 Ramesh C. Kainthia
- 👤 David J. Manko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:58
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/24; C; C01; C01G; C01G45/00; C01G45/02; C01G45/024; C01G45/12; C01G45/1221; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/50; H01M4/62; H01M4/624; C01P; C01P2004/00; C01P2004/80; C01P2004/82; C01P2006/00; C01P2006/10; C01P2006/11; C01P2006/40; H01M4/625; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
66 words
A method of making a rechargeable, modified manganese dioxide electrode material, comprising mixing manganese dioxide with an aqueous solution of a water soluble salt component to establish MnO 2 particles suspended in a first solution, and admixing with said first solution, a second solution which is an aqueous solution of an alkaline hydroxide to establish precipitation of a resultant product which coats said MnO 2 particles.
Claim 2
Independent Claim
66 words
A method of making a rechargeable, modified manganese dioxide electrode material, comprising mixing manganese dioxide with an aqueous solution of a water soluble salt component to establish MnO 2 particles suspended in a first solution, and admixing with said first solution, a second solution which is an aqueous solution of an alkaline hydroxide to establish precipitation of a resultant product which coats said MnO 2 particles.
Claim 3
Dependent Claim
32 words
The method of claim 1 including selecting said water soluble salt component from the group consisting of bismuth nitrate, lead acetate, lead nitrate, copper sulfate, copper nitrate, copper chloride and mixtures thereof.
Claim 4
Dependent Claim
24 words
The method of claim 2 including selecting said alkaline hydroxide for said second solution from the group consisting of potassium hydroxide and sodium hydroxide.
Claim 5
Dependent Claim
25 words
The method of claim 3 also including washing, filtering and drying said resultant product including said coated particles to obtain said modified manganese dioxide material.
Claim 6
Dependent Claim
14 words
The method of claim 1 including mixing electrolytic manganese dioxide with said first solution.
Claim 7
Dependent Claim
14 words
The method of claim 1 including mixing chemical manganese dioxide with said first solution.
Claim 8
Dependent Claim
22 words
The method of claim 3 including continuously stirring said first solution while said second solution is being added during said admixing stage.
Claim 9
Dependent Claim
48 words
The method of claim 3 including selecting bismuth nitrate as said water soluble salt component and establishing said first solution by dissolving said bismuth nitrate in a solution of nitric acid, and adding said bismuth nitrate dissolved in nitric acid to distilled water and adding manganese dioxide thereto.
Claim 10
Dependent Claim
60 words
The method of claim 8 including establishing said first solution by dissolving about 5 to 35 grams of bismuth nitrate in about 5 to 35 milliliters of concentrated nitric acid, and adding to said bismuth nitrate dissolved in said nitric acid about 250 to 1000 milliliters of distilled water, and adding about 30 to 60 grams of MnO 2 .
Claim 11
Dependent Claim
37 words
The method of claim 9 including selecting as said second solution an aqueous solution of potassium hydroxide, and filtering said resultant product to obtain a modified manganese dioxide material of the formula MnO 2 .Bi(OH) 3 .
Claim 12
Dependent Claim
24 words
The method of claim 10 including dissolving about 20 to 40 milliliters of potassium hydroxide in about 75 to 150 milliliters of distilled water.
Claim 13
Dependent Claim
15 words
The method of claim 3 including selecting lead nitrate as said water soluble salt component.
Claim 14
Dependent Claim
23 words
The method of claim 12 including establishing said first solution by dissolving said lead nitrate in distilled water, and adding manganese dioxide thereto.
Claim 15
Dependent Claim
51 words
The method of claim 13 including establishing said first solution by dissolving about 15 to 20 grams of lead nitrate in about 80 to 125 milliliters of distilled water, and adding an additional 400 to 600 milliliters of water, and adding thereto about 40 to 50 grams of MnO 2 .
Claim 16
Dependent Claim
37 words
The method of claim 14 including selecting as said second solution an aqueous solution of potassium hydroxide and filtering said resultant product to obtain a modified manganese dioxide compound of the formula MnO 2 .Pb(OH) 2 .
Claim 17
Dependent Claim
24 words
The method of claim 15 including dissolving about 2 to 5 grams of potassium hydroxide in about 80 to 125 milliliters of distilled water.
Claim 18
Dependent Claim
57 words
The method of claim 4 including the further steps of mixing said modified manganese dioxide material with an electrically conducting reinforcement component, ball milling the mixture for enhancing the efficiency of mixing, adding a binder to said mixture, and ball milling said mixture including said binder for an additional predetermined time period to create a cathode mix.
Claim 19
Dependent Claim
44 words
The method of claim 17 including mixing about 15 to 80 percent by weight of said modified manganese dioxide material with about 15 to 80 percent by weight of said conducting reinforcement component and about 2 to 10 percent by weight of said binder.
Claim 20
Dependent Claim
33 words
The method of claim 18 including mixing about 50 to 80 percent by weight of said modified manganese dioxide material with about 15 to 45 percent by weight of said conducting reinforcement component.
Claim 21
Dependent Claim
23 words
The method of claim 18 including selecting said conducting reinforcement component from the group consisting of graphite, acetylene black, metal powder and fiber.
Claim 22
Dependent Claim
32 words
The method of claim 20 including employing metal powder as said conducting reinforcement component, and selecting said metal powder from the group consisting of nickel, nickel plated iron and nickel plated copper.
Claim 23
Dependent Claim
11 words
The method of claim 21 including providing tetrafluoroethylene as said binder.
Claim 24
Dependent Claim
30 words
A rechargeable, modified manganese dioxide material, comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof.
Claim 25
Dependent Claim
30 words
A rechargeable, modified manganese dioxide material, comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof.
Claim 26
Dependent Claim
26 words
The modified manganese dioxide material of claim 23 wherein said selected metal is bismuth and wherein said material has the formula MnO 2 .Bi(OH) 3 .
Claim 27
Dependent Claim
26 words
The modified manganese dioxide material of claim 23 wherein said selected metal is lead such that said material has the formula MnO 2 .Pb(OH) 2 .
Claim 28
Dependent Claim
33 words
The modified manganese dioxide material of claim 23 wherein said selected metal is a mixture of lead and bismuth such that said material has the formula MnO 2 .Pb(OH) 2 .Bi(OH) 3 .
Claim 29
Dependent Claim
54 words
A modified manganese dioxide electrode material comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof, an electrically conducting reinforcement component selected from the group consisting of graphite, acetylene black, metal powder and fiber, and a binder bonding said mixture.
Claim 30
Dependent Claim
54 words
A modified manganese dioxide electrode material comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof, an electrically conducting reinforcement component selected from the group consisting of graphite, acetylene black, metal powder and fiber, and a binder bonding said mixture.
Claim 31
Dependent Claim
14 words
The modified manganese dioxide electrode material of claim 27 wherein said binder is tetrafluoroethylene.
Claim 32
Dependent Claim
28 words
The modified manganese dioxide electrode material of claim 28 wherein said metal powder is selected from the group consisting of nickel, nickel plated iron, and nickel plated copper.
Claim 33
Dependent Claim
29 words
The modified manganese dioxide electrode material of claim 29 wherein said material has a pressed density at about 15,000 psi, of between about 3.0 and 3.4 gm/cm 3 .
Claim 34
Dependent Claim
25 words
The modified manganese dioxide electrode material of claim 30 wherein said material has an electrical resistivity of between about 2×10 3 and 5×10 3 ohm-cm.
Claim 35
Dependent Claim
30 words
The modified manganese dioxide electrode material of claim 31 wherein said material has a cycling capacity of about 70 percent of the theoretical two-electron capacity for at least 500 cycles.
Claim 36
Dependent Claim
32 words
The modified manganese dioxide electrode material of claim 31 wherein said material has a cycling capacity of at least about 55 percent of the theoretical two-electron capacity for at least 900 cycles.
Claim 37
Dependent Claim
33 words
The modified manganese dioxide electrode material of claim 32 wherein said material includes graphite as said conducting reinforcement component, and said material has a volume capacity of about 420 ampere-hours/liter to 1.0 volt.
Claim 38
Dependent Claim
106 words
A rechargeable battery cell comprising a battery housing, a positive electrode composed of a modified manganese dioxide material comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof, and said positive electrode also including an electrically conducting reinforcement component and a binder, a negative electrode disposed within said housing in spaced relationship to said positive electrode, a separator disposed between said positive and said negative electrode, an electrolyte contained within said housing in contact with said positive and negative electrode, and means for electrically connecting said positive electrode and said negative electrode.
Claim 39
Dependent Claim
106 words
A rechargeable battery cell comprising a battery housing, a positive electrode composed of a modified manganese dioxide material comprising manganese dioxide coated with a metal hydroxide wherein said metal is selected from the group consisting of bismuth, lead, copper and mixtures thereof, and said positive electrode also including an electrically conducting reinforcement component and a binder, a negative electrode disposed within said housing in spaced relationship to said positive electrode, a separator disposed between said positive and said negative electrode, an electrolyte contained within said housing in contact with said positive and negative electrode, and means for electrically connecting said positive electrode and said negative electrode.
Claim 40
Dependent Claim
26 words
The battery cell of claim 35 wherein said positive electrode includes a material having the formula MnO 2 .Bi(OH) 3 as said modified manganese dioxide material.
Claim 41
Dependent Claim
26 words
The battery cell of claim 35 wherein said positive electrode includes a material having the formula MnO 2 .Pb(OH) 2 as said modified manganese dioxide material.
Claim 42
Dependent Claim
23 words
The battery cell of claim 35 wherein said positive electrode includes a material having the formula MnO 2 .Pb(OH) 2 .Bi(OH) 3 .
References Cited (Backward Citations)
US1293463A
Cited
US3535217A
Cited
US3533740A
Cited
US3773916A
Cited
US4042586A
Cited
US3948684A
Cited
US4006217A
Cited
US4048027A
Cited
US4133856A
Cited
US4170527A
Cited
US4269691A
Cited
US4277360A
Cited
US4295943A
Cited
US4362791A
Cited
US4405699A
Cited
US4476104A
Cited
EP0138316A1
Cited
US4451543A
Cited
US4520005A
Cited
US4728586A
Cited
US4863817A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-20 | 1996-04-20 | 1996-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-20 | 2000-04-20 | 2000-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-20 | 2004-04-20 | 2004-10-20 | $7700.00 | Window Closed / Lapsed |