Abstract This specification is directed to a method of making a compound selected from the group consisting of birnessite compounds of the formula Bi x Mn y O 2y+1 .5x.zH 2 O, wherein the y/x ratio is in a range of from about 7 to about 18 and the z/y ratio is in a range of from about 0.5 to about 0.6, Pb x Mn y O 2y+x .zH 2 O, wherein the y/x ratio is in a range of from about 6 to about 10 and the z/y ratio is in a range of from about 0.5 to about 0.6, and manganese oxide compounds containing both of these compounds. The method is characterized by the following steps. A solution is formed by mixing Mn(NO 3 ) 2 with a nitrate of bismuth or lead or mixtures thereof. The solution is maintained at a relatively constant temperature and NaOH is added to the solution, whereby Mn(OH) 2 and a hydroxide of bismuth or lead or mixtures thereof form a suspension. While the suspension is being agitated, oxygen is passed through the suspension, whereby the Mn(OH) 2 and the hydroxide of bismuth or lead or mixtures thereof can react to form a compound. The suspension is filtered to recover the birnessite compound. Thereafter, the compound is washed with water and dried.
A method of making a compound selected from the group consisting of birnessite compounds of the formula Bi x Mn y O 2y+1 .5x.zH 2 O, wherein the y/x ratio is in a range of from about 7 to about 18 and the z/y ratio is in a range of from about 0.5 to about 0.6, Pb x Mn y O 2y+x .zH 2 O, wherein the y/x ratio is in a range of from about 6 to about 10 and the z/y ratio is in a range of from about 0.5 to about 0.6, and manganese oxide compounds containing both of these compounds, characterized by the steps of: forming a solution by mixing Mn(NO 3 ) 2 with a nitrate of bismith or lead or mixtures thereof; maintaining said solution at a relatively constant temperature; adding NaOH to said solution, whereby Mn(OH) 2 and a hydroxide of bismuth or lead or mixtures thereof form a suspension; agitating said suspension; passing oxygen through said suspension while said suspension is being agitated, whereby said Mn(OH) 2 and said hydroxide of bismuth or lead or mixtures thereof can react to form a compound selected from the group consisting of birnessite compounds of the formula Bi x Mn y O 2y+1 .5x.zH 2 O, wherein the y/x ratio is in a range of from about 7 to about 18 and the z/y ratio is in a range of from about 0.5 to about 0.6, Pb x Mn y O 2y+x .zH 2 O, wherein the y/x ratio is in a range of from about 6 to about 10 and the z/y ratio is in a range of from about 0.5 to about 0.6, and manganese oxide compounds containing both of these compounds; filtering said suspension to recover said birnessite compound; washing said recovered birnessite compound with water; and drying said washed birnessite compound.
Claim 2
Independent Claim
310 words
A method of making a compound selected from the group consisting of birnessite compounds of the formula Bi x Mn y O 2y+1 .5x.zH 2 O, wherein the y/x ratio is in a range of from about 7 to about 18 and the z/y ratio is in a range of from about 0.5 to about 0.6, Pb x Mn y O 2y+x .zH 2 O, wherein the y/x ratio is in a range of from about 6 to about 10 and the z/y ratio is in a range of from about 0.5 to about 0.6, and manganese oxide compounds containing both of these compounds, characterized by the steps of: forming a solution by mixing Mn(NO 3 ) 2 with a nitrate of bismith or lead or mixtures thereof; maintaining said solution at a relatively constant temperature; adding NaOH to said solution, whereby Mn(OH) 2 and a hydroxide of bismuth or lead or mixtures thereof form a suspension; agitating said suspension; passing oxygen through said suspension while said suspension is being agitated, whereby said Mn(OH) 2 and said hydroxide of bismuth or lead or mixtures thereof can react to form a compound selected from the group consisting of birnessite compounds of the formula Bi x Mn y O 2y+1 .5x.zH 2 O, wherein the y/x ratio is in a range of from about 7 to about 18 and the z/y ratio is in a range of from about 0.5 to about 0.6, Pb x Mn y O 2y+x .zH 2 O, wherein the y/x ratio is in a range of from about 6 to about 10 and the z/y ratio is in a range of from about 0.5 to about 0.6, and manganese oxide compounds containing both of these compounds; filtering said suspension to recover said birnessite compound; washing said recovered birnessite compound with water; and drying said washed birnessite compound.
Claim 3
Dependent Claim
19 words
The method of claim 1, wherein said filtered birnessite compound is washed with a dilute acid before being dried.