Steel plate with organic coating having improved corrosion resistance
Assignee: JFE Steel Corp
•
Filing: 1991-11-07
•
Granted: 1992-09-15
•
Expires: 2011-11-07
Abstract
Abstract The improved corrosion-resistant steel plate with an organic coating comprises a steel plate having a zinc or zinc alloy plate layer which is overlaid with a chromate film which in turn is coated with an organic resin paint film. The organic resin coat comprises an epoxy resin having a dialkanolamine incorporated into its bisphenol A skeleton, an amino resin, and silica. The dialkanolamine combines with the amino resin to provide satisfactory curability at low temperatures; at the same time, it combines with the silica to provide a satisfactory film reinforcing effect. The organic coat formed of this composition can be effectively cured at low temperatures and yet it will neither dissolve nor soften upon swelling under the action of the alkali that is generated during cationic electrodeposition at the interface between the electrodeposited film and the organic coat. Thus, the organic coat has good paint adhesion, high corrosion resistance, as well as good workability and weldability and makes the steel plate suitable for use as an automotive part after painting. If the proportion of trivalent chromium in the chromate film and the amounts of zinc oxide and silica sol to be incorporated as additives are properly adjusted, the organic coating will exhibit satisfactory resistance to chromium dissolution and hence its paint adhesion and corrosion resistance are further improved to make the steel plate more suitable for use as an automotive part after painting.
Inventors
- 👤 Hideo Ogishi
- 👤 Shigeru Umino
- 👤 Kenji Takao
- 👤 Hajime Kimura
- 👤 Koji Yamato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:14
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/16; C; C23; C23C; C23C28/00; C09; C09D; C09D163/00; C23C22/00; C23C22/82; C23C22/83; C23C2222/00; C23C2222/20; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12556; Y10T428/12569; Y10T428/12611; Y10T428/12618; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12799
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
119 words
A steel plate with an organic coating having improved corrosion resistance comprising a zinc or zinc alloy plated steel plate having on its surface a chromate film deposited in an amount of 5-500 mg/m 2 in terms of metallic chromium, said chromate film being overlaid with a solid film adhered in an amount of 0.1-4.0 g/m 2 and formed of a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8-1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 5-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight of silica.
Claim 2
Dependent Claim
119 words
A steel plate with an organic coating having improved corrosion resistance comprising a zinc or zinc alloy plated steel plate having on its surface a chromate film deposited in an amount of 5-500 mg/m 2 in terms of metallic chromium, said chromate film being overlaid with a solid film adhered in an amount of 0.1-4.0 g/m 2 and formed of a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8-1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 5-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight of silica.
Claim 3
Dependent Claim
14 words
A steel plate according to claim 1 wherein said amino resin is benzoguanamine resin.
Claim 4
Dependent Claim
25 words
A steel plate according to claim 1 wherein said chromate film is present in an amount of 10-200 mg/m 2 in terms of metallic chromium.
Claim 5
Dependent Claim
32 words
A steel plate according to claim 1 wherein said silane coupling agent is incorporated in an amount of 1-5 parts by weight per 100 parts by weight of said modified epoxy resin.
Claim 6
Dependent Claim
31 words
A steel plate according to claim 1 wherein said amino resin is incorporated in an amount of 10-40 parts by weight per 100 parts by weight of said modified epoxy resin.
Claim 7
Dependent Claim
21 words
A steel plate according to claim 1 wherein said solid film is present in an amount of 0.3-2.0 g/m 2 .
Claim 8
Dependent Claim
25 words
A steel plate according to claim 1 wherein said dialkanolamine is at least one member selected from the group consisting of diethanolamine, dipropanolamine and dibutanolamine.
Claim 9
Dependent Claim
77 words
A steel plate according to claim 1 wherein said silane coupling agent is represented by the following general formula (I): X.sub.4-n Si - (OR).sub.n (I) wherein is an integer of 1-3; X is at least one functional group selected from the group consisting of a vinyl group, a mercapto group, an epoxy group and a chloride group; and OR is at least one group selected from the group consisting of a methoxy group and an ethoxy group.
Claim 10
Dependent Claim
179 words
A steel place with an organic coating having improved corrosion resistance comprising a steel plate at least one side of which is plated with zinc or a zinc alloy and thereafter coated with a chromium solution that is adhered in an amount of 5-500 mg/m 2 in terms of metallic chromium, has a molar ratio of trivalent chromium to total chromuium (Cr 3+ /T-Cr) in the range of 0.05-0.7 and contains zinc oxide in such an amount that the molar ratio of total chromium to zinc oxide (T-Cr/ZnO) is in the range of 4-25, the applied chromate solution having a baked solid film overlay present in an amount of 0.1-4.0 g/m 2 and comprising a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8 to 1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 500-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight on a solids base of silica.
Claim 11
Dependent Claim
179 words
A steel place with an organic coating having improved corrosion resistance comprising a steel plate at least one side of which is plated with zinc or a zinc alloy and thereafter coated with a chromium solution that is adhered in an amount of 5-500 mg/m 2 in terms of metallic chromium, has a molar ratio of trivalent chromium to total chromuium (Cr 3+ /T-Cr) in the range of 0.05-0.7 and contains zinc oxide in such an amount that the molar ratio of total chromium to zinc oxide (T-Cr/ZnO) is in the range of 4-25, the applied chromate solution having a baked solid film overlay present in an amount of 0.1-4.0 g/m 2 and comprising a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8 to 1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 500-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight on a solids base of silica.
Claim 12
Dependent Claim
190 words
A steel plate with an organic coating having improved corrosion resistance comprising a steel plate at least one side of which is plated with zinc or a zinc alloy and thereafter coated with a chromate solution that is adhered in an amount of 5-500 mg/m 2 in terms of metallic chromium, has a molar ratio of trivalent chromium to total chromuium (Cr 3+ /T-Cr) in the range of 0.05-0.7 and contains zinc oxide in such an amount that the molar ratio of total chromium to zinc oxide (T-Cr/ZnO) is in the range of 4-25, and contains a silica sol in an amount of 50-300% of total chromium, the applied chromate solution having a baked solid film overlay present in an amount of 0.1-4.0 g/m 2 and comprising a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8-1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 500-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight on a solids basis of silica.
Claim 13
Dependent Claim
190 words
A steel plate with an organic coating having improved corrosion resistance comprising a steel plate at least one side of which is plated with zinc or a zinc alloy and thereafter coated with a chromate solution that is adhered in an amount of 5-500 mg/m 2 in terms of metallic chromium, has a molar ratio of trivalent chromium to total chromuium (Cr 3+ /T-Cr) in the range of 0.05-0.7 and contains zinc oxide in such an amount that the molar ratio of total chromium to zinc oxide (T-Cr/ZnO) is in the range of 4-25, and contains a silica sol in an amount of 50-300% of total chromium, the applied chromate solution having a baked solid film overlay present in an amount of 0.1-4.0 g/m 2 and comprising a paint composition consisting of 100 parts by weight of a modified epoxy resin having 0.8-1.0 mole of a dialkanolamine per equivalent of epoxy groups in an epichlorohydrin-bisphenol A epoxy resin having 500-5,000 epoxy equivalents, 0.5-10 parts by weight of a silane coupling agent, 5-70 parts by weight of an amino resin, and 10-150 parts by weight on a solids basis of silica.
Claim 14
Dependent Claim
24 words
A steel plate according to claim 9 or 10 wherein said chromate solution comprises deposit of 10-200 mg/m 2 in terms of metallic chromium.
Claim 15
Dependent Claim
34 words
A steel plate according to claim 9 or 10 wherein said silane coupling agent is incorporated in an amount of 1-5 parts by weight per 100 parts by weight of said modified epoxy resin.
Claim 16
Dependent Claim
33 words
A steel plate according to claim 9 or 10 wherein said amino resin is incorporated in an amount of 10-40 parts by weight per 100 parts by weight of said modified epoxy resin.
Claim 17
Dependent Claim
23 words
A steel plate according to claim 9 or 10 wherein said solid film is present in an amount of 0.3-2.0 g/m 2 .
Claim 18
Dependent Claim
27 words
A steel plate according to claim 9 or 10 wherein said dialkanolamine is at least one member selected from the group consisting of diethanolamine, dipropanolamine and dibutanolamine.
Claim 19
Dependent Claim
80 words
A steel plate according to claim 9 or 10 wherein said silane coupling agent is represented by the following general formula (I): X.sub.4-n Si - (OR).sub.n (I) where n is an integer of 1-3; X is at least one functional group selected from the group consisting of a vinyl group, a mercapto group, an epoxy group and a chloride group; and OR is at least one group selected from the group consisting of a methoxy group and an ethoxy group.
Claim 20
Dependent Claim
38 words
A steel plate according to claim 9 or 10 wherein said amino resin is at least one member selected from the group consisting of a benzoguanamine resin, a melamine resin and the polycondensation product of urea and formaldehyde.
References Cited (Backward Citations)
EP0017232A1
Cited
DE3151115A1
Cited
US4411964A
Cited
DE3432118A1
Cited
US4659394A
Cited
EP0172624A1
Cited
FR2604729A1
Cited
US4775600A
Cited
US4889775A
Cited
JPS6418033A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-15 | 1996-03-16 | 1996-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-15 | 2000-03-16 | 2000-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-15 | 2004-03-16 | 2004-09-15 | $7700.00 | Window Closed / Lapsed |