Composite coating steel sheets having good corrosion resistance paintability and corrosion resistance after paint coating
Assignee: JFE Engineering Corp
•
Filing: 1981-12-17
•
Granted: 1983-10-25
•
Expires: 2001-12-17
Abstract
Abstract A composite coating steel sheet is disclosed which has good corrosion resistance, paintability and corrosion resistance after paint coating. The steel sheet comprises a plated base steel sheet, such as a galvanized, zinc alloy plated or aluminum plated steel sheet, and a chromate film formed on the plated base steel sheet. A composite silicate resin film is formed on the chromate film. The composite silicate film is composed of a reaction product of a colloidal silica, an organic resin and a silane compound.
Inventors
- 👤 Tomihiro Hara
- 👤 Masahiro Ogawa
- 👤 Masakazu Tsukada
- 👤 Masaaki Yamashita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 05:18
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C23; C23C; C23C22/00; C23C22/82; C23C22/83; C23C2222/00; C23C2222/20; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/928; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12556; Y10T428/12569; Y10T428/12583; Y10T428/1259; Y10T428/12611; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
63 words
A composite coating steel sheet having good corrosion resistance, paintability and corrosion resistance after point coating, which consisting essentially of a plated base steel sheet, a chromate film formed on the surface of the plated base steel sheet and a composite silicate resin film formed on the chromate film and consisting essentially of a colloidal silica, an organic resin and a silane compound.
Claim 2
Dependent Claim
63 words
A composite coating steel sheet having good corrosion resistance, paintability and corrosion resistance after point coating, which consisting essentially of a plated base steel sheet, a chromate film formed on the surface of the plated base steel sheet and a composite silicate resin film formed on the chromate film and consisting essentially of a colloidal silica, an organic resin and a silane compound.
Claim 3
Dependent Claim
20 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is a galvanized steel sheet.
Claim 4
Dependent Claim
22 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is a zinc-iron alloy plated steel sheet.
Claim 5
Dependent Claim
30 words
The steel sheet as claimed in claim 3, in which the zinc-iron alloy layer of said zinc-iron alloy plated steel sheet contains from 5 to 50% by weight of iron.
Claim 6
Dependent Claim
30 words
The steel sheet as claimed in claim 3, in which the zinc-iron alloy layer of said zinc-iron alloy plated steel sheet contains from 10 to 30% by weight of iron.
Claim 7
Dependent Claim
22 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is a zinc-nickel alloy plated steel sheet.
Claim 8
Dependent Claim
30 words
The steel sheet as claimed in claim 6, in which the zinc-nickel alloy layer of said zinc-nickel alloy plated steel sheet contains from 5 to 20% by weight of nickel.
Claim 9
Dependent Claim
30 words
The steel sheet as claimed in claim 6, in which the zinc-nickel alloy layer of said zinc-nickel alloy plated steel sheet contains from 12 to 13% by weight of nickel.
Claim 10
Dependent Claim
22 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is a zinc-manganese alloy plated steel sheet.
Claim 11
Dependent Claim
21 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is an aluminum plated steel sheet.
Claim 12
Dependent Claim
47 words
The steel sheet as claimed in claim 1, in which said plated base steel sheet is a multi-layer plated steel sheet having at least two layers selected from a zinc layer, a zinc-iron alloy layer, a zinc-nickel alloy layer, a zinc-manganese alloy layer and an aluminum layer.
Claim 13
Dependent Claim
35 words
The steel sheet as claimed in any one of claims 1 to 11, in which the coating amount of the chromate film is from 10 to 150 mg/m 2 , as calculated as metal chromium.
Claim 14
Dependent Claim
35 words
The steel sheet as claimed in any one of claims 1 to 11, in which the coating amount of the chromate film is from 40 to 100 mg/m 2 , as calculated as metal chromium.
Claim 15
Dependent Claim
24 words
The steel sheet as claimed in claim 1, in which said composite silicate resin film has a thickness of from 0.04 to 4 μm.
Claim 16
Dependent Claim
24 words
The steel sheet as claimed in claim 1, in which said composite silicate resin film has a thickness of from 0.4 to 4 μm.
Claim 17
Dependent Claim
49 words
The steel sheet as claimed in any one of claims 1 to 11, in which the coating amount of said chromate film is from 70 to 100 mg/m 2 as calculated as metal chromium and said composite silicate resin film has a thickness of from 0.5 to 0.9 μm.
Claim 18
Dependent Claim
82 words
The steel sheet as claimed in claim 1, in which said composite silicate resin film is formed by application of a composite silicate resin treatment solution prepared by adding, to a treatment solution composed of a mixture of a colloidal silica and an organic resin in a solid content weight ratio of from 5:95 to 95:5, from 0.5 to 15% by weight, based on the weight of the total solid content of said colloidal silica and organic resin, of a silane compound.
Claim 19
Dependent Claim
41 words
The steel sheet as claimed in claim 17, in which said silane compound is added in an amount of from 1 to 10% by weight, based on the weight of the total solid content of said colloidal silica and organic resins.
Claim 20
Dependent Claim
44 words
The steel sheet as claimed in claim 17, in which an alkoxide chelate compound is further added to said composite silicate resin treatment solution, in a solid content weight ratio of the treatment solution to the alkoxide chelate compound being from 97:3 to 80:20.
Claim 21
Dependent Claim
67 words
The steel sheet as claimed in claim 17, in which one or more additives selected from the group consisting of oxy acids of molybdenum, tungsten, vanadium, tin, boron and silicon, and salts of such oxy acids, are added to said composite silicate resin treatment solution, in a solid content amount of not more than 10% by weight, based on the solid content of the composite silicate resin.
Claim 22
Dependent Claim
45 words
The steel sheet as claimed in claim 20, in which said one or more additives are added to the composite silicate resin solution, in a solid content amount of from 0.3 to 5% by weight, based on the solid content of the composite silicate resin.
Claim 23
Dependent Claim
17 words
The steel sheet as claimed in claim 20 or 21, in which said additive is ammonium metavanadate.
Claim 24
Dependent Claim
58 words
The steel sheet as claimed in claim 17, in which an alkoxide chelate compound and one or more additives selected from the group consisting of oxy acids of molybdenum, tungsten, vanadium, tin, boron and silicon, and salts of such oxy acids, are added to said composite silicate resin treatment solution in the following solid content weight ratios: ##EQU1##
Claim 25
Dependent Claim
100 words
The steel sheet as claimed in claim 17, in which said organic resin is a polyvinyl alcohol, and one or more additives selected from the group consisting of water soluble salts and coordination compounds of copper, zinc, aluminum, zirconium, chromium, cobalt, and nickel, are added to the composite silicate resin treatment solution, in a solid content amount of from 0.3 to 5% by weight, based on the solid content of the treatment solution, and an alkoxide chelate compound is further added in the following solid content weight ratio: Composite silicate resin+said one or more additives: alkoxide chelate compound=97:3 to 80:2.
Claim 26
Dependent Claim
115 words
The steel sheet as claimed in claim 17, in which said organic resin is an ultraviolet or electron beam curing type resin, and one or more additives selected from the group consisting of oxy acids of molybdenum, tungsten and vanadium and salts of such oxy acids, are added to said composite silicate resin treatment solution, in a solid content amount of from 0.1 to 6% by weight, based on the solid content of the treatment solution, and a photosensitizer selected from the group consisting of zinc oxide, titanium oxide (anatase type), and titanic acid, is added in a solid content amount of from 30 to 200% by weight, based on said one or more additives.
References Cited (Backward Citations)
US3827866A
Cited
US3671205A
Cited
US3558442A
Cited
US3743551A
Cited
US3799814A
Cited
US3860398A
Cited
US4162350A
Cited
US4069360A
Cited
US4152487A
Cited
US4298661A
Cited
US4307156A
Cited
US4249999A
Cited
US4313996A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-24 | 1987-04-25 | 1987-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-24 | 1991-04-25 | 1991-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-24 | 1995-04-25 | 1995-10-25 | $7700.00 | Window Closed / Lapsed |