Assignee: JFE Engineering Corp
•
Filing: 1984-08-27
•
Granted: 1987-04-21
•
Expires: 2004-08-27
Abstract
Abstract The present invention relates to a process for the preparation of a highly anticorrosive surface-treated steel plate. This process comprises the steps of subjecting a surface of a steel plate having a plating layer of the zinc or aluminum type deposited thereon to a chromate treatment to form a chromate film, treating the steel plate with an organic composite silica solution comprising an epoxy resin in an amount exceeding a certain level as an indispensable component and a curing agent optionally incorporated therein to form an organic composite silicate film comprising colloidal silica, organic resin and silane formed on the chromate film, and heat-treating the steel plate at a specific temperature.
Inventors
- 👤 Tomihiro Hara
- 👤 Takeshi Adaniya
- 👤 Masaaki Yamashita
- 👤 Akira Enatsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 00:32
CPC Classifications
C; C23; C23F; C23F17/00; C09; C09D; C09D5/00; C09D5/08; C23C; C23C22/00; C23C22/82; C23C22/83; C25; C25D; C25D11/00; C25D11/38; C23C2222/00; C23C2222/20; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12556; Y10T428/12569
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
142 words
A process for the preparation of a highly anticorrosive surface-treated steel plate, which comprises subjecting a plated surface of a steel plate having a plating layer of the zinc or aluminum type to the following treatments: (a) subjecting the steel plate to a chromate treatment to form a chromate film, (b) treating the steel plate with an organic composite silicate solution comprising an organic resin, a colloidal silica compound and a silane compound and containing an epoxy resin in an amount of at least 15% by weight based on the total solids to form an organic composite silicate film formed on said chromate film and consisting essentially of colloidal silica, organic resin and silane in an amount deposited of 0.5 to 4.0 g/m 2 on the chromate film, and (c) heat-treating the steel plate at a temperature of 100° to 300° C.
Claim 2
Dependent Claim
142 words
A process for the preparation of a highly anticorrosive surface-treated steel plate, which comprises subjecting a plated surface of a steel plate having a plating layer of the zinc or aluminum type to the following treatments: (a) subjecting the steel plate to a chromate treatment to form a chromate film, (b) treating the steel plate with an organic composite silicate solution comprising an organic resin, a colloidal silica compound and a silane compound and containing an epoxy resin in an amount of at least 15% by weight based on the total solids to form an organic composite silicate film formed on said chromate film and consisting essentially of colloidal silica, organic resin and silane in an amount deposited of 0.5 to 4.0 g/m 2 on the chromate film, and (c) heat-treating the steel plate at a temperature of 100° to 300° C.
Claim 3
Dependent Claim
80 words
A process according to claim 1, wherein the steel plate is treated with an organic composite silicate solution containing an epoxy resin in an amount of at least 26% by weight, based on the total solids and having an SiO 2 /organic resin weight ratio of from 60/40 to 10/90, preferably from 50/50 to 20/80, to form an organic composite silicate film on the chromate film and the steel plate is heat-treated at a temperature of 250° to 300° C.
Claim 4
Dependent Claim
94 words
A process according to claim 1 or 2, wherein the steel plate having a plating layer of the zinc type is a steel plate having a plating layer of Zn, an Ni-Zn alloy, an Fe-Zn alloy, a Zn-Mn alloy, a Zn-Al alloy or a Zn-Co-Cr alloy, a steel plate having a plating layer of at least one element selected from Ni, Fe, Mn, Co, Al and Cr, incorporated into one of the foregoing plating components, or a steel plate having at least two same or different plating layers selected from the foregoing plating layers.
Claim 5
Dependent Claim
41 words
A process according to claim 1 or 2, wherein the chromate treatment is carried out so that the chromate film is deposited in an amount of 1 to 1000 mg/m 2 , preferably 10 to 200 mg/m 2 , as chromium.
Claim 6
Dependent Claim
18 words
A process according to claim 1 or 2, wherein the chromate treatment is a coating type chromate treatment.
Claim 7
Dependent Claim
17 words
A process according to claim 1 or 2, wherein the chromate treatment is an electrolytic chromate treatment.
Claim 8
Dependent Claim
18 words
A process according to claim 1 or 2, wherein the chromate treatment is a reaction type chromate treatment.
Claim 9
Dependent Claim
34 words
A process according to claim 1 or 2, wherein the organic composite silicate is an epoxy composite silicate or a mixture of an epoxy composite silicate with at least one other organic composite silicate.
Claim 10
Dependent Claim
59 words
A process according to claim 1 or 2, wherein at least one additive selected from oxyacids of molybdenum, tungsten and vanadium, salts thereof and alkoxide chelates of titanium and zirconium are incorporated into the organic composite silica in an amount of up to 14% by weight based on the total solids of the organic resin and SiO 2 .
Claim 11
Dependent Claim
147 words
A process for the preparation of a highly anticorrosive surface-treated steel plate, which comprises subjecting a plated surface of a steel plate having a plating layer of the zinc type or aluminum type to the following treatments: (a) subjecting the steel plate to a chromate treatment to form a chelate film, (b) treating the steel plate with an organic composite silicate solution comprising an organic resin, a colloidal silica compound and a silane compound and containing an epoxy resin in an amount of at least 15% by weight based on the total solids, in which a curing agent is incorporated, to form an organic composite silicate film formed on said chromate film and comprising colloidal silica, organic resin and silane in an amount of 0.4 to 4.0 g/m 2 on the chromate film, and (c) heat-treating the steel plate at a temperature of 100° to 350° C.
Claim 12
Dependent Claim
147 words
A process for the preparation of a highly anticorrosive surface-treated steel plate, which comprises subjecting a plated surface of a steel plate having a plating layer of the zinc type or aluminum type to the following treatments: (a) subjecting the steel plate to a chromate treatment to form a chelate film, (b) treating the steel plate with an organic composite silicate solution comprising an organic resin, a colloidal silica compound and a silane compound and containing an epoxy resin in an amount of at least 15% by weight based on the total solids, in which a curing agent is incorporated, to form an organic composite silicate film formed on said chromate film and comprising colloidal silica, organic resin and silane in an amount of 0.4 to 4.0 g/m 2 on the chromate film, and (c) heat-treating the steel plate at a temperature of 100° to 350° C.
Claim 13
Dependent Claim
80 words
A process according to claim 10, wherein the steel plate is treated with an organic composite silicate solution containing an epoxy resin in an amount of at least 26% by weight based on the total solids and having an SiO 2 /organic resin weight ratio of from 60/40 to 10/90, preferably from 50/50 to 20/80, to form an organic composite silicate film on the chromate film and the steel plate is heat-treated at a temperature of 250° to 350° C.
Claim 14
Dependent Claim
86 words
A process according to claim 10 or 11, wherein at least one member selected from melamine, a blocked isocyanate, urea, a phenol, a polyamide, an amino resin, an amine, an organic acid, an inorganic acid, an alcohol, a mercaptan and an acid anhydride is incorporated as the curing agent in the organic composite silicate solution in an amount of 0.1 to 100 parts by weight, preferably 0.3 to 50 parts by weight, per 100 parts by weight of the epoxy resin in the organic composite silicate.
Claim 15
Dependent Claim
94 words
A process according to claim 10 or 11, wherein the steel plate having a plating layer of the zinc type is a steel plate having a plating layer of Zn, an Ni--Zn alloy, an Fe--Zn alloy, a Zn--Mn alloy, a Zn--Al alloy or a Zn--Co--Cr alloy, a steel plate having a plating layer of at least one element selected from Ni, Fe, Mn, Co, Al and Cr, incorporated into one of the foregoing plating components, or a steel plate having at least two same or different plating layers selected from the foregoing plating layers.
Claim 16
Dependent Claim
41 words
A process according to claim 10 or 11, wherein the chromate treatment is carried out so that the chromate film is deposited in an amount of 1 to 1000 mg/m 2 , preferably 10 to 200 mg/m 2 , as chromium.
Claim 17
Dependent Claim
18 words
A process according to claim 10 or 11, wherein the chromate treatment is a coating type chromate treatment.
Claim 18
Dependent Claim
17 words
A process according to claim 10 or 11, wherein the chromate treatment is an electrolytic chromate treatment.
Claim 19
Dependent Claim
18 words
A process according to claim 10 or 11, wherein the chromate treatment is a reaction type chromate treatment.
Claim 20
Dependent Claim
34 words
A process according to claim 10 or 11, wherein the organic composite silicate is an epoxy composite silicate or a mixture of an epoxy composite silicate with at least one other organic composite silicate.
Claim 21
Dependent Claim
59 words
A process according to claim 10 or 11, wherein at least one additive selected from oxyacids of molybdenum, tungsten and vanadium, salts thereof and alkoxide chelates of titanium and zirconium are incorporated into the organic composite silicate in an amount of up to 14% by weight based on the total solids of the organic resin and SiO 2 .
Claim 22
Dependent Claim
46 words
A process according to claim 1, 2, 10 or 11, wherein one surface of a steel plate having both the surfaces deposited with a plating layer of the zinc type is subjected to the chromate treatment, the organic composite silicate solution treatment and the heat treatment.
Claim 23
Dependent Claim
68 words
A process according to claim 1, 2, 10 or 11, wherein one surface of a steel plate having both the surfaces deposited with a plating layer of the zinc type is plated with iron or an iron-zinc alloy having an iron content of at least 50% by weight and the other surface is subjected to the chromate treatment, the organic composite silicate solution treatment and the heat treatment.
Claim 24
Dependent Claim
21 words
A process according to claim 2, wherein said epoxy resin is present in an amount of at least 35% by weight.
Claim 25
Dependent Claim
26 words
A process according to claim 9, wherein said alkoxide chelates are incorporated into said organic composite silicate in an amount of up to 14% by weight.
Claim 26
Dependent Claim
21 words
A process according to claim 11, wherein said epoxy resin is present in an amount of at least 35% by weight.
Claim 27
Dependent Claim
26 words
A process according to claim 19, wherein said alkoxide chelates are incorporated into said organic composite silicate in an amount of up to 14% by weight.
References Cited (Backward Citations)
US4411964A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |