Hydrophobic microporous membrane

Claim 2

A cured hydrophobic microporous membrane laminated to a support material, said membrane having a thickness of about 0.1 inches or less, which in its part cure and full cure stages is the rapidly polymerized reaction product of ultraviolet or electron beam polymerized monomer and oligomer components comprising: a primary membrane oligomer component selected from the group comprising acrylic polyester urethanes derived through reaction of a polyester polyol and a polyisocyanate; and a secondary membrane monomer component selected from the group comprising:

Claim 3

1, 3, 3-tetramethylbutylacrylamide; a perfluoromonomer of the general formula ##STR5## where R F is the perfluoroalkyl radical C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and a perfluoroacrylic monomer of the general formula ##STR6## where R F =C z F 2z+1 and z=6 to 8; said secondary membrane monomer being in an amount effective to impart hydrophobic properties to said membrane.

Claim 4

1, 3, 3-tetramethylbutylacrylamide; a perfluoromonomer of the general formula ##STR5## where R F is the perfluoroalkyl radical C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and a perfluoroacrylic monomer of the general formula ##STR6## where R F =C z F 2z+1 and z=6 to 8; said secondary membrane monomer being in an amount effective to impart hydrophobic properties to said membrane.

Claim 5

The membrane of claim 1 wherein said primary membrane oligomer component is a mixture of one or more acrylic polyester urethanes selected from the following general formulas ##STR7## where R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polymester polyol, and n=0 to 4.

Claim 6

The membrane of claim 1 wherein said components further comprises a monomer component selected from difunctional and trifunctional crosslinking monomers.

Claim 7

The membrane of claim 1 wherein said components further comprises a polymer modifying monomer.

Claim 8

The membrane of claim 1 wherein said microporous membrane is laminated to a support material.

Claim 9

A hydrophobic microporous membrane structure comprising: A. ultraviolet or electron beam rapidly polymerized monomer and oligomer components which in its part cure and full cure stages form a microporous membrane comprising: 1. a primary membrane oligomer component selected from acrylic polyester urethanes derived through reaction of a polyester polyol and a polyisocyanate of the following general formulas ##STR8## wherein R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polyester polyol, and n=0 to 4; and

Claim 10

A hydrophobic microporous membrane structure comprising: A. ultraviolet or electron beam rapidly polymerized monomer and oligomer components which in its part cure and full cure stages form a microporous membrane comprising: 1. a primary membrane oligomer component selected from acrylic polyester urethanes derived through reaction of a polyester polyol and a polyisocyanate of the following general formulas ##STR8## wherein R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polyester polyol, and n=0 to 4; and

Claim 11

a secondary membrane monomer component in an amount effective to impart hydrophobic barrier properties to said microporous membrane selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR9## where R F is the perfluoroalkyl radical of C k F 2K+1 where k is essentially 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR10## where R F is C z F 2z+1 and z=6 to 8; said microporous membrane having a thickness of about 0.1 inches or less; and B. a support material laminated to at least one surface of said microporous membrane.

Claim 12

a secondary membrane monomer component in an amount effective to impart hydrophobic barrier properties to said microporous membrane selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR9## where R F is the perfluoroalkyl radical of C k F 2K+1 where k is essentially 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR10## where R F is C z F 2z+1 and z=6 to 8; said microporous membrane having a thickness of about 0.1 inches or less; and B. a support material laminated to at least one surface of said microporous membrane.

Claim 13

The structure of claim 6 wherein said polymerized monomer and oligomer components further comprises difunctional and trifunctional crosslinking monomers selected from 1,4-butanedioldiacrylate, 1,6-hexanedioldiacrylate, trimethylolpropanetriacylate, tetraethylene glycol diacrylate, tripropylene glycol diacrylate, neopentyl glycol diacrylate, polyethylene glycol diacrylates, polypropylene glycol diacrylates 1,3 butylene glycol diacrylate, diacrylates and triacrylates derived from ethoxylated and propoxylated diols and triols.

Claim 14

The structure of claim 6 wherein said polymerized monomer and oligomer components further comprises polymer modifying monomers selected from acrylic acid, N-vinylpyrrolidone, N-vinylcaprolactam, 2-ethylhexylacrylate, phenoxyethylacrylate, isobornylacrylate, dicyclopentadienyl ethyl acrylate, tetrahydrofurfuyl acrylate, ethyldiglycolacrylate, hydroxyethylacrylate, hydroxypropylacrylate, butyl carbanylethyacrylate, isobutoxymethylacrylamide.

Claim 15

A process for preparing a membrane laminate, comprising: A. mixing into a liquid vehicle to form a solution 1. oligomers selected from the group comprising acrylic polyester urethanes derived through reaction of a polyester polyol and a polyisocyanate, and 2. monomers selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR11## where R F is the perfluoroalkyl radical C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR12## said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from, and otherwise chemically inert to, said oligomers and polymers; B. forming a layer of said solution; C. partially polymerizing with ultraviolet or electron beam irradiation said oligomers and said monomers in the presence of atmospheric oxygen to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation, said monomers being in an amount sufficient to impart hydrophobic barrier properties to the completely polymerized layer; and F. removing said liquid vehicle to form a microporous membrane-support layer laminate.

Claim 16

A process for preparing a membrane laminate, comprising: A. mixing into a liquid vehicle to form a solution 1. oligomers selected from the group comprising acrylic polyester urethanes derived through reaction of a polyester polyol and a polyisocyanate, and 2. monomers selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR11## where R F is the perfluoroalkyl radical C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR12## said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from, and otherwise chemically inert to, said oligomers and polymers; B. forming a layer of said solution; C. partially polymerizing with ultraviolet or electron beam irradiation said oligomers and said monomers in the presence of atmospheric oxygen to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation, said monomers being in an amount sufficient to impart hydrophobic barrier properties to the completely polymerized layer; and F. removing said liquid vehicle to form a microporous membrane-support layer laminate.

Claim 17

The process of claim 9 wherein said oligomers mixed into said liquid vehicle are selected from acrylic polyester urethanes selected from the following general formulas ##STR13## where R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polyester polyol, and n is 0 to 4.

Claim 18

The process of claim 9 further comprising mixing into said solution prior to polymerization a monomer selected from difunctional and trifunctional crosslinking monomers.

Claim 19

The process of claim 9 further comprising mixing into said solution prior to polymerization a polymer modifying monomer.

Claim 20

A process for preparing a membrane laminate, comprising: A. mixing into a liquid vehicle acrylic polyester oligomers derived through reaction of a polyester polyol and a polyisocyanate and monomers which are rapidly polymerizable under electron beam or ultraviolet irradiation to form a first solution, said monomers being selected from the group comprising 1. 1, 1, 3, 3-tetramethylbutylacrylamide, 2. a perfluoromonomer of the general formula ##STR14## where R F is C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and

Claim 21

A process for preparing a membrane laminate, comprising: A. mixing into a liquid vehicle acrylic polyester oligomers derived through reaction of a polyester polyol and a polyisocyanate and monomers which are rapidly polymerizable under electron beam or ultraviolet irradiation to form a first solution, said monomers being selected from the group comprising 1. 1, 1, 3, 3-tetramethylbutylacrylamide, 2. a perfluoromonomer of the general formula ##STR14## where R F is C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m=2 to 4, and R' is hydrogen or methyl; and

Claim 22

a perfluoroacrylic monomer of the general formula ##STR15## where R F is C z F 2z+1 and z=6 to 8; and further being in an amount sufficient to impart hydrophobic barrier properties to the membrane laminate prepared by the process; said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from, and otherwise chemically inert to, said oligomers and polymers; B. forming a layer of said solution; C. partially polymerizing with ultraviolet or electron beam irradiation said oligomers and said monomers in the presence of atmospheric oxygen to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation; F. forming a second layer from solution as defined in step A; G. partially polymerizing with ultraviolet or electron beam irradiation oligomers and monomers in said second layer in the presence of atmospheric oxygen to form a second partially polymerized layer; H. contacting the coated side of the laminate formed in step E to said second partially polymerized layer; I. completing the polymerization of said second partially polymerized layer with ultraviolet or electron beam radiation; and J. removing said liquid vehicle from both polymerized layers.

Claim 23

a perfluoroacrylic monomer of the general formula ##STR15## where R F is C z F 2z+1 and z=6 to 8; and further being in an amount sufficient to impart hydrophobic barrier properties to the membrane laminate prepared by the process; said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from, and otherwise chemically inert to, said oligomers and polymers; B. forming a layer of said solution; C. partially polymerizing with ultraviolet or electron beam irradiation said oligomers and said monomers in the presence of atmospheric oxygen to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation; F. forming a second layer from solution as defined in step A; G. partially polymerizing with ultraviolet or electron beam irradiation oligomers and monomers in said second layer in the presence of atmospheric oxygen to form a second partially polymerized layer; H. contacting the coated side of the laminate formed in step E to said second partially polymerized layer; I. completing the polymerization of said second partially polymerized layer with ultraviolet or electron beam radiation; and J. removing said liquid vehicle from both polymerized layers.

Claim 24

A process for preparing a hydrophobic microporous membrane laminate, comprising: A. mixing into a liquid vehicle to form a solution 1. acrylic polyester urethane oligomers derived through reaction of a polyester polyol and a polyisocyanate selected from the group comprising urethanes of the following general formulas ##STR16## where R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polyester polyol, and n is 0 to 4; and

Claim 25

A process for preparing a hydrophobic microporous membrane laminate, comprising: A. mixing into a liquid vehicle to form a solution 1. acrylic polyester urethane oligomers derived through reaction of a polyester polyol and a polyisocyanate selected from the group comprising urethanes of the following general formulas ##STR16## where R 1 is the radical of a hydroxyterminated acrylate monomer, R 2 is a dicarbamate or tricarbamate group, R 3 is a polyester polyol, and n is 0 to 4; and

Claim 26

monomers selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR17## where R F is the perfluoroalkyl radical of C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m is 2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR18## where R F is C z F 2z+1 and z is 6 to 8, and being in an amount sufficient to impart hydrophobic barrier properties to the membrane laminate prepared by the process; said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from said oligomers and said monomers and otherwise chemically inert to said oligomers and monomers; B. forming a layer of said solution; C. partially polymerizing the oligomers and polymers of said solution in the presence of atmospheric oxygen with ultraviolet or electron beam irradiation to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation; and F. removing said liquid vehicle to form a microporous membrane-support layer laminate.

Claim 27

monomers selected from the group comprising (a) 1, 1, 3, 3-tetramethylbutylacrylamide, (b) a perfluoromonomer of the general formula ##STR17## where R F is the perfluoroalkyl radical of C k F 2K+1 where k is 6 to 10, R is C m H 2m+1 where m is 2 to 4, and R' is hydrogen or methyl; and (c) a perfluoroacrylic monomer of the general formula ##STR18## where R F is C z F 2z+1 and z is 6 to 8, and being in an amount sufficient to impart hydrophobic barrier properties to the membrane laminate prepared by the process; said liquid vehicle being a solvent for said oligomers and monomers and a nonsolvent for polymers formed from said oligomers and said monomers and otherwise chemically inert to said oligomers and monomers; B. forming a layer of said solution; C. partially polymerizing the oligomers and polymers of said solution in the presence of atmospheric oxygen with ultraviolet or electron beam irradiation to form a partially polymerized layer; D. contacting a support material layer to said partially polymerized layer; E. completing the polymerization of said partially polymerized layer with ultraviolet or electron beam irradiation; and F. removing said liquid vehicle to form a microporous membrane-support layer laminate.

Claim 28

The process of claim 14 further comprising mixing into said solution prior to polymerization a monomer selected from difunctional and trifunctional crosslinking monomers.

Claim 29

The process of claim 14 further comprising mixing into said solution prior to polymerization a polymer modifying monomer.

Claim 30

The process of claim 14 further comprising mixing into said solution prior to polymerization a surfactant.

Claim 31

The process of claim 14 wherein said support material is selected from woven and nonwoven fabric and paper.

Claim 36

The method of claim 20 wherein after contacting the support material to the partially polymerized layer, the irradiation is directed thorough the support material.

Claim 37

The method of claim 20 wherein the partial polymerization step is conducted in the presence of atmospheric oxygen.

Claim 38

The method of claim 20 further including the steps of partially polymerizing a second solution layer containing oligomers and monomers with electron beam or ultraviolet irradiation, contacting said second partially polymerized layer with the laminated material at the polymerized coating interface and completing polymerization of the second partially polymerized layer with electron beam or ultraviolet irradiation.

Claim 39

The method of claim 20 wherein the coating surface of a second laminate prepared according to steps (a) through (e) is contacted to the coating surface of the first laminate and the contacted coating surfaces are irradiated with ultraviolet or electron beam irradiation.