Moisture-permeable waterproof coated fabric
Assignee: Toray Industries Inc
•
Filing: 1983-10-28
•
Granted: 1985-12-24
•
Expires: 2003-10-28
Abstract
Abstract A moisture-permeable waterproof coated fabric having a microporous polyurethane layer is obtained by the so-called wet coagulation method using as a coated solution a polar organic solvent solution containing 8 to 25% by weight of a polyurethane elastomer, 0.1 to 10% by weight of a water repellent agent, 0.2 to 3% by weight of polyisocyanate and 1 to 8% by weight of a nonionic surfactant.
Inventors
- 👤 Yasushi Naka
- 👤 Kiyoshi Kawakami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:12
CPC Classifications
D; D06; D06N; D06N3/00; D06N3/12; D06N3/14; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249975; Y10T428/249978; Y10T428/24998; Y10T428/249981; Y10T428/31504; Y10T428/31551; Y10T428/31562; Y10T428/31565; Y10T442/00; Y10T442/20; Y10T442/2033; Y10T442/2139; Y10T442/2164; Y10T442/2197
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
176 words
A moisture-permeable waterproof coated fabric comprising a base fabric and a microporous layer of a synthetic polymer consisting essentially of polyurethane formed on at least one face of said base fabric characterized in that said microporous layer being provided therewithin with cavity portions communicating with fine pores having diameters not larger than 5 microns formed on the surface of said microporous layer, the void portions of said cavity portions having diameters at least three times as large as the diameters of said fine pores and further characterized in that the inner wall of said respective cavity is covered with water repellent agent and at least a part of said inner wall is provided at least a communication hole on it to communicate between adjacent cavities, said microporous layer being formed from a coating solution of a polar organic solvent containing 8 to 25% by weight of a polyurethane elastomer, 0.1 to 10% by weight of a water repellent agent, 0.2 to 3% by weight of polyisocyanate and 1 to 8% by weight of a nonionic surfactant.
Claim 2
Dependent Claim
176 words
A moisture-permeable waterproof coated fabric comprising a base fabric and a microporous layer of a synthetic polymer consisting essentially of polyurethane formed on at least one face of said base fabric characterized in that said microporous layer being provided therewithin with cavity portions communicating with fine pores having diameters not larger than 5 microns formed on the surface of said microporous layer, the void portions of said cavity portions having diameters at least three times as large as the diameters of said fine pores and further characterized in that the inner wall of said respective cavity is covered with water repellent agent and at least a part of said inner wall is provided at least a communication hole on it to communicate between adjacent cavities, said microporous layer being formed from a coating solution of a polar organic solvent containing 8 to 25% by weight of a polyurethane elastomer, 0.1 to 10% by weight of a water repellent agent, 0.2 to 3% by weight of polyisocyanate and 1 to 8% by weight of a nonionic surfactant.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-23 | 1989-06-24 | 1989-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-23 | 1993-06-24 | 1993-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-23 | 1997-06-24 | 1997-12-24 | $7700.00 | Window Closed / Lapsed |