US5094984A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Suppression of water vapor absorption in glass encapsulation
Assignee: HP Inc
•
Filing: 1991-06-25
•
Granted: 1992-03-10
•
Expires: 2011-06-25
Abstract
Abstract A method for encapsulation of an integrated circuit array that suppresses or eliminates absorption and subsequent out-gassing of water vapor and suppresses or eliminates out-gassing of toxic constituents of the encapsulation layer such as trimethyl borate. A first layer of borophosphosilicate glass is deposited on the integrated circuit array, followed immediately by deposit of a thin cap layer of undoped oxide of silicon. The method also allows use of boron and phosphorous concentrations in the borophosphosilicate glass as high as 9 weight percent with no loss of stability of that layer, before or after thermal treatment. Reflow processing temperatures as low as Tr=700 DEG -900 DEG C. may be used here. Alternatively, silicon nitride can replace the silicon oxide in the cap layer, using either a high temperature process or a lower temperature plasma-enhanced process.
Inventors
- 👤 Charles C. Liu
- 👤 Krzysztof Nauka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:10
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6923; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/66; H10P14/662; H10P14/69215; H10W; H10W74/00; H10W74/40; H10W74/43; H10P14/668; H10P14/6681; H10P14/6682; Y; Y10; Y10S; Y10S148/00; Y10S148/043; Y10S148/133
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
87 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; and immediately, without breaking the vacuum, forming a layer of undoped oxide of silicon, of thickness more than 100 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 2
Independent Claim
87 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; and immediately, without breaking the vacuum, forming a layer of undoped oxide of silicon, of thickness more than 100 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 3
Dependent Claim
34 words
The method of claim 1, further comprising the step of choosing the temperature at which said layer of undoped silicon oxide is formed at between T f =300° C. and T f =450° C.
Claim 4
Dependent Claim
19 words
The method of claim 2, further comprising the step of choosing said temperature T f as approximately 420° C.
Claim 5
Dependent Claim
25 words
The method of claim 1, further comprising the step of choosing said phosphorous concentration in said borophosphosilicate glass in the range of 1-9 weight percent.
Claim 6
Dependent Claim
26 words
The method of claim 1, further comprising the step of annealing said encapsulated integrated circuit array at a temperature of at least T a =700° C.
Claim 7
Independent Claim
123 words
A method of encapsulating an integrated circuit array that allows use of reflow processing temperatures in the approximate range T r =700°-900° C. on the encapsulated structure, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the circuit array in a vacuum; adjusting the temperature of the borophosphosilicate layer to a temperature T<750° C.; subjecting the encapsulating layer to reflow processing at a reflow temperature in the range T r =700°-900° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 8
Independent Claim
123 words
A method of encapsulating an integrated circuit array that allows use of reflow processing temperatures in the approximate range T r =700°-900° C. on the encapsulated structure, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the circuit array in a vacuum; adjusting the temperature of the borophosphosilicate layer to a temperature T<750° C.; subjecting the encapsulating layer to reflow processing at a reflow temperature in the range T r =700°-900° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 9
Independent Claim
110 words
A method of encapsulating an integrated circuit array that allows use of reflow processing temperatures in the approximate range T r =700°-900° C. on the encapsulated structure, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration of 5-9 weight percent, said borophosphosilicate layer being at least 02. μm thick over the circuit array in a vacuum; subjecting the encapsulating layer to reflow processing at a reflow temperature in the range T=700°-900° C.; and immediately, without breaking the vacuum, forming a layer of an undoped oxide of silicon, of thickness more than 100 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 10
Independent Claim
110 words
A method of encapsulating an integrated circuit array that allows use of reflow processing temperatures in the approximate range T r =700°-900° C. on the encapsulated structure, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration of 5-9 weight percent, said borophosphosilicate layer being at least 02. μm thick over the circuit array in a vacuum; subjecting the encapsulating layer to reflow processing at a reflow temperature in the range T=700°-900° C.; and immediately, without breaking the vacuum, forming a layer of an undoped oxide of silicon, of thickness more than 100 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 11
Independent Claim
100 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; adjusting the temperature of the borophosphosilicate layer to a temperature T≧750° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 12
Independent Claim
100 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; adjusting the temperature of the borophosphosilicate layer to a temperature T≧750° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50 Å over the borophosphosilicate layer, after formation of the borophosphosilicate layer.
Claim 13
Dependent Claim
25 words
The method of claim 8, further comprising the step of choosing said phosphorous concentration in said borophosphosilicate glass in the range of 1-9 weight percent.
Claim 14
Dependent Claim
32 words
The method of claim 8, further comprising the step of annealing said encapsulated integrated circuit array, after formation of said borophosphosilicate layer, at a temperature of at least T a =750° C.
Claim 15
Independent Claim
104 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; adjusting the temperature of the borophosphosilicate layer to the approximate temperature range 275° C.≦T≦400° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50 Å after formation of the borophosphosilicate layer, by plasma-enhanced chemical vapor deposition.
Claim 16
Independent Claim
104 words
A method of encapsulating an integrated circuit array that suppresses the absorption of water vapor by the encapsulating layer, the method comprising the steps of: forming a layer of borophosphosilicate glass having a boron concentration in the range of 5-9 weight percent, said borophosphosilicate layer being at least 0.2 μm thick over the array in a vacuum; adjusting the temperature of the borophosphosilicate layer to the approximate temperature range 275° C.≦T≦400° C.; and immediately, without breaking the vacuum, forming a layer of an undoped nitride of silicon, of thickness more than 50 Å after formation of the borophosphosilicate layer, by plasma-enhanced chemical vapor deposition.
Claim 17
Dependent Claim
25 words
The method of claim 11, further comprising the step of choosing said phosphorous concentration in said borophosphosilicate glass in the range of 1-9 weight percent.
References Cited (Backward Citations)
US4097889A
Cited
US4628590A
Cited
US4835597A
Cited
US4708884A
Cited
US4903117A
Cited
US4879253A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-10 | 1995-09-09 | 1996-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-10 | 1999-09-09 | 2000-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-10 | 2003-09-09 | 2004-03-10 | $7700.00 | Window Closed / Lapsed |