Photographic support comprising a layer containing an electron beam hardened resin and white pigment of a thickness of 5-100 microns
Assignee: Mitsubishi Paper Mills Ltd
•
Filing: 1989-02-23
•
Granted: 1992-01-28
•
Expires: 2009-02-23
Abstract
Abstract A photographic support having a layer of a white pigment and an electron beam hardenable resin on a support can be improved in adhesive strength, surface appearance and other properties by forming an outermost layer containing an ultraviolet curable resin, or impregnating an electron beam hardenable resin into the support, or inserting an electron beam hardenable leveling agent into the white pigment-resin layer, or forming an outermost layer containing a fluorescent agent and an electron beam hardenable resin.
Inventors
- 👤 Junji Harada
- 👤 Seigo Ebato
- 👤 Takahisa Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 02:24
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/76; G03C1/775; G03C1/79; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/926; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2995; Y10T428/31; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T428/31855; Y10T428/3188; Y10T428/31884; Y10T428/31909; Y10T428/31913; Y10T428/31971; Y10T428/31993; Y10T428/31996
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
81 words
A photographic support comprising a base sheet, a hardened layer having a thickness of 5 to 100 μm obtained from a composition comprising a white pigment and an electron beam hardened resin, said composition formed on one surface of the base sheet, and a hardened layer having a thickness of 0.1 to 10 μm obtained from a composition comprising an ultraviolet hardened resin and a photopolymerization initiator, said latter composition formed on the hardened layer containing the electron beam hardened resin.
Claim 2
Dependent Claim
81 words
A photographic support comprising a base sheet, a hardened layer having a thickness of 5 to 100 μm obtained from a composition comprising a white pigment and an electron beam hardened resin, said composition formed on one surface of the base sheet, and a hardened layer having a thickness of 0.1 to 10 μm obtained from a composition comprising an ultraviolet hardened resin and a photopolymerization initiator, said latter composition formed on the hardened layer containing the electron beam hardened resin.
Claim 3
Dependent Claim
21 words
A photographic support according to claim 1, wherein the hardened layer containing the ultraviolet hardened resin further contain a white pigment.
Claim 4
Dependent Claim
64 words
A photographic support comprising a base sheet obtained by impregnating an electron beam hardenable resin containing tri- or higher polyfunctional acrylate thereinto, followed by hardening with irradiation of electron beams, and an opaque resin coating layer containing a white pigment, formed on one surface of the base sheet, wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 5
Dependent Claim
64 words
A photographic support comprising a base sheet obtained by impregnating an electron beam hardenable resin containing tri- or higher polyfunctional acrylate thereinto, followed by hardening with irradiation of electron beams, and an opaque resin coating layer containing a white pigment, formed on one surface of the base sheet, wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 6
Dependent Claim
30 words
A photographic support according to claim 3, wherein a primer layer obtained by melt extruding a polyofefin resin is formed between the base sheet and the opaque resin coating layer.
Claim 7
Dependent Claim
30 words
A photographic support according to claim 3, wherein the opaque resin coating layer comprises a white pigment and an electron beam hardened resin and hardened by irradiation with electron beams.
Claim 8
Dependent Claim
69 words
A photographic support comprising a base sheet and a hardened layer obtained from a composition comprising a white pigment, an electron beam hardened resin, and an electron beam hardenable leveling agent, formed on one surface of the base sheet, electron beam irradiation being conducted in an oxygen concentration of 660 ppm or less, wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 9
Dependent Claim
69 words
A photographic support comprising a base sheet and a hardened layer obtained from a composition comprising a white pigment, an electron beam hardened resin, and an electron beam hardenable leveling agent, formed on one surface of the base sheet, electron beam irradiation being conducted in an oxygen concentration of 660 ppm or less, wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 10
Dependent Claim
22 words
A photographic support according to claim 6, wherein the electron beam hardenable leveling agent is a fluorine-containing acrylate or a perfluoroalkyl acrylate.
Claim 11
Dependent Claim
18 words
A photographic support according to claim 6, wherein the electron beam hardenable leveling agent is a silicone-containing acrylate.
Claim 12
Dependent Claim
22 words
A photographic support according to claim 6, wherein the electron beam hardenable leveling agent is an acrylate modified hydrocarbon surface active agent.
Claim 13
Dependent Claim
129 words
A photographic support comprising a base sheet, a hardened resin layer obtained from a composition comprising a white pigment and an electron beam hardened resin, said composition formed on one surface of the base sheet, and a hardened fluorescent-resin layer obtained from a composition comprising an electron beam hardened resin and a fluorescent agent, wherein the amount of said agent in said fluorescent resin layer is 0.01 to 1.00% by weight based on the weight of the electron beam resin, and said latter composition is formed on the hardened resin layer, hardening of the fluorescent-resin layer being conducted by irradiation of electron beams in an oxygen concentration of 660 ppm or less, and wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 14
Dependent Claim
129 words
A photographic support comprising a base sheet, a hardened resin layer obtained from a composition comprising a white pigment and an electron beam hardened resin, said composition formed on one surface of the base sheet, and a hardened fluorescent-resin layer obtained from a composition comprising an electron beam hardened resin and a fluorescent agent, wherein the amount of said agent in said fluorescent resin layer is 0.01 to 1.00% by weight based on the weight of the electron beam resin, and said latter composition is formed on the hardened resin layer, hardening of the fluorescent-resin layer being conducted by irradiation of electron beams in an oxygen concentration of 660 ppm or less, and wherein the electron beam hardened resin-pigment layer has a film thickness of 5 to 100 μm.
Claim 15
Dependent Claim
20 words
A photographic support according to claim 10, wherein the hardened fluorescent-resin layer has a thickness of 5 μm or less.
Claim 16
Dependent Claim
30 words
A photographic support according to claim 10, wherein an electron beam hardened leveling agent is contained in at least one of the hardened resin layer and the hardened fluorescent-resin layer.
Claim 17
Dependent Claim
16 words
A photographic support according to claim 10, wherein the fluorescent-resin layer further contains a photopolymerization initiator.
Claim 18
Dependent Claim
19 words
A photographic support according to claim 1-, which further comprises a hydrophilic coating layer on the hardened fluorescent-resin layer.
References Cited (Backward Citations)
US4070497A
Cited
US4311732A
Cited
US4384040A
Cited
US4364971A
Cited
US4326001A
Cited
US4508751A
Cited
US4426431A
Cited
US4645736A
Cited
US4558002A
Cited
US4729945A
Cited
US4590147A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-27 | 1995-07-29 | 1996-01-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-27 | 1999-07-29 | 2000-01-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-27 | 2003-07-29 | 2004-01-28 | $7700.00 | Window Closed / Lapsed |