US5070041A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of removing flash from a semiconductor leadframe using coated leadframe and solvent
Assignee: Mitsui Chemicals Inc
•
Filing: 1989-08-10
•
Granted: 1991-12-03
•
Expires: 2009-08-10
Abstract
Abstract In accordance with the present invention, semiconductor devices are produced by the process involving the steps of obtaining a core-box resin molded item integrated with a lead frame by coating said lead frame on its portions expected to be in non-contact with said core-box resin molded item with an organic high molecular substance having a melting or softening point higher than the molding temperature of the resin constituting said core-box resin molded item and soluble in a solvent which does not dissolve said core-box resin molded item, placing the thus coated lead frame in position within a mold and injecting the resin into the mold thereby carrying out injection or transfer molding and immersing the lead frame bearing core-box resin molded item obtained in the foregoing step in said solvent to remove by dissolving said organic high molecular substance. On that account, flashes of the resin formed on the lead frame can be removed with facility or the formation of said flashes can be suppressed without damaging the resin molded portion, whereby a good electrical connection between the lead frame and the semiconductor element can be accomplished.
Inventors
- 👤 Shigeru Katayama
- 👤 Kaoru Tominaga
- 👤 Toshio Suetsugu
- 👤 Kazumi Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:11
CPC Classifications
H; H10; H10W; H10W95/00; H10W70/00; H10W70/01; H10W70/04; H10W70/045; H10W76/00; H10W76/60; H10W72/00; H10W72/50; H10W72/551; H10W72/552; H10W72/5522; H10W72/5524; H10W72/851; H10W72/874; H10W72/884; H10W74/00; H10W90/00; H10W90/701; H10W90/731; H10W90/736; H10W90/751; H10W90/756; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49121
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
202 words
A process for producing a semiconductor device which is received in a concavity of a core-box resin molded item, said process comprising the steps of: coating a lead frame on its portions expected to be in non-contact with said core-box resin molded item with an organic high molecular substance having a melting or softening point higher than the molding temperature of a resin constituting said one-box resin molded item and soluble in a solvent which does not dissolve said core-box resin molded item, the organic high molecular substance being selected from the group consisting or cellulose derivatives and epoxy resins; placing the thus coated lead frame in position within a mold and injecting said resin into said mold, thereby obtaining the core-box resin molded item integrated with the lead frame; immersing the lead frame of the core-box resin molded item into said solvent to dissolve said organic high molecular substance coated on said lead frame; die-bonding said semiconductor element to an island of said lead frame and then wire bonding electrodes of said semiconductor element to said lead frame; and fusion-bonding a covering member of said core-box resin molded item to seal hermetically the whole concavity of said core-box resin molded item.
Claim 2
Dependent Claim
202 words
A process for producing a semiconductor device which is received in a concavity of a core-box resin molded item, said process comprising the steps of: coating a lead frame on its portions expected to be in non-contact with said core-box resin molded item with an organic high molecular substance having a melting or softening point higher than the molding temperature of a resin constituting said one-box resin molded item and soluble in a solvent which does not dissolve said core-box resin molded item, the organic high molecular substance being selected from the group consisting or cellulose derivatives and epoxy resins; placing the thus coated lead frame in position within a mold and injecting said resin into said mold, thereby obtaining the core-box resin molded item integrated with the lead frame; immersing the lead frame of the core-box resin molded item into said solvent to dissolve said organic high molecular substance coated on said lead frame; die-bonding said semiconductor element to an island of said lead frame and then wire bonding electrodes of said semiconductor element to said lead frame; and fusion-bonding a covering member of said core-box resin molded item to seal hermetically the whole concavity of said core-box resin molded item.
Claim 3
Dependent Claim
35 words
The process for producing a semiconductor device as claimed in claim 1 wherein a difference in linear expansion coefficient between the lead frame and the core-box resin molded item is less than 100×10 -7 cm/cm.°C.
Claim 4
Dependent Claim
22 words
The process for producing a semiconductor device as claimed in claim 1 wherein the lead frame is made of a copper alloy.
Claim 5
Dependent Claim
29 words
The process for producing a semiconductor device as claimed in claim 1 wherein the lead frame has a linear expansion coefficient of from 50×10 -7 to 200×10 -7 cm/cm.°C.
Claim 6
Dependent Claim
51 words
The process for producing a semiconductor device as claimed in claim 1 wherein the organic high molecular substance coated on the lead frame of the lead frame bearing core-box resin molded item is dissolved therefrom by immersing the lead frame in the solvent and subjecting the lead frame to ultrasonic vibration.
Claim 7
Dependent Claim
29 words
The process for producing a semiconductor device as claimed in claim 5 wherein the liquid used is selected from the group consisting of water, alcohols, ketones and halogenated hydrocarbons.
Claim 8
Dependent Claim
47 words
The process for producing a semiconductor device as claimed in claim 5 wherein the ultrasonic vibration treatment is carried out by two stages involving vibration with an ultrasonic wave having a frequency of 10-100 KHz and then with an ultrasonic wave having a frequency of 500-2,000 KHz.
Claim 9
Dependent Claim
142 words
A process for producing a semiconductor device having a semiconductor element which is received in a concavity of a core-box resin molded item, said process comprising the steps of: placing in position a lead frame having a linear expansion coefficient of from 50×10 -7 to 200×10 -7 cm/cm.°C. within a mold, and injecting the resin into said mold, thereby obtaining the core-box resin molded item integrated with the lead frame, a difference in linear expansion coefficient between the lead frame and the core-box resin molded item being less than 100×10 -7 cm/cm.°C.; die-bonding said semiconductor element to an island of the lead frame and then wire bonding electrodes of said semiconductor element to said lead frame; and fusion-bonding a covering member to the concavity of said core-box resin molded item to seal hermetically the whole concavity of said core-box resin molded item.
Claim 10
Dependent Claim
142 words
A process for producing a semiconductor device having a semiconductor element which is received in a concavity of a core-box resin molded item, said process comprising the steps of: placing in position a lead frame having a linear expansion coefficient of from 50×10 -7 to 200×10 -7 cm/cm.°C. within a mold, and injecting the resin into said mold, thereby obtaining the core-box resin molded item integrated with the lead frame, a difference in linear expansion coefficient between the lead frame and the core-box resin molded item being less than 100×10 -7 cm/cm.°C.; die-bonding said semiconductor element to an island of the lead frame and then wire bonding electrodes of said semiconductor element to said lead frame; and fusion-bonding a covering member to the concavity of said core-box resin molded item to seal hermetically the whole concavity of said core-box resin molded item.
Claim 11
Dependent Claim
22 words
The process for producing a semiconductor device as claimed in claim 8 wherein the lead frame is made of a copper alloy.
Claim 12
Dependent Claim
35 words
The process for producing a semiconductor device as claimed in claim 1 wherein the core-box resin molded item is made of a thermosetting resin selected from the group consisting of epoxy resins and imide resins.
Claim 13
Dependent Claim
22 words
The process for producing a semiconductor device as claimed in claim 2 wherein the lead frame is made of a copper alloy.
Claim 14
Dependent Claim
22 words
The process for producing a semiconductor device as claimed in claim 4 wherein the lead frame is made of a copper alloy.
References Cited (Backward Citations)
JPS553611A
Cited
JPS5662347A
Cited
JPS5694636A
Cited
EP0084424A2
Cited
JPS60152033A
Cited
JPS6128313A
Cited
JPS61283134A
Cited
JPS6214916A
Cited
EP0211618A2
Cited
EP0213764A2
Cited
JPS6317243A
Cited
EP0273556A1
Cited
JPS63172432A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-02 | 1995-06-03 | 1995-12-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-02 | 1999-06-03 | 1999-12-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-02 | 2003-06-03 | 2003-12-03 | $7700.00 | Window Closed / Lapsed |