Method of manufacturing optical waveguide fiber with titania-silica outer cladding
Assignee: Corning Inc
•
Filing: 1989-12-22
•
Granted: 1991-11-26
•
Expires: 2009-12-22
Abstract
Abstract A method of making an optical waveguide fiber with a fatigue resistant TiO 2 -SiO 2 outer cladding, and a substantially glass blank for drawing into optical fiber, wherein a glass soot TiO 2 -SiO 2 outermost layer, with an initial TiO 2 concentration greater than 10.5 wt. %, is deposited on a preform, and the preform is exposed to an atmosphere of chlorine at a high temperature, and the resulting TiO 2 concentration in the outermost layer of the TiO 2 -SiO 2 outer cladding of the substantially glass blank is less than the initial TiO 2 concentration. In the glass blank form, the outermost layer includes a substantial volume percentage of crystalline phases and in the fiber form, the outermost layer includes inhomogeneities.
Inventors
- 👤 Marcella R. Backer
- 👤 Ralston Cavender
- 👤 Melanie L. Elder
- 👤 Peter C. Jones
- 👤 James A. Murphy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:17
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/036; G02B6/03616; G02B6/03622; C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01446; C03C; C03C13/00; C03C13/04; C03C13/045; C03B2201/00; C03B2201/06; C03B2201/30; C03B2201/40; C03B2201/42; C03B2207/00; C03B2207/04; C03B2207/06; C03B2207/12; C03B2207/20
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
215 words
A method of making a glass blank with a TiO 2 --SiO 2 outer cladding layer for drawing into an optical waveguide fiber with a TiO 2 --SiO 2 outer cladding having a predetermined TiO 2 concentration profile, comprising, depositing glass soot in the form of a preform including an outer cladding of TiO 2 --SiO 2 , said outer cladding including an outermost layer having an initial TiO 2 concentration greater than 10.5 wt. %, exposing said preform to an atmosphere containing chlorine and at a temperature in the range of from 900° to 1400° C., the chlorine being supplied in a sufficient concentration, for a sufficient time and at a sufficient temperature to increase the size of TiO 2 crystals in said outer cladding of TiO 2 --SiO 2 such that the concentration of resulting TiO 2 crystals with diameters in the range of 0.3 to 5 μm is greater than or equal to 0.1 vol. %, and consolidating said preform into said glass blank with a TiO 2 --SiO 2 outer cladding layer, wherein the resulting TiO 2 concentration in at least said outermost layer of the TiO 2 --SiO 2 outer cladding layer of the glass blank is greater than 10.5 wt. % and less than said initial TiO 2 concentration.
Claim 2
Independent Claim
215 words
A method of making a glass blank with a TiO 2 --SiO 2 outer cladding layer for drawing into an optical waveguide fiber with a TiO 2 --SiO 2 outer cladding having a predetermined TiO 2 concentration profile, comprising, depositing glass soot in the form of a preform including an outer cladding of TiO 2 --SiO 2 , said outer cladding including an outermost layer having an initial TiO 2 concentration greater than 10.5 wt. %, exposing said preform to an atmosphere containing chlorine and at a temperature in the range of from 900° to 1400° C., the chlorine being supplied in a sufficient concentration, for a sufficient time and at a sufficient temperature to increase the size of TiO 2 crystals in said outer cladding of TiO 2 --SiO 2 such that the concentration of resulting TiO 2 crystals with diameters in the range of 0.3 to 5 μm is greater than or equal to 0.1 vol. %, and consolidating said preform into said glass blank with a TiO 2 --SiO 2 outer cladding layer, wherein the resulting TiO 2 concentration in at least said outermost layer of the TiO 2 --SiO 2 outer cladding layer of the glass blank is greater than 10.5 wt. % and less than said initial TiO 2 concentration.
Claim 3
Dependent Claim
33 words
The method of claim 1, wherein the concentration of resulting TiO 2 crystals with diameters in the range of from 0.5 to 1.5 μm is greater than or equal to 0.1 vol. %.
Claim 4
Dependent Claim
56 words
The method of claim 1, wherein said exposing step further comprises exposing the preform to an atmosphere containing oxygen in a quantity that is sufficient to substantially reduce the depletion of TiO 2 in the outermost layer of the TiO 2 --SiO 2 outer cladding that results from the presence of chlorine in said exposing step.
Claim 5
Dependent Claim
21 words
The method of claim 3, wherein said exposing and consolidating steps are carried out in a furnace with an alumina muffle.
Claim 6
Independent Claim
196 words
A method of making a fatigue resistant optical waveguide fiber with a TiO 2 --SiO 2 outer cladding, comprising, forming a doped SiO 2 preform with a core portion and a cladding portion, depositing a layer of TiO 2 --SiO 2 soot on the outside of said cladding portion to create an augmented preform, said TiO 2 --SiO 2 layer including at least one cylindrical axially symmetric layer with thickness of about 0.1 μm or greater having a TiO 2 concentration greater than 10.5 wt. %, exposing said augmented preform to an atmosphere containing chlorine at a temperature within the range of from about 900° to 1400° C., consolidating said preform into a glass blank with a TiO 2 --SiO 2 outer cladding layer, said exposing and consolidating steps resulting in greater than about 2 volume percent TiO 2 crystalline phases with diameters greater than or equal to about 0.3 μm within the TiO 2 --SiO 2 outer cladding layer of said glass blank, and drawing said glass blank with a TiO 2 --SiO 2 outer cladding layer into an optical waveguide fiber with inhomogeneities in the outer TiO 2 --SiO 2 layer of the fiber.
Claim 7
Independent Claim
196 words
A method of making a fatigue resistant optical waveguide fiber with a TiO 2 --SiO 2 outer cladding, comprising, forming a doped SiO 2 preform with a core portion and a cladding portion, depositing a layer of TiO 2 --SiO 2 soot on the outside of said cladding portion to create an augmented preform, said TiO 2 --SiO 2 layer including at least one cylindrical axially symmetric layer with thickness of about 0.1 μm or greater having a TiO 2 concentration greater than 10.5 wt. %, exposing said augmented preform to an atmosphere containing chlorine at a temperature within the range of from about 900° to 1400° C., consolidating said preform into a glass blank with a TiO 2 --SiO 2 outer cladding layer, said exposing and consolidating steps resulting in greater than about 2 volume percent TiO 2 crystalline phases with diameters greater than or equal to about 0.3 μm within the TiO 2 --SiO 2 outer cladding layer of said glass blank, and drawing said glass blank with a TiO 2 --SiO 2 outer cladding layer into an optical waveguide fiber with inhomogeneities in the outer TiO 2 --SiO 2 layer of the fiber.
Claim 8
Dependent Claim
38 words
The method of claim 5, wherein said TiO 2 crystalline phases in said TiO 2 --SiO 2 outer cladding layer of said glass blank are substantially within the range of from 0.3 μm to 5 μm in diameter.
Claim 9
Dependent Claim
16 words
The method of claim 6, wherein said range of diameters is from 0.5 to 1.5 μm.
Claim 10
Dependent Claim
60 words
The method of claim 5, wherein said step of depositing a layer of TiO 2 --SiO 2 soot further comprises, depositing a first soot layer with a first TiO 2 concentration, and depositing a second soot layer on the outside of said first soot layer, said second soot layer having a greater TiO 2 concentration than said first soot layer.
Claim 11
Dependent Claim
16 words
The method of claim 5, wherein said inhomogeneities are less than about 200 Angstroms in diameter.
Claim 12
Dependent Claim
33 words
The method of claim 5, wherein said at least one cylindrical axially symmetric layer with thickness of about 0.1 μm or greater is the outermost layer in said TiO 2 --SiO 2 layer.
Claim 13
Dependent Claim
38 words
The method of claim 5, further comprising the step of dehydrating and consolidating said preform prior to depositing said layer of TiO 2 --SiO 2 soot on the outside of said cladding portion to create said augmented preform.
Claim 14
Dependent Claim
60 words
The method of claim 5, wherein the region of said drawn fiber corresponding with said at least one cylindrical axially symmetric layer with thickness of about 0.1 μm or greater having TiO 2 concentration greater than 10.5 wt. %, has a resulting TiO 2 concentration that is greater than 10.5 wt. % but less than the initial TiO 2 concentration.
Claim 15
Dependent Claim
61 words
The method of claim 12, wherein said exposing step further comprises exposing the preform to an atmosphere containing oxygen in a quantity that is sufficient to substantially reduce the depletion of TiO 2 in said at least one cylindrical axially symmetric layer with thickness of about 0.1 μm or greater that results from the presence of chlorine in said exposing step.
Claim 16
Dependent Claim
21 words
The method of claim 13, wherein said exposing and consolidating steps are carried out in a furnace with an alumina muffle.
References Cited (Backward Citations)
USRE27560E
Cited
US3673049A
Cited
US3884550A
Cited
US4108674A
Cited
US3962515A
Cited
US4181403A
Cited
US4184860A
Cited
US4263031A
Cited
US4243298A
Cited
US4768859A
Cited
JPS60215538A
Cited
US4620861A
Cited
US4877306A
Cited
JPH01255795A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-25 | 1995-05-27 | 1995-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-25 | 1999-05-27 | 1999-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-25 | 2003-05-27 | 2003-11-26 | $7700.00 | Window Closed / Lapsed |