US4263031A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing glass optical filaments
Assignee: Corning Glass Works
•
Filing: 1978-06-12
•
Granted: 1981-04-21
•
Expires: 1998-06-12
Abstract
Abstract A method of incorporating an additive or dopant oxide into a glass body produced by the oxidation of vaporous source material in a flame. The resultant glassy particles are deposited to form a porous preform having a uniform refractive index. During the consolidation process, the preform is subjected to an atmosphere including a drying agent which penetrates the interstices of the soot preform to simultaneously dry and dope the preform.
Inventors
- 👤 Peter C. Schultz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:03
CPC Classifications
C; C03; C03C; C03C23/00; C03C23/0085; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01446; C03C23/0095; C03C3/00; C03C3/04; C03C3/06; C03B2201/00; C03B2201/06; C03B2201/30; C03B2201/31; C03B2203/00; C03B2203/10; C03B2203/22; C03C2201/00; C03C2201/06; C03C2201/08; C03C2201/10; C03C2201/20; C03C2201/28; C03C2201/30; C03C2201/31; C03C2201/32; C03C2201/40; C03C2201/42; C03C2203/00; C03C2203/40; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
171 words
A method of forming a glass article comprising the steps of providing a tubular glass preform having an aperture therethrough, said preform having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, flowing into said preform aperture a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent, at least a portion of said stream flowing outwardly from the center of said preform through the interstices thereof to the outer surface thereof, said doping agent forming a dopant oxide, the concentration of which is greatest at the inner surface of said preform and which progressively decreases with increasing radius within said preform so that the refractive index within said preform is a maximum at the inner surface of said preform and decreases with increasing radius, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Claim 2
Independent Claim
171 words
A method of forming a glass article comprising the steps of providing a tubular glass preform having an aperture therethrough, said preform having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, flowing into said preform aperture a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent, at least a portion of said stream flowing outwardly from the center of said preform through the interstices thereof to the outer surface thereof, said doping agent forming a dopant oxide, the concentration of which is greatest at the inner surface of said preform and which progressively decreases with increasing radius within said preform so that the refractive index within said preform is a maximum at the inner surface of said preform and decreases with increasing radius, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein the steps of flowing and consolidating are simultaneously performed.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the step of consolidating occurs after the step of flowing.
Claim 5
Dependent Claim
44 words
The method of claim 1 further comprising the steps of heating said dense glass article to the drawing temperature thereof, and drawing said dense glass article to close said aperture and to reduce the cross-sectional area thereof, thereby forming a glass optical waveguide filament.
Claim 6
Dependent Claim
11 words
The method of claim 1 wherein said drying agent comprises chlorine.
Claim 7
Dependent Claim
20 words
The method of claim 5 wherein said atmosphere comprises a compound which reacts to form chlorine and said doping agent.
Claim 8
Dependent Claim
55 words
The method of claim 6 wherein said preform comprises a glass doped with a dopant material to increase the refractive index thereof, said method further comprising the step of flowing along the outside of said preform a stream of a flushing atmosphere containing means to leach dopant material from the outer portion of said preform.
Claim 9
Dependent Claim
55 words
The method of claim 6 wherein the step of flowing is prior to the step of consolidating and wherein the step of flowing comprises subjecting said preform to a temperature lower than the consolidation temperature of said preform but sufficiently high to cause said compound to break down and form chlorine and said dopant agent.
Claim 10
Independent Claim
235 words
A method of producing a light-conducting glass fiber having a refractive index distribution which progressively decreases from a maximum value at the axis thereof to a minimum value at some radius thereof, said method comprising providing a substantially cylindrical mandrel, depositing on said mandrel a coating of flame hydrolysis-produced glass soot to form a water-containing soot preform having a network of continuous open pores throughout its mass, the composition of said soot being substantially uniform throughout said preform, removing said mandrel to form a soot preform having an aperture therethrough, flowing into said preform aperture a stream of an atmosphere containing a drying agent and a doping agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof, at least a portion of said stream flowing outwardly from the center of said preform through the interstices therein to the outer surface thereof, to simultaneously dope said preform and remove water therefrom, heating said preform to a temperature within the consolidation temperature range thereof for a time sufficient to cause said soot particles to fuse and form a dense glass article, heating said dense glass article to the drawing temperature thereof, and drawing said dense glass article to close said aperture and to reduce the cross-sectional area thereof, thereby forming an optical waveguide filament.
Claim 11
Independent Claim
235 words
A method of producing a light-conducting glass fiber having a refractive index distribution which progressively decreases from a maximum value at the axis thereof to a minimum value at some radius thereof, said method comprising providing a substantially cylindrical mandrel, depositing on said mandrel a coating of flame hydrolysis-produced glass soot to form a water-containing soot preform having a network of continuous open pores throughout its mass, the composition of said soot being substantially uniform throughout said preform, removing said mandrel to form a soot preform having an aperture therethrough, flowing into said preform aperture a stream of an atmosphere containing a drying agent and a doping agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof, at least a portion of said stream flowing outwardly from the center of said preform through the interstices therein to the outer surface thereof, to simultaneously dope said preform and remove water therefrom, heating said preform to a temperature within the consolidation temperature range thereof for a time sufficient to cause said soot particles to fuse and form a dense glass article, heating said dense glass article to the drawing temperature thereof, and drawing said dense glass article to close said aperture and to reduce the cross-sectional area thereof, thereby forming an optical waveguide filament.
Claim 12
Dependent Claim
11 words
The method of claim 9 wherein said drying agent comprises chlorine.
Claim 13
Dependent Claim
20 words
The method of claim 10 wherein said atmosphere comprises a compound that reacts to form chlorine and said doping agent.
Claim 14
Dependent Claim
56 words
The method of claim 12 wherein said preform comprises glass particles doped with a dopant material to increase the refractive index thereof, said method further comprising the step of flowing along the outside of said preform a stream of a flushing atmosphere containing means to leach said dopant material from the outer portion of said preform.
Claim 15
Dependent Claim
14 words
The method of claim 11 wherein said drying atmosphere further comprises helium and oxygen.
Claim 16
Dependent Claim
14 words
The method of claim 13 wherein said flushing atmosphere further comprises helium and oxygen.
Claim 17
Dependent Claim
23 words
The method of claim 9 further comprising the step of flowing along the outside of said preform a stream of a flushing atmosphere.
Claim 18
Dependent Claim
99 words
The method of claim 9 wherein said preform comprises a glass doped with a dopant material to increase the refractive index thereof, and wherein, prior to the step of heating said preform to a temperature within the consolidation temperature range, the following steps are performed: heating said preform to a temperature less than the consolidation temperature of said preform, reducing the pressure within said preform to a value less than that at the outside thereof, and flowing along the outside of said preform a stream of a flushing atmosphere containing means to leach said dopant material from said preform.
Claim 19
Independent Claim
153 words
A method of forming a glass article comprising the steps of providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, subjecting the outer surface of said preform to an atmosphere containing a drying agent for removing water from said preform and an agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof, reducing the pressure within said preform aperture to a value lower than that at the outside surface thereof, so that said atmosphere flows radially inwardly through said preform, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Claim 20
Independent Claim
153 words
A method of forming a glass article comprising the steps of providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, subjecting the outer surface of said preform to an atmosphere containing a drying agent for removing water from said preform and an agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof, reducing the pressure within said preform aperture to a value lower than that at the outside surface thereof, so that said atmosphere flows radially inwardly through said preform, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Claim 21
Independent Claim
147 words
A method of forming a glass article comprising the steps of providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, flowing radially outwardly through the interstices of said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for increasing the refractive index at the inner portion of said preform, flowing radially inwardly through said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for lowering the refractive index at the outer portion of said preform, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Claim 22
Independent Claim
147 words
A method of forming a glass article comprising the steps of providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform, disposing said preform in a furnace where it is heated to an elevated temperature, flowing radially outwardly through the interstices of said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for increasing the refractive index at the inner portion of said preform, flowing radially inwardly through said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for lowering the refractive index at the outer portion of said preform, and consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
References Cited (Backward Citations)
US3943218A
Cited
US3938974A
Cited
US3859073A
Cited
US3864113A
Cited
US3933454A
Cited
US4110093A
Cited
US3980459A
Cited
US4030901A
Cited
US4125388A
Cited
US4165223A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-20 | 1984-10-20 | 1985-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-20 | 1988-10-20 | 1989-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-20 | 1992-10-20 | 1993-04-21 | $7700.00 | Window Closed / Lapsed |