Method of manufacturing polycrystalline silicon film
Assignee: Kanazawa University
•
Filing: 1990-01-31
•
Granted: 1991-11-12
•
Expires: 2010-01-31
Abstract
Abstract In a method of manufacturing a poly-Si film, silicon is deposited on a substrate by means of a thermal decomposition of a feed gas and plasma generation. The method comprises the step of arranging said substrate within a reaction apparatus, the step of introducing into said reaction apparatus a feed gas containing a silane-series gas for thermal decomposition of the feed gas at 500° to 800° C., and the step of generating plasma within the feed gas by applying power for generating the plasma simultaneously with the thermal decomposition, said power for plasma generation being controlled at a level lower than the power applied for forming a poly-Si film oriented in the <110> direction, so as to form a poly-Si film substantially oriented in the <100> direction and having a smooth surface.
Inventors
- 👤 Seiichi Hasegawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:21
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2921; H10D; H10D30/00; H10D30/60; H10D30/67; H10D30/674; H10D30/6741; H10D30/6743; H10D30/6745; H10P14/24; H10P14/2922; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3466; Y; Y10; Y10S; Y10S148/00; Y10S148/122
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
134 words
A method of manufacturing a poly-Si film, in which silicon is deposited on a substrate by means of a thermal decomposition of a feed gas and plasma generation, comprising: the step of arranging said substrate within a reaction apparatus; the step of introducing into said reaction apparatus a feed gas containing a silane-series gas for thermal decomposition of the feed gas at 500° to 800° C.; and the step of generating plasma within the feed gas by applying power for the plasma generation simultaneously with the thermal decomposition, said power for plasma generation being controlled at a level lower than the power applied for forming a poly-Si film oriented in the <110> direction, so as to form, prior to annealing, a poly-Si film substantially oriented in the <100> direction and having a smooth surface.
Claim 2
Independent Claim
134 words
A method of manufacturing a poly-Si film, in which silicon is deposited on a substrate by means of a thermal decomposition of a feed gas and plasma generation, comprising: the step of arranging said substrate within a reaction apparatus; the step of introducing into said reaction apparatus a feed gas containing a silane-series gas for thermal decomposition of the feed gas at 500° to 800° C.; and the step of generating plasma within the feed gas by applying power for the plasma generation simultaneously with the thermal decomposition, said power for plasma generation being controlled at a level lower than the power applied for forming a poly-Si film oriented in the <110> direction, so as to form, prior to annealing, a poly-Si film substantially oriented in the <100> direction and having a smooth surface.
Claim 3
Dependent Claim
66 words
The method of manufacturing a poly-Si film according to claim 1, wherein said feed gas is selected from the group consisting of a silane series gas, a mixed gas of a silane series gas and a carrier gas, a mixed gas of a silane series gas and a dopant gas, and a mixed gas of a silane series gas, a dopant gas and a carrier gas.
Claim 4
Dependent Claim
63 words
The method of manufacturing a poly-Si film according to claim 2, wherein said silane series gas is selected from the group consisting of monosilane, disilane and a mixture thereof, said carrier gas is selected from the group consisting of hydrogen, argon and a mixture thereof, and said dopant gas is selected from the group consisting of phosphine, arsine, diborane and a mixture thereof.
Claim 5
Dependent Claim
36 words
The method of manufacturing a poly-Si film according to claim 2, wherein said carrier gas includes hydrogen and the volume ratio of silane to hydrogen in said silane series gas to hydrogen is at least 1/8.
Claim 6
Dependent Claim
23 words
The method of manufacturing a poly-Si film according to claim 1, wherein said thermal decomposition is carried out at 500° to 800° C.
Claim 7
Dependent Claim
36 words
The method of manufacturing a poly-Si film according to claim 1, wherein the pressure within the reaction apparatus of the feed gas is set to fall within the range of between 100 mTorr and 10 Torr.
Claim 8
Dependent Claim
43 words
The method of manufacturing a poly-Si film according to claim 1, wherein the flow rate of the feed gas into the reaction apparatus is controlled to permit the upper limit of the silicon film deposition rate not to exceed 1 to 2 μm/hour.
Claim 9
Dependent Claim
47 words
A method of manufacturing a poly-Si film according to claim 1, wherein said method comprises a step of forming a poly-Si film oriented in the <110> direction on the substrate, and step of forming a poly-Si film oriented in the <100> direction and having a smooth surface.
Claim 10
Independent Claim
157 words
A method of manufacturing a poly-Si film, in which silicon is deposited on a substrate by means of a thermal decomposition of a feed gas and plasma generation, comprising: the step of arranging said substrate within a reaction apparatus; the step of introducing into said reaction apparatus a feed gas containing a silane-series gas for thermal decomposition of the feed gas at 500° to 800° C.; the step of generating plasma within the feed gas by applying power for the plasma generation simultaneously with the thermal decomposition, said power for plasma generation being controlled at a level lower than the power applied for forming a poly-Si film oriented in the <110> direction, so as to form, prior to annealing a poly-Si film substantially oriented in the <100> direction and having a smooth surface; and the step of applying a treatment for increasing the size of the crystal grains to the poly-Si film obtained in the preceding step.
Claim 11
Independent Claim
157 words
A method of manufacturing a poly-Si film, in which silicon is deposited on a substrate by means of a thermal decomposition of a feed gas and plasma generation, comprising: the step of arranging said substrate within a reaction apparatus; the step of introducing into said reaction apparatus a feed gas containing a silane-series gas for thermal decomposition of the feed gas at 500° to 800° C.; the step of generating plasma within the feed gas by applying power for the plasma generation simultaneously with the thermal decomposition, said power for plasma generation being controlled at a level lower than the power applied for forming a poly-Si film oriented in the <110> direction, so as to form, prior to annealing a poly-Si film substantially oriented in the <100> direction and having a smooth surface; and the step of applying a treatment for increasing the size of the crystal grains to the poly-Si film obtained in the preceding step.
Claim 12
Dependent Claim
25 words
The method of manufacturing a poly-Si film according to claim 9, wherein the size-increasing step comprises annealing the poly-Si film at 600° C. or less.
Claim 13
Dependent Claim
88 words
The method of manufacturing a poly-Si film according to claim 9, wherein the treatment for increasing the crystal grain size comprises the steps of: implanting silicon ions into a poly-Si film, which is substantially oriented in the <100> direction, in a direction of the crystal axis of the poly-Si film for making amorphous at least some of the crystal grains oriented in directions other than the <100> direction; and applying an annealing treatment so as to increase the size of the crystal grains oriented in the <100> direction.
Claim 14
Dependent Claim
94 words
The method of manufacturing a poly-Si film according to claim 9, wherein the treatment for increasing the crystal grain size comprises the steps of: depositing an amorphous silicon film on a poly-Si film, which is substantially oriented in the <100> direction; and applying an annealing treatment at a predetermined temperature so as to permit the amorphous silicon in contact with the poly-Si film oriented in the <100> direction to be preferentially crystallized in an oriented manner like the poly-Si film oriented in the <100> direction and, then, to proceed to a solid phase growth.
Claim 15
Dependent Claim
94 words
The method of manufacturing a poly-Si film according to claim 9, wherein the treatment for increasing the crystal grain size comprises the steps of: forming a silicon oxide film on a poly-Si film substantially oriented in the <100> direction; selectively removing the silicon oxide film to partly expose the surface of the poly-Si film; depositing an amorphous silicon film on the silicon film; and applying an annealing treatment at a predetermined temperature so as to permit the amorphous silicon positioned in contact with the poly-Si film to proceed to a solid phase crystal growth.
Claim 16
Dependent Claim
37 words
A method of manufacturing a poly-Si film oriented in the <100> direction and having a smooth surface as recited in claim 1, wherein a poly-Si film oriented in the <110> direction is formed first on said substrate.
References Cited (Backward Citations)
US3976511A
Cited
JPS57109323A
Cited
US4784723A
Cited
US4497683A
Cited
JPS5982715A
Cited
JPS59155121A
Cited
US4662059A
Cited
US4918028A
Cited
US4942058A
Cited
US4814292A
Cited
JPS63236310A
Cited
JPH0214139A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-11 | 1995-05-13 | 1995-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-11 | 1999-05-13 | 1999-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-11 | 2003-05-13 | 2003-11-12 | $7700.00 | Window Closed / Lapsed |