Abstract
Abstract A latch-up free CMOS structure and method of fabrication thereof is disclosed. A P-type substrate (40) is appropriately masked to form a plurality of sites in which isolated wells (50) are formed. A thermal oxide layer (56) is grown on the surface of each well (50), and a boron channel stop (62) implanted therearound. Polysilicon semiconductor material (68) is formed within each well, and implant doped to form an N-well (76) of material. The P-substrate (40) is planarized. PMOS transistors are formed within the oxide isolate N-wells (76), while NMOS transistors are formed in the P-substrate (40) outside the wells.
Inventors
- 👤 Clarence W. Teng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:55
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/80; H10D84/82; H10D84/83; H10D84/85; H10D84/854
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
114 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: (a) forming a PMOS transistor in a substrate; (b) forming an NMOS transistor in the substrate; (c) electrically isolating the PMOS transistor from the NMOS transistor; (d) forming an isolation well for forming therein one of said PMOS or NMOS transistors; wherein said well is formed by: (e) forming a well in the substrate; (f) forming a channel stop peripherally outside said well and surrounding said well; (g) forming a layer of isolating material on the surface of said well; (h) forming a silicon semiconductor material in the isolated well; and (i) forming on said transistor in said well.
Claim 2
Independent Claim
114 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: (a) forming a PMOS transistor in a substrate; (b) forming an NMOS transistor in the substrate; (c) electrically isolating the PMOS transistor from the NMOS transistor; (d) forming an isolation well for forming therein one of said PMOS or NMOS transistors; wherein said well is formed by: (e) forming a well in the substrate; (f) forming a channel stop peripherally outside said well and surrounding said well; (g) forming a layer of isolating material on the surface of said well; (h) forming a silicon semiconductor material in the isolated well; and (i) forming on said transistor in said well.
Claim 3
Independent Claim
123 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: (a) providing a substrate of semiconductor material; (b) forming a channel stop peripherally outside side well and surrounding said well; (c) forming a first MOS transistor in said substrate; and (d) forming a second MOS transistor complementary to said first MOS transistor in said substrate which is electrically isolated from said first MOS transistor by the steps of: (e) forming a well in said substrate; (f) forming a layer of electrically insulating material on the surface of said well; and (g) forming said second MOS transistor in said well, said second MOS transistor being electrically isolated from said first MOS transistor by said layer of electrically insulating material.
Claim 4
Independent Claim
123 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: (a) providing a substrate of semiconductor material; (b) forming a channel stop peripherally outside side well and surrounding said well; (c) forming a first MOS transistor in said substrate; and (d) forming a second MOS transistor complementary to said first MOS transistor in said substrate which is electrically isolated from said first MOS transistor by the steps of: (e) forming a well in said substrate; (f) forming a layer of electrically insulating material on the surface of said well; and (g) forming said second MOS transistor in said well, said second MOS transistor being electrically isolated from said first MOS transistor by said layer of electrically insulating material.
Claim 5
Dependent Claim
18 words
The method of claim 2 wherein the semiconductor material is formed by chemical vapor deposition of silicon material.
Claim 6
Dependent Claim
12 words
The method of claim 3 further including recrystallizing said deposited silicon material.
Claim 7
Dependent Claim
15 words
The method of claim 4 wherein said silicon material is implanted with an N-type impurity.
Claim 8
Dependent Claim
22 words
The method of claim 5 further including forming a plurality of said wells and forming only PMOS transistor in each said well.
Claim 9
Independent Claim
96 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: masking a P-type substrate for protection against ion implantation; patterning said mask to form openings to said substrate; forming wells in said substrate through said openings; growing a thermal oxide isolation layer on all surface of said well for isolating said well from said P-substrate; filling said well with semiconductor material; doping said semiconductor material to form N-type material; planarizing the top surface of said substrate; forming a PMOS transistor in said well; and forming an NMOS transistor in said P-substrate.
Claim 10
Independent Claim
96 words
A method of fabricating a CMOS structure having improved latch-up immunity, comprising the steps of: masking a P-type substrate for protection against ion implantation; patterning said mask to form openings to said substrate; forming wells in said substrate through said openings; growing a thermal oxide isolation layer on all surface of said well for isolating said well from said P-substrate; filling said well with semiconductor material; doping said semiconductor material to form N-type material; planarizing the top surface of said substrate; forming a PMOS transistor in said well; and forming an NMOS transistor in said P-substrate.
Claim 11
Dependent Claim
22 words
The method of claim 7 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
Claim 12
Dependent Claim
18 words
The method of claim 7 wherein said doping step includes ion implanting N-type ions in said semiconductor material.
Claim 13
Dependent Claim
22 words
The method of claim 9 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
Claim 14
Dependent Claim
19 words
The method of claim 7 wherein said well formation step includes etching said well to about 0.5 micron deep.
Claim 15
Dependent Claim
22 words
The method of claim 11 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
Claim 16
Dependent Claim
21 words
The method of claim 7 wherein said growing step includes growing thermal oxide to a thickness of about 2000 angstroms thick.
Claim 17
Dependent Claim
21 words
The method claim 13 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
Claim 18
Dependent Claim
37 words
The method claim 7 wherein said planarization step includes spinning a mask material on said substrate having an etch ratio substantially identical to that of said semiconductor material and etching said mask material and said semiconductor material.
Claim 19
Dependent Claim
22 words
The method of claim 15 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
Claim 20
Dependent Claim
23 words
The method of claim 7, wherein said planarization step includes anisotropically depositing said semiconductor material on said substrate and chemically removing said masking.
Claim 21
Dependent Claim
22 words
The method of claim 17 further including the step of forming a channel stop peripherally outside said well and surrounding said well.
References Cited (Backward Citations)
US4075754A
Cited
US4299024A
Cited
US4416050A
Cited
JPS58192364A
Cited
US4507158A
Cited
US4814287A
Cited
JPS60136330A
Cited
US4879585A
Cited
US4570330A
Cited
US4593458A
Cited
US4685199A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-16 | 1995-03-18 | 1995-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-16 | 1999-03-18 | 1999-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-16 | 2003-03-18 | 2003-09-17 | $7700.00 | Window Closed / Lapsed |