Moldable shrunken thermoplastic polymer foam beads
Assignee: Pregis Innovative Packaging Inc
•
Filing: 1989-01-10
•
Granted: 1991-06-25
•
Expires: 2009-01-10
Abstract
Abstract Moldable shrunken foam beads comprising a foamable thermoplastic polymer, preferably a silane-crosslinked polyolefin foam, are produced by mixing a composition comprising a silane-modified polyolefin (such as a silane-grafted polyethylene) and a silanol condensation catalyst in an extruder to produce a melt, then projecting a blowing agent into the melt at a rate effective to produce a desired foam density in the extrudate; extruding and cutting the melt to form foam beads; allowing the beads to shrink; and exposing the foam beads to moisture to produce silane crosslinking of the polyolefin foam. In certain other embodiments the crosslinking of the thermoplastic polymer can be omitted, and/or shrinkage of the beads produced by vacuum treatment.
Inventors
- 👤 Thomas M. Pontiff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 02:57
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/3461; B29C44/3465; B29B; B29B9/00; B29B9/02; B29B9/06; C; C08; C08J; C08J9/00; C08J9/16; C08J9/22; C08J9/228; B29K; B29K2023/00; B29K2105/00; B29K2105/04; B29K2105/24; C08J2323/00; C08J2323/26
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
69 words
A thermoplastic polymer foam bead, comprising: a moldable and shrunken thermoplastic polymer foam bead having a density, cell size and degree of shrinkage effective to provide a predetermined molding expansion ratio, wherein the density is in the range of from about 0.8 to about 20 pcf (12.8 to 320 Kg.m -3 ), and wherein the molding expansion ratio is in the range of from about 1.1 to about 4.
Claim 2
Dependent Claim
69 words
A thermoplastic polymer foam bead, comprising: a moldable and shrunken thermoplastic polymer foam bead having a density, cell size and degree of shrinkage effective to provide a predetermined molding expansion ratio, wherein the density is in the range of from about 0.8 to about 20 pcf (12.8 to 320 Kg.m -3 ), and wherein the molding expansion ratio is in the range of from about 1.1 to about 4.
Claim 3
Dependent Claim
50 words
Moldable shrunken foam beads in accordance with claim 1, wherein said thermoplastic polymer is selected from the group consisting of homopolymers and copolymers comprising olefin monomers having from 2 to about 8 carbon atoms, alkenyl aromatic polymers, polyvinyl polymers, polycarbonates, polyamides, polyesters, polyphenylene ethers, polyetherimides, fluorocarbon polymers and mixtures thereof.
Claim 4
Dependent Claim
35 words
Moldable shrunken foam beads in accordance with claim 2, wherein said polymer is a polyolefin selected from the group consisting of homopolymers and copolymers comprising olefin monomers having from 2 to about 8 carbon atoms.
Claim 5
Dependent Claim
37 words
Moldable shrunken foam beads in accordance with claim 3, wherein said polyolefin is selected from the group consisting of polypropylene, medium density polyethylene, low density polyethylene, low density polyethylene, linear low density polyethylene, polybutylene and mixtures thereof.
Claim 6
Dependent Claim
36 words
Moldable shrunking foam beads in accordance with claim 2, wherein said alkenyl aromatic polymer is a polystyrene, said polyamide is a nylon, said polyester is a polyethylene terephthalate and said polyvinyl polymer is a polyvinyl halide.
Claim 7
Dependent Claim
16 words
Moldable shrunken foam beads in accordance with claim 1, wherein said polymer is a thermoplastic elastomer.
Claim 8
Dependent Claim
17 words
Moldable shrunken foam beads in accordance with claim 1, produced by extrusion foaming with a blowing agent.
Claim 9
Dependent Claim
28 words
Moldable shrunken foam beads in accordance with claim 7, wherein said blowing agent is a volatile organic agent selected from the group consisting of hydrocarbons and halogenated hydrocarbons.
Claim 10
Dependent Claim
17 words
Moldable shrunken foam beads in accordance with claim 7, wherein said blowing agent is an inert gas.
Claim 11
Dependent Claim
23 words
Moldable shrunken foam beads in accordance with claim 7, wherein said blowing agent is a solid material which decomposes to form a gas.
Claim 12
Dependent Claim
20 words
Moldable shrunken foam beads in accordance with claim 1, wherein said thermoplastic polymer is crosslinked after the bead has shrunk.
Claim 13
Dependent Claim
20 words
Moldable shrunken foam beads in accordance with claim 11, wherein said crosslinking is accomplished by electromagnetic radiation or chemical means.
Claim 14
Dependent Claim
58 words
Moldable shrunken foam beads in accordance with claim 11, wherein said thermoplastic polymer is selected from homopolymers and copolymers comprising olefin monomers having from 2 to about 8 carbon atoms, and mixtures thereof, said foam contains a silane crosslinking agent and a silanol condensation catalyst, and crosslinking is accomplished by exposure of the shrunken foam beads to moisture.
Claim 15
Dependent Claim
53 words
Moldable shrunken foam beads in accordance with claim 7, wherein said beads shrink promptly following foaming due to at least one of the relatively high permeability of the foam cell wall to said blowing agent compared with the ambient atmosphere and the relatively low vapor pressure of said blowing agent at ambient temperature.
Claim 16
Dependent Claim
15 words
Moldable foam beads in accordance with claim 7, having a wrinkled surface layer or skin.
Claim 17
Dependent Claim
23 words
Moldable shrunken foam beads in accordance with claim 7, wherein the shrinkage is substantially complete within less than about one hour following foaming.
Claim 18
Dependent Claim
22 words
Moldable foam beads in accordance with claim 7, wherein the shrinkage is substantially complete within less than about 15 minutes following foaming.
Claim 19
Dependent Claim
27 words
Moldable foam beads in accordance with claim 7, wherein said polymer foam contains at least one permeability adjustment additive to adjust the permeability of said cell walls.
Claim 20
Dependent Claim
45 words
Moldable foam beads in accordance with claim 18, wherein said permeability adjustment additive is selected from the group consisting of esters of long-chain fatty acids and polyhydric alcohols, saturated higher fatty acid amides, saturated higher aliphatic amines and complete esters of saturated higher fatty acids.
Claim 21
Dependent Claim
21 words
Moldable foam beads in accordance with claim 18 wherein said permeability adjustment additive comprises a mixture of glycerol mono- and diglycerides.
Claim 22
Dependent Claim
16 words
Moldable foam beads in accordance with claim 18 wherein said permeability adjustment additive comprises a polystyrene.
Claim 23
Dependent Claim
15 words
Molded articles produced by thermal molding of the moldable shrunken foam beads of claim 1.
References Cited (Backward Citations)
US2787809A
Cited
US2871218A
Cited
US3015650A
Cited
US3214411A
Cited
US3233025A
Cited
US3250730A
Cited
US3278658A
Cited
US3413244A
Cited
US3446781A
Cited
US3632845A
Cited
US3504068A
Cited
US3843757A
Cited
US3644230A
Cited
US3960792A
Cited
US3657165A
Cited
US3766099A
Cited
GB1286460A
Cited
US3646155A
Cited
US3646166A
Cited
GB1408154A
Cited
US3769245A
Cited
US4032609A
Cited
US3953558A
Cited
US3992501A
Cited
US4117195A
Cited
US4117195B1
Cited
US4160072A
Cited
US4168353A
Cited
US4333898A
Cited
US4275023A
Cited
US4278628A
Cited
US4252906A
Cited
US4214054A
Cited
US4217319A
Cited
US4413066A
Cited
US4464425A
Cited
US4446254A
Cited
US4347329A
Cited
US4368276A
Cited
US4399087A
Cited
US4323528A
Cited
US4440703A
Cited
US4424180A
Cited
US4436840A
Cited
US4456704A
Cited
US4443393A
Cited
US4483809A
Cited
US4519963A
Cited
US4504601A
Cited
US4464484A
Cited
US4558094A
Cited
US4540718A
Cited
US4644013A
Cited
US4602047A
Cited
US4526930A
Cited
WO1985001944A1
Cited
US4587270A
Cited
US4598100A
Cited
US4528300A
Cited
US4676939A
Cited
US4596833A
Cited
US4762860A
Cited
US4657937A
Cited
US4602082A
Cited
US4554293A
Cited
US4778829A
Cited
US4640933A
Cited
US4640933B1
Cited
US4748191A
Cited
US4689355A
Cited
US4761431A
Cited
US4720509A
Cited
US4812484A
Cited
US4727093A
Cited
US4861531A
Cited
US4702868A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-24 | 1994-12-24 | 1995-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-24 | 1998-12-24 | 1999-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-24 | 2002-12-24 | 2003-06-25 | $7700.00 | Window Closed / Lapsed |