Buried disordering sources in semiconductor structures employing photo induced evaporation enhancement during in situ epitaxial growth
Assignee: Xerox Corp
•
Filing: 1989-03-24
•
Granted: 1991-05-07
•
Expires: 2009-03-24
Abstract
Abstract In situ removal of selected or patterned portions of semiconductor layers is accomplished by induced evaporation enhancement to form patterned buried impurity layers in semiconductor devices, such as heterostructure lasers and array lasers, which function as buried impurity induced layer disordering (BIILD) sources upon subsequent annealing. These layers may be formed to either function as buried impurity induced layer disordering (BIILD) sources or function as a reverse bias junction configuration of confining current to the active region of a laser structure. Their discussion here is limited to the first mentioned function.
Inventors
- 👤 John E. Epler
- 👤 Thomas L. Paoli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 01:03
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/10; H01S5/18; H01S5/183; H01S5/18308; H01S5/18305; H10; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2911; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3221; H10P14/3242; H10P14/3244; H10P14/3251; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3421; H10P14/38; H10P14/3824; H01S5/18322; H01S5/1833; H01S5/20; H01S5/2054; H01S5/2059; H01S5/2063; H01S5/2068; H01S5/2072; H01S5/30; H01S5/305; H01S5/3095; Y; Y10; Y10S; Y10S148/00; Y10S148/015; Y10S148/072; Y10S148/094; Y10S148/095; Y10S438/00; Y10S438/914; Y10S438/925
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
117 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least one of said layers containing a concentration of an impurity species between 10 19 and the point of saturated concentration of said impurity species in said one layer, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer, selectively desorbing in situ portions of said one layer to the interface with the layer therebeneath employing photo induced evaporation, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer.
Claim 2
Independent Claim
117 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least one of said layers containing a concentration of an impurity species between 10 19 and the point of saturated concentration of said impurity species in said one layer, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer, selectively desorbing in situ portions of said one layer to the interface with the layer therebeneath employing photo induced evaporation, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer.
Claim 3
Independent Claim
166 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least some layers have different elemental constituents relative to other layers, at least one of said layers containing a high concentration of an impurity species sufficient to bring about induced impurity layer disordering to layers in close proximity to said one layer containing a high concentration of an impurity species under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, selectively desorbing in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath employing photo induced evaporation, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species.
Claim 4
Independent Claim
166 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least some layers have different elemental constituents relative to other layers, at least one of said layers containing a high concentration of an impurity species sufficient to bring about induced impurity layer disordering to layers in close proximity to said one layer containing a high concentration of an impurity species under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, selectively desorbing in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath employing photo induced evaporation, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species.
Claim 5
Dependent Claim
70 words
In the method of forming buried impurity sources in a semiconductor structure of claim 2 wherein said one layer containing a high concentration of said impurity species comprises an ultra thin layer of quantum well size and doped with said impurity species at a concentration between 10 19 and the point of saturated concentration of said impurity species in said one layer containing a high concentration of said impurity species.
Claim 6
Dependent Claim
37 words
In the method of forming buried impurity sources in a semiconductor structure of claim 3 wherein said one layer containing a high concentration of said impurity species comprises GaAs and said impurity species comprises Si and Se.
Claim 7
Dependent Claim
48 words
In the method of forming buried impurity sources in a semiconductor structure of claim 2 wherein a doping sheet comprising a atomic submonolayer or more of said impurity species is deposited on at least one surface of said one layer containing a high concentration of said impurity species.
Claim 8
Dependent Claim
47 words
In the method of forming buried impurity sources in a semiconductor structure of claim 2 wherein a doping sheet comprising a atomic submonolayer, monolayer or more of said impurity species is deposited on opposite surfaces of said one layer containing a high concentration of said impurity species.
Claim 9
Dependent Claim
55 words
In the method of forming buried impurity sources in a semiconductor structure of claim 2 wherein there is a plurality of said quantum well layers doped with said impurity species, a plurality of doping sheets comprising an atomic submonolayer, monolayer or more of said impurity species, said doping sheets alternated with said quantum well layers.
Claim 10
Independent Claim
161 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least some layers have different elemental constituents relative to other layers, at least one of said layers containing a high concentration of an impurity species sufficient to bring about induced impurity layer disordering to layers in close proximity to said one layer containing a high concentration of an impurity species under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, patterning in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species.
Claim 11
Independent Claim
161 words
The method of forming buried impurity sources in a semiconductor structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, at least some layers have different elemental constituents relative to other layers, at least one of said layers containing a high concentration of an impurity species sufficient to bring about induced impurity layer disordering to layers in close proximity to said one layer containing a high concentration of an impurity species under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, patterning in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species.
Claim 12
Dependent Claim
70 words
In the method of forming buried impurity sources in a semiconductor structure of claim 8 wherein said one layer containing a high concentration of said impurity species comprises an ultra thin layer of quantum well size and doped with said impurity species at a concentration between 10 19 and the point of saturated concentration of said impurity species in said one layer containing a high concentration of said impurity species.
Claim 13
Dependent Claim
37 words
In the method of forming buried impurity sources in a semiconductor structure of claim 9 wherein said one layer containing a high concentration of said impurity species comprises GaAs and said impurity species comprises Si and Se.
Claim 14
Dependent Claim
48 words
In the method of forming buried impurity sources in a semiconductor structure of claim 8 wherein a doping sheet comprising a atomic submonolayer or more of said impurity species is deposited on at least one surface of said one layer containing a high concentration of said impurity species.
Claim 15
Dependent Claim
47 words
In the method of forming buried impurity sources in a semiconductor structure of claim 8 wherein a doping sheet comprising a atomic submonolayer, monolayer or more of said impurity species is deposited on opposite surfaces of said one layer containing a high concentration of said impurity species.
Claim 16
Dependent Claim
55 words
In the method of forming buried impurity sources in a semiconductor structure of claim 8 wherein there is a plurality of said quantum well layers doped with said impurity species, a plurality of doping sheets comprising an atomic submonolayer, monolayer or more of said impurity species, said doping sheets alternated with said quantum well layers.
Claim 17
Independent Claim
174 words
The method of forming buried impurity sources in a semiconductor laser structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, said layers including an active region for light wave generation and propagation under lasing conditions, at least one of said layers intermediate of the other layers and in proximity to said active region containing a high concentration of an impurity species sufficient to bring about induce impurity layer disordering to layers in close proximity thereto under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, patterning in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species and producing in situ a buried active region.
Claim 18
Independent Claim
174 words
The method of forming buried impurity sources in a semiconductor laser structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, said layers including an active region for light wave generation and propagation under lasing conditions, at least one of said layers intermediate of the other layers and in proximity to said active region containing a high concentration of an impurity species sufficient to bring about induce impurity layer disordering to layers in close proximity thereto under proper disordering conditions, interrupting the epitaxial growth of said semiconductor layers after the deposition of said one layer containing a high concentration of said impurity species, patterning in situ portions of said one layer containing a high concentration of said impurity species to the interface with the layer therebeneath, and continuing the epitaxial deposition of remaining layers inducing at least initial impurity disordering of regions of deposited layers in proximity to the remaining portions of said one layer containing a high concentration of said impurity species and producing in situ a buried active region.
Claim 19
Dependent Claim
71 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 14 wherein said one layer containing a high concentration of said impurity species comprises an ultra thin layer of quantum well size and doped with said impurity species at a concentration between 10 19 and the point of saturated concentration of said impurity species in said one layer containing a high concentration of said impurity species.
Claim 20
Dependent Claim
38 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 15 wherein said one layer containing a high concentration of said impurity species comprises GaAs and said impurity species comprises Si and Se.
Claim 21
Dependent Claim
49 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 14 wherein a doping sheet comprising a atomic submonolayer or more of said impurity species is deposited on at least one surface of said one layer containing a high concentration of said impurity species.
Claim 22
Dependent Claim
48 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 14 wherein a doping sheet comprising a atomic submonolayer, monolayer or more of said impurity species is deposited on opposite surfaces of said one layer containing a high concentration of said impurity species.
Claim 23
Dependent Claim
56 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 14 wherein there is a plurality of said quantum well layers doped with said impurity species, a plurality of doping sheets comprising an atomic submonolayer, monolayer or more of said impurity species, said doping sheets alternated with said quantum well layers.
Claim 24
Dependent Claim
61 words
In the method of forming buried impurity sources in a semiconductor laser structure of claim 14 further comprising the step of: forming in situ a buried current confinement means in close proximity to said buried active region, said buried current confinement means comprising a reverse bias junction configuration containing a current channel therein in approximate alignment with said buried active layer.
Claim 25
Independent Claim
160 words
The method of forming impurity sources in a surface emitting semiconductor laser structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, said layers including an active region for light wave generation and propagation under lasing conditions with a Fabry-Perot cavity transverse to the planar extent of said active region, a surface emission region at one end of said cavity and a DBR formed at the other end of said cavity to function as a reflector for optical feedback for propagating radiation, forming in situ a buried current confinement means in close proximity to said buried active region, said buried current confinement means comprising a reverse bias junction configuration containing a current channel therein in approximate alignment with said buried active layer, impurity induced disordering of said DBR outside the region of said cavity to form regions to provide for both optical confinement for propagating radiation in said cavity and current injection means to said active region.
Claim 26
Independent Claim
160 words
The method of forming impurity sources in a surface emitting semiconductor laser structure comprising the steps of: epitaxially depositing several semiconductor layers on a substrate, said layers including an active region for light wave generation and propagation under lasing conditions with a Fabry-Perot cavity transverse to the planar extent of said active region, a surface emission region at one end of said cavity and a DBR formed at the other end of said cavity to function as a reflector for optical feedback for propagating radiation, forming in situ a buried current confinement means in close proximity to said buried active region, said buried current confinement means comprising a reverse bias junction configuration containing a current channel therein in approximate alignment with said buried active layer, impurity induced disordering of said DBR outside the region of said cavity to form regions to provide for both optical confinement for propagating radiation in said cavity and current injection means to said active region.
References Cited (Backward Citations)
US4329660A
Cited
US4511408A
Cited
US4843032A
Cited
US4654090A
Cited
US4810670A
Cited
US4771010A
Cited
US4824798A
Cited
US4830983A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-06 | 1994-11-05 | 1995-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-06 | 1998-11-05 | 1999-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-06 | 2002-11-05 | 2003-05-07 | $7700.00 | Window Closed / Lapsed |